PubMed2007

[Chemically modified, ultra-hydrophilic titanium implant surfaces].

Recently, a chemically modified ultra-hydrophilic sand-blasted, large grit and acid-etched (modSLA) titanium surface has been introduced in order to enhance bone apposition. Indeed, preliminary preclinical and clinical data have indicated that modSLA implants may enhance bone apposition during early stages of wound healing. These positive effects on bone regeneration might be probably mainly due to the hydrophilic surface properties noted for modSLA which ensured a stabilization of the blood clot. The aim of the present review article is to evaluate, based on the currently available evidence, the potential impact of modSLA surfaces for implant dentistry.

Animals↗

PubMed2006

Bone regeneration in dehiscence-type defects at chemically modified (SLActive) and conventional SLA titanium implants: a pilot study in dogs.

OBJECTIVES: The aim of the present study was to evaluate bone regeneration in dehiscence-type defects at titanium implants with chemically modified (mod) and conventional sand-blasted/acid-etched (SLA) surfaces. MATERIAL AND METHODS: Standardized buccal dehiscence defects (height: 3 mm, width: 3 mm) were surgically created following implant site preparation in both the upper and lower jaws of four beagle dogs. modSLA and SLA implants were inserted bilaterally according to a split-mouth design. The animals were sacrificed after 2 and 12 weeks (n=2 animals each). Dissected blocks were processed for histomorphometrical analysis: defect length, new bone height (NBH), percent linear fill (PLF), percent of bone-to-implant contact (BIC-D) and area of new bone fill (BF). RESULTS: Wound healing at SLA implants was predominantly characterized by the formation of a dense connective tissue at 2 and 12 weeks, without significant increases in mean NBH, PLF, BIC-D or BF values. In contrast, modSLA implants exhibited a complete defect fill at 12 weeks following implant placement. In particular, histomorphometrical analysis revealed the following mean values at 12 weeks: NBH (3.2+/-0.3 mm), PLF (98%), BIC-D (82%) and BF (2.3+/-0.4 mm(2)). CONCLUSION: Within the limits of the present study, it was concluded that modSLA titanium surfaces may promote bone regeneration in acute-type buccal dehiscence defects at submerged implants.

Acid Etching, Dental↗

PubMed2006

Integrin beta1 silencing in osteoblasts alters substrate-dependent responses to 1,25-dihydroxy vitamin D3.

Surface microroughness increases osteoblast differentiation and enhances responses of osteoblasts to 1,25-dihydroxyvitamin D3 [1alpha,25(OH)2D3]. The observations that beta1 integrin expression is increased in osteoblasts grown on Ti substrates with rough microarchitecture, and that it is regulated by 1alpha,25(OH)2D3 in a surface-dependent manner, suggest that beta1 may play a role in mediating osteoblast response. To test this hypothesis, we silenced beta1 expression in MG63 human osteoblast-like cells using small interfering RNA (siRNA) and examined the responses of the beta1-silenced osteoblasts to surface microtopography and 1alpha,25(OH)2D3. To better understand the role of beta1, MG63 cells were also treated with two different monoclonal antibodies to human beta1 to block ligand binding. beta1-silenced MG63 cells grown on a tissue culture plastic had reduced alkaline phosphatase activity and levels of osteocalcin, transforming growth factor beta1, prostaglandin E2, and osteoprotegerin in comparison with control cells. Moreover, beta1-silencing inhibited the effects of surface roughness on these parameters and partially inhibited effects of 1alpha,25(OH)2D3. Anti beta1 antibody AIIB2 had no significant effect on cell number and osteocalcin, but decreased alkaline phosphatase; MAB2253Z caused dose-dependent decreases in cell number and alkaline phosphatase and an increase in osteocalcin. Effects of 1alpha,25(OH)2D3 on cell number and alkaline phosphatase were reduced and effects on osteocalcin were increased. These findings indicate that beta1 plays a major and complex role in osteoblastic differentiation modulated by either surface microarchitecture or 1alpha,25(OH)2D3. The results also show that beta1 mediates, in part, the synergistic effects of surface roughness and 1alpha,25(OH)2D3.

Animals↗

PubMed2006

Osteoblast-like cells are sensitive to submicron-scale surface structure.

OBJECTIVES: Studies showing that osteoblasts exhibit a more differentiated phenotype on rough titanium (Ti) surfaces and osteoclast-resorbed bone surfaces used materials characterized by average peak to valley distance (Ra). Other surface features impacting the cells include distance between peaks, curvature of the valleys, and relative distribution of flat and smooth regions. We used novel Ti surfaces prepared by electrochemical micromachining as models to examine specific contributions of individual design features to osteoblast response. Results show that micron-scale topography modulates cell number, cell morphology and prostaglandin E2 (PGE2). In the presence of the appropriate microtopography, submicron-scale rugosity modulates differentiation and transforming growth factor-beta1 (TGF-beta1) levels. In this study, we examined the role of different types of submicron-scale structures. MATERIAL AND METHODS: Thirty micrometer diameter craters on Ti disks were produced by photolithography resulting in an electropolished smooth surface, and arranged so that inside crater area vs. outside flat area was 6 (30/6). Submicron-scale structures were superposed by acid etching and porous anodization. Ra's were 700, 400, 60 nm on acid-etched, porous anodized and smooth 30/6 surfaces, respectively. RESULTS: MG63 osteoblast-like cells were sensitive to submicron-scale architecture. Cell morphology on anodized surfaces was similar to morphology on smooth surfaces, whereas on etched surfaces, cells had a more elongated differentiated shape. Cell number was greatest on smooth surfaces > anodized > etched. Osteocalcin and PGE2 were affected in a reverse manner. Active TGF-beta1 was greatest on etched 30/6 surfaces > anodized > smooth; latent TGF-beta1 was elevated on all rough surfaces. CONCLUSIONS: These results support our previous observations that submicron-scale structures modulate osteoblastic phenotype and show that the physical properties of the submicron-scale structures are important variables in determining osteoblast response to substrate topography.

Acid Etching, Dental↗

PubMed2005

Surface reactions of 4-aminothiophenol with heterobifunctional crosslinkers bearing both succinimidyl ester and maleimide for biomolecular immobilization.

Surface reactions of 4-aminothiophenol (4-ATP) with a series of heterogeneous crosslinkers containing both maleimide and succinimidyl ester groups were investigated with infrared reflection absorption spectroscopy (IRRAS) and X-ray photoelectron spectroscopy (XPS). Two types of surface reactions exist: (1) for most crosslinkers, a dominant reaction of amine and succinimidyl ester gave homogeneous maleimide-pendant surfaces; (2) for other crosslinkers, a side reaction between amine and maleimide, accompanying the main reaