PubMed2002

Development of emission factors for polycarbonate processing.

Emission factors for selected volatile organic compounds (VOCs) and particulate emissions were developed while processing eight commercial grades of polycarbonate (PC) and one grade of a PC/acrylonitrile-butadiene-styrene (ABS) blend. A small commercial-type extruder was used, and the extrusion temperature was held constant at 304 degrees C. An emission factor was calculated for each substance measured and is reported as pounds released to the atmosphere/million pounds of polymer resin processed [ppm (wt/wt)]. Scaled to production volumes, these emission factors can be used by processors to estimate emission quantities from similar PC processing operations.

Air Pollutants↗
PubMed2001

Development of emission factors for polyamide processing.

Emission factors for selected volatile organic compounds (VOCs) and particulate material were developed during processing of commercial grades of polyamide 6, polyamide 66, and polyamide 66/6 resins. A small commercial-type extruder was used, and melt temperatures ranged from 475 to 550 degrees F. An emission factor was calculated for each substance measured and is reported as pounds released to the atmosphere per million pounds of polymer resin processed. Scaled to production volumes, these emission factors can be used by processors to estimate emission quantities from similar polyamide extrusion operations.

Air Pollutants↗
PubMed1999

Testing of household products and materials for emission of toluene diisocyanate.

Polyurethane products were subjected to chamber testing to determine their emission rates of 2,4- and 2,6-toluene diisocyanate (TDI). The polyurethane (PU) products included carpet padding, furniture cushions, sheet foam, varnishes, and sealants, as well as a commercially-applied water sealant product for concrete that contained up to 4 percent TDI by weight. The PU products were screened in a 9-L glass chamber, under elevated temperature and chamber loading conditions, using both a time-integrated sampling and analysis method specific for TDI and a continuous but non-specific real-time monitor for isocyanates. None of the products normally found in residences showed a positive response in the screening tests, indicating that TDI emissions and consequently toxic effects from such products are negligible. However, the commercially-applied water sealant gave a positive response in the screening test. Further testing of that product at realistic temperatures showed initial TDI emission rates of about 300,000 micrograms/m2/hr, with emissions lasting only one hour or less. At 21 and 27 degrees C, about 1 percent and 5 percent, respectively, of the TDI content of the product was released to the air. The emitted TDI was predominantly the 2,6-isomer, although the TDI originally present in the product was predominantly the 2,4-isomer.

Air Pollution, Indoor↗