PubMed1999

Detection and determination of surface levels of poloxamer and PVA surfactant on biodegradable nanospheres using SSIMS and XPS.

The surface chemical characterisation of sub-200 nm poly(DL-lactide co-glycolide) nanospheres has been carried out using the complementary analytical techniques of static secondary ion mass spectrometry (SSIMS) and X-ray photoelectron spectroscopy (XPS). The nanospheres, which are of interest for site-specific drug delivery, were prepared using an emulsification-solvent evaporation technique with poly(vinyl alcohol), Poloxamer 407 and Poloxamine 908 respectively as stabilisers. The presence of surfactant molecules on the surface of cleaned biodegradable colloids was confirmed and identified on a qualitative molecular level (SSIMS) and from a quantitative elemental and functional group analysis (XPS) perspective. SSIMS and XPS data were also used in combination with electron microscopy to monitor the effectiveness of cleaning procedures in removing poorly bound surfactant molecules from the surface of nanospheres. The findings are discussed with respect to the development of nanoparticle delivery systems, particularly the composition of the surface for extending blood circulation times and achieving site-specific deposition.

Adsorption↗

PubMed1999

In vivo biocompatibility and degradation studies of polyhydroxyoctanoate in the rat: a new sealant for the polyester arterial prosthesis.

The present study examined the biocompatibility and degradation properties of poly (beta-hydroxy octanoate) (PHO) as an impregnation substrate on arterial prostheses. PHO-impregnated polyester grafts sterilized by ethylene oxide (EO) or gamma (gamma) radiation, and polyester Dacron(R) prostheses impregnated with fluoropolymer, gelatin, or albumin were implanted subcutaneously in rats for periods ranging from 2 to 180 days. The biocompatibility was assessed by quantifying the alkaline and acid phosphatase secretion while performing histological studies at the tissue/prosthesis interface. The degradation was determined by chemical analysis of the EO and gamma-sterilized PHO after implantation using differential scanning calorimetry (DSC), wide angle x-ray diffraction (WAXD), and size exclusion chromatography (SEC). Alkaline phosphatase activity by the sterilized PHO and by the gelatin and albumin grafts was significantly elevated early after implantation in contrast to that of the Dacron and fluoropolymer grafts that occurred later, at 7 and 5 days, respectively The peak of acid phosphatase activity for all of the grafts occurred between 5 and 10 days postimplantation, with the gamma-sterilized PHO grafts recording the greatest activity. Histological study revealed that the tissue incorporation into the graft wall was earlier and more complete for the Dacron and fluoropolymer grafts after 6 months than for the gelatin and albumin grafts, because the latter induced important inflammatory reactions during the resorption of the cross-linked protein substrates. The EO and gamma-sterilized PHO grafts exhibited a similar healing sequence characterized by the development of a collagenous tissue surrounding the prostheses. However, no infiltration of tissue into the graft wall was observed after 6 months, mainly because of the presence of the PHO. Degradation of the EO and gamma-sterilized PHO occurred preferentially by a hydrolytic mechanism as shown by a 30% molecular weight decrease after 6 months. In conclusion, PHO showed good biocompatibility in terms of enzyme activity and tissue reaction. Degradation was a slow, in vivo process controlled primarily by a random hydrolytic reaction and by a local enzymatic attack by macrophages and giant cells.

Acid Phosphatase↗

PubMed1999

Effect of sterilization on the physical and structural characteristics of polyhydroxyoctanoate (PHO).

The present study examined the potential applicability of poly(beta-hydroxy octanoate) (PHO), a bacterial polyester, as a candidate for biomaterial applications, by investigating the effect of sterilization on the physical and structural characteristics of PHO. PHO-cast films were sterilized by either ethylene oxide (EO) gas at 38 degrees C or gamma radiation (2.5 Mrad) in air at room temperature. The physical characteristics of the EO and gamma-sterilized PHO were determined by scanning electron microscopy (SEM) and tensile strength analyses. In addition, various analytical methods were used to detect modifications in the chemical and morphological structure of PHO, namely, electron spectroscopy for chemical analysis (ESCA), Fourier transform infrared (FTIR) spectroscopy, differential scanning calorimetry (DSC), wide angle X-ray diffraction (WAXD), and size exclusion chromatography (SEC). The results show that EO sterilization did not modify the chemical and physical characteristics of PHO, however, significant modifications in both the structural and tensile properties were observed with gamma-sterilized PHO. These changes accounted for decreases in both the weight average, number average and melting temperature, and increases in the heat of fusion and tensile strength. No residual EO was detected following sterilization as revealed by head-space chromatography. The physical and structural properties of PHO were shown to be well preserved following EO sterilization, whereas gamma radiation caused random chain scission and physical cross-linking, a frequent phenomenon observed with organic polymers.

Bacteria↗

PubMed1999

Hydrolytic and enzymatic incubation of polyhydroxyoctanoate (PHO): a short-term in vitro study of a degradable bacterial polyester.

The present study examined the degradation behaviour of poly(beta-hydroxy octanoate) (PHO), a bacterial poly(beta-hydroxy alkanoate), following incubation under hydrolytic or enzymatic conditions in vitro. Solution-cast PHO films were incubated in a citrate buffer solution with and without acid phosphatase and in an acetate buffer with and without beta-glucuronidase for periods ranging from 7 to 60 days. The physical characterization of the PHO films was analyzed by SEM and tensile strength studies. In addition, various analytical methods were used to detect modifications in the chemical and morphological structure of the PHO, namely, ESCA, FTIR, DSC, X-ray diffraction, and SEC. The results indicate that the enzymatic conditions selected in the present study induced no significant surface morphological or chemical modifications, and no significant weight loss was observed after 60 days of incubation. However, as revealed by weight average molecular weight Mw and number average molecular weight Mn decreases, changes in the bulk structure of the PHO were observed with acid phosphatase at 28 and 60 days, in contrast to smaller Mw and Mn decreases recorded in both the buffers and the beta-glucuronidase. The tensile properties had decreased following incubation, yet showed no difference under all of the selected conditions. With no weight loss or surface changes, the PHO films incubated in acid phosphatase showed only a chemical hydrolytic process characterized by Mw and Mn decreases with time of incubation. The present study demonstrated that the degradation of PHO films is one of slow, chemical hydrolysis only, perhaps requiring several months of incubation. The hydrophobic nature of the long alkyl pendent chain in PHO may be responsible for this slow process. The inability of enzymes to degrade PHO may be attributed to the latter's poor adsorption capacity, due to its hydrophobic nature, and to a lack of specificity in the catalytic activity of these enzymes.

Acid Phosphatase↗

PubMed1998

Something new in the field of PLA/GA bioresorbable polymers?

Polymers issued from glycolic acid and lactic acids (PLAGA) are now used worldwide as bioresorbable devices in surgery and in pharmacology. Their abiotic hydrolytic degradation has been shown to depend on diffusion-reaction phenomena and to proceed homogeneously or heterogeneously, depending on many factors. Two initiators are presently used industrially to make PLAGA polymers by ring opening polymerisation of lactide and/or glycolide in the bulk, namely Sn octanoate and zinc metal. In this contribution, attention is paid to the differences generated by the use of these two initiator systems in the case of the polymerisation of DL-lactide. Various poly(DL-lactide)s were prepared and characterised by size-exclusion chromatography (SEC), differential scanning calorimetry (DSC) and nuclear magnetic resonance spectroscopy (NMR). These polymers were allowed to age in pH=7.4 isoosmolar phosphate buffer at 37 degrees C. Under these conditions, polymers prepared by the two initiator systems showed dramatic differences when the fates of parallel sided specimens of rather large dimensions were considered. These differences were related to the esterification of some of the OH chain ends by octanoic acid and to the presence of rather hydrophobic low molecular weight by-products which were insoluble in the solvent generally used to purify the crude PLAGA polymers. These new findings should be of great interest in the case of PLAGA based matrices aimed at drug delivery.

Biocompatible Materials↗

PubMed1998

Capillary zone electrophoresis in normal or reverse polarity separation modes for the analysis of hydroxy acid oligomers in neutral phosphate buffer.

Capillary zone electrophoresis (CZE) with neutral phosphate buffer as the background electrolyte was used to analyse water-soluble oligomers obtained by polycondensation of racemic lactic acid. Two CZE separation modes were tested. The first mode was based on normal separation (injection at the anodic side) using a fused-silica capillary. Eight peaks were observed within a 60-min migration time range. They were ascribed to dimer and higher water-soluble oligomers. Peaks from dimer to tetramer were split due to sensitivity for the fine structures at the level of the distribution of chiral lactic acid moieties in oligomer chains. The second mode was based on reverse separation (injection at the cathodic side) using a fused-silica capillary modified by adsorption of a polycation on its inner wall. Under these conditions, oligomers were rapidly separated without peak splitting. Considering the forces which are involved in CZE, data were plotted as a function of 1/t scale, according to the equation [signal]=f((-1)(k)/t) where k=0 and k=1 for normal and reverse separation modes, respectively. Such a plot allowed direct comparison between the various runs after a simple translation along the 1/t axis, regardless of the separation mode and the variation of electroosmotic flow. The second separation mode allowed separation of 3-hydroxybutyric acid and 6-hydroxyhexanoic acid oligomers. For the former series of oligomers, a side reaction generating crotyl bonds was observed due to the high sensitivity of CZE. It was shown that separation was governed by the ratio charge/mass of the oligoesters whatever their structure.

Buffers↗

PubMed1998

Metabolite-derived artificial polymers designed for drug targeting, cell penetration and bioresorption.

The use of poly(beta-malic acid) and poly(l-lysine citramide) carriers to transport doxorubicin (Dox) within K562 myeloblastic cells was studied by taking advantage of laser microspectrofluorometry (L-MSF). This technique provided a means to monitor and to quantify the penetration of Dox molecules in the cytoplasm and in the nucleus of Dox-sensitive and Dox-resistant cells. Comparison was made between polymer-drug conjugates more or less hydrophobised by C2, C7 and C12 aliphatic substituents and by the Dox attached to the polymer backbone as pendent chains. Furthermore, a method was proposed to introduce a cleavable non-peptidic spacer of the lactyllactyl-type between the poly(L-lysine citramide) backbone and the drug. It is shown that: Dox was released from the conjugates by a non-enzymatic route in the absence of cells, the Dox-uptake by cells was slower for the conjugates than for the free drug, and the hydrophobisation promoted the penetration of the released drug within the nucleus, even in the case of Dox-resistant cells. However, no reversion of the resistance was observed.

Cell Nucleus↗

PubMed1998

Calcium alginate dressings--I. Physico-chemical characterization and effect of sterilization.

In order to analyze the alginate components of alginate dressings and the fractions which are released when the dressing is in contact with model biological fluids, the use of various analytical methods was considered. The first step was the conversion of a calcium alginate batch to pure sodium alginate. The recovery of the latter from either insoluble or soluble mixed sodium/calcium alginates was performed by complexation of calcium ions with sodium citrate followed by ultrafiltration. Comparisons were made between sugar analysis, 1H NMR and circular dichroism (CD) data to determinate the contents in guluronic and mannuronic acids of sodium alginate chains. It was shown that CD measurements afford a rapid and nondestructive method for determination of %G when one takes the ratio theta200/theta220 into account. Fractionation of crude alginate (generally ranging from 30 to 70% G) was achieved by the triangle dissolution/precipitation method in order to increase the range of alginate in sugar composition. The various validated procedures were applied to investigate the effects of irradiation sterilization on alginate dressings. It was shown that sugar composition is retained whereas molecular weight decreased dramatically due to chain scission.

Alginates↗

PubMed1998

Uptake and intracellular distribution of 4-aminofluorescin-labelled poly(L-lysine citramide imide) in K562 cells.

4-Aminofluorescein (F1-NH2) was conjugated with various macromolecular carriers of the poly(L-lysine citramide)-type which were hydrophobised by ethyl (C2), heptyl (C7), and dodecyl (C12) alkyl groups attached to the pendent carboxyl of the lysine moieties present in repeating units. The dye was used to label the carriers and monitor their intracellular fate after introduction within the incubation medium of K562 cells. The labelled hydrophobised carriers formed multimolecular compacted aggregates stabilised by the balance of attractive hydrophobic interactions and repulsive electrostatic forces in the aqueous culture medium. The apparent molecular weights and the sizes of these aggregates were determined by Size Exclusion Chromatography (SEC) and by light scattering respectively. Comparison was made of the cell distribution of free and conjugated F1-NH2 in the cell cytoplasm and nucleus by using fluorescence microscopy and laser microspectrofluorometry. It was shown that cell uptakes resulted from adsorptive pinocytosis and depended on hydrophobicity and aggregation of the conjugates. The influence of physical entrapment of free-F1-NH2 within the hydrophobic microdomains formed by aggregates F1-NH2 conjugates was also discussed.

Chromatography, Gel↗

PubMed1996

Hydrolytic degradation of films prepared from blends of high and low molecular weight poly(DL-lactic acid)s.

Biodegradable films were prepared by casting acetone solutions of mixtures of a high molecular weight poly(DL-lactic acid) (HMW-PLA50) with 0, 10, and 30% w/w poly(DL-lactic acid) oligomers (LMW-PLA50), before drying. From size exclusion chromatography (SEC) it was shown that degradation occurred during film processing, in agreement with the acid-catalyzed degradation of polyesters. The higher the content of LMW-PLA50, the larger the decrease of the molar masses. The three selected film formulations were then allowed to age in isoosmolar 0.13M, pH 7.4 sodium phosphate buffer at 37 degrees C. The hydrolytic degradation was monitored by using various techniques, namely weighing to quantify water absorption and weight loss, SEC to evaluate molar mass changes, head space gas chromatography to assess the desorption of residual acetone, and enzymatic assay of the L-lactic acid released in the aging media. The presence of LMW-PLA50 clearly accelerated film degradation. Moreover, it was shown that the mechanism of degradation greatly depended on the content in the oligomers.

Absorption↗

PubMed1996

Screening of microorganisms for biodegradation of poly(lactic-acid) and lactic acid-containing polymers.

The ability of some microorganisms to use lactic acid stereocopolymers and copolymers with glycolic acid as sole carbon and energy sources was studied under controlled or natural conditions. First, 14 filamentous fungal strains were tested in liquid cultures, adopting total lactic acid consumption, nitrogen source exhaustion, and maximal biomass production as selection criteria. Two strains of Fusarium moniliforme and one strain of Penicillium roqueforti were able to totally assimilate DL-lactic acid, partially soluble racemic oligomers (MW = 1,000), and the nitrogen source. Only one strain of F. moniliforme was able to grow on a poly(lactic acid)-glycolic acid copolymer (MW = 150,000) after 2 months of incubation at 28 degrees C on synthetic agar medium. Mycelium development was examined by scanning electron microscopy. F. moniliforme filaments were observed to grow not only at the copolymer surface but also through the bulk of the copolymer. In a second approach, plates made of a racemic poly(lactic acid) were buried in the soil before being incubated in petri dishes containing mineral agar medium under controlled conditions. Five strains of different filamentous fungi were isolated, and their ability to assimilate racemic poly(lactic acid) oligomers was tested in liquid cultures.

Biodegradation, Environmental↗

PubMed1996

Hydrolytic degradation of the coral/poly(DL-lactic acid) bioresorbable material.

A bioresorbable composite material composed of a high molecular weight poly(DL-lactic acid) and granules of natural coral (40/60 w/w) was made by blending in acetone with further evaporation of the solvent. The blend and the unfilled polymer matrix were compression moulded and machined to yield 12 x 12 mm plates of different thicknesses (1.4 mm for the blend vs 2.1 mm for the polymer). The resulting plates were allowed to age at 37 degrees C in a pH 7.4 isoosmolar phosphate buffer solution taken as a model of body fluids. Hydrolytic degradation of the blend was investigated comparatively with the unfilled polymer matrix. The fate of the specimens was monitored by weighing, enzymatic assay, size-exclusion chromatolography and differential scanning calorimetry. Data on water absorption, weight loss, release of L-lactic acid, molecular weight and morphology changes conclusively showed that the presence of coral dramatically modified the degradation characteristics of poly(DL-lactic acid). In particular, the faster internal degradation observed for the unfilled polymer matrix was not detected for the blend. This finding was assigned to the buffering effect of calcium carbonate which neutralized the carboxyl end groups of the degradation products and to the presence of coral/polymer interfaces which facilitated ion exchanges with the external solution, both contributing to eliminate autocatalysis.

Animals↗

PubMed1996

Structural characterization and hydrolytic degradation of a Zn metal initiated copolymer of L-lactide and epsilon-caprolactone.

A bioresorbable aliphatic polyester was synthesized by bulk copolymerization of a 1/1 M/M L,L-lactide/epsilon-caprolactone mixture using zinc metal as initiator. The actual composition of the copolymer was found to be 1.5/1 as deduced from 1H NMR spectra obtained in DMSO-d6 solutions where higher resolution was obtained as compared with chlorinated solvents. Resonances due to L-lactyl units (L) exhibited triads stereosensitivity, epsilon-oxycaproyl units (C) being sensitive to dyads. Average lengths of both poly(lactic acid) and polycaprolactone sequences were evaluated and showed the presence of rather long PLA blocks. Furthermore, no CLC triad signal was found, suggesting the absence of transesterification rearrangements. 10 x 10 x 2 mm specimens made of the copolymer were allowed to age in isoosmolar pH = 7.4 phosphate buffer at 37 degrees C. Degradation was monitored by various analytical techniques such as SEC, X-ray diffractometry, DSC, and 1H NMR. Data were compared with the behaviour of PCL and PLA homopolymers allowed to age under similar conditions. Crystallinity and composition changes are discussed in terms of preferential degradation in L- and C-containing amorphous domains, crystallized long PLA blocks being much more resistant.

Absorption↗

PubMed1995

Hydrolytic degradation of devices based on poly(DL-lactic acid) size-dependence.

The hydrolytic degradation of aliphatic polyesters derived from lactic and glycolic acids (PLA/GA polymers) has been previously shown to proceed heterogeneously in the case of large size devices, the rate of degradation being greater inside than at the surface. A qualitative model based on diffusion-reaction phenomena was proposed which accounts for the formation of the more stable outer layer. However, this model also suggested that devices with dimensions smaller than the thickness of the outer layer should degrade less rapidly than larger ones. In an attempt to check this hypothesis, 15 x 10 x 2 mm compression moulded plates, millimetric beads and submillimetric microspheres and cast films, derived from the same batch of poly (DL-lactic acid) polymer were allowed to age comparatively in isoosmolar 0.13 M phosphate buffer, pH 7.4, at 37 degrees C. Ageing of the various devices was monitored by measuring water absorption, weight loss, L-lactic acid formation, pH and molar mass changes. As expected, large size plates and millimetric beads degraded heterogeneously and much faster than homogeneously degraded submillimetric films and particles.

Absorption↗

PubMed1995

Hydrolytic degradation of benzylated poly(beta-malic acid): influence of sample size, sample shape, and polymer composition.

In order to investigate the effects of sample size, sample shape, and polymer composition on the hydrolytic degradation of water-insoluble benzylated poly(beta-malic acid) derivatives, three polymers were synthesized, namely PMLABe100, PMLABe90H10 and PMLABe80H20, containing 100, 90, and 80% of benzyl units respectively. For each polymer, 4-mm-thick compression molded pellets, 0.3-mm-thick casted films and 250-500 microns ground particles were made and allowed to age in 0.13 M, pH 7.4 sodium phosphate buffer at 37 degrees C. Degradation was monitored by measuring weight changes, variations of polymer composition, formation of benzyl alcohol, and molecular weight decreases. It was shown that degradation of particles and films depended initially on polymer composition due primarily to fast degradation of acid-rich segments present or formed by benzyl ester cleavages which led more or less rapidly to similar compositions for the three polymers. The higher the content in acid groups, the faster the degradation rate and the characteristic changes. It was also found that pellets made of PMLABe90H10 or PMLABe80H20 degraded heterogeneously and much faster than corresponding films and particles.

Benzene Derivatives↗

PubMed1995

[Risks and regulations related to materials used in implantology and maxillofacial surgery].

In the present paper, the authors call in mind the definitions of biocompatibility and the essential qualities required for biomaterials. The materials mostly used in implantology and maxillofacial surgery are numerous alloys, bioceramics, resorbable and non-resorbable polymers, and finally osseous substitutes of human or animal origin. As to synthetic and non-living materials, the risks in patients are generated by the degradation products. These may induce tissular reactions of inflammatory or immune origin owing to toxic effects. Concerning osseous substitutes, rejections are mostly of immune origin, for allografts and in particular for xenografts. Infections may be another major risk and in spite of all precautionary measures viral infections by hepatitis B, HIV and transmissible spongiform encephalopathy are not yet got under total control. It is just in these domains that one can state juristic lacks which national and european organisation of standardisation and homologation have to cover during the next few years.

Alloys↗

PubMed1994

End-chain radiolabeling and in vitro stability studies of radiolabeled poly(hydroxy acid) nanoparticles.

In order to study the tissue distribution of biodegradable nanoparticles after oral administration in animals, end-chain-radiolabeled poly(D,L-lactides) were prepared. Two groups of polymers (Mn = 7500, I = 2.4 and Mn = 28000, I = 1.4 as determined by organic size-exclusion chromatography) were chemically modified by reaction of [14C]acetic anhydride with hydroxyl end-chain groups. The activities of both resulting radioactive poly(D,L-lactides) varied from 57 to 1140 microCi/g. Poly(D,L-lactide) or poly(D,L-lactide-co-glycolide) nanoparticles containing various amounts of radioactive polymer were prepared according to the solvent evaporation process with acetone as cosolvent with methylene chloride in the organic phase. Their mean diameter was 133 +/- 25 nm, measured by photon correlation spectroscopy. The radiolabeled-end-group stability of these particles in buffer solutions was found to be greater when the matrix was made from the radiolabeled poly(D,L-lactide) having the highest molecular weight and the lowest polydispersity index. The polymer-chain stability was totally retained for at least 1 week in a phosphate buffer, pH 7.4, i.e. for the selected experiment time.

Carbon Radioisotopes↗

PubMed1994

Biodegradation of PLA/GA polymers: increasing complexity.

The degradation of aliphatic polyesters derived from lactic and glycolic acids (PLA/GA) depends on many factors. It has been found recently that the interior of large size devices degrades faster than the outer zone. A qualitative model has been proposed to account for this heterogeneous degradation. It is based on diffusion-reaction phenomena combined with the well-known autocatalytic effect of carboxylic chain ends. This contribution recalls the present understanding of the hydrolytic degradation of PLA/GA polymers and emphasizes its complexity on the basis of the influence of secondary factors such as the presence of a basic load, namely, gentamycin, in poly(lactic acid) matrices, and the presence of long stereoregular sequences in poly(DL-lactic acid) macromolecules.

Biocompatible Materials↗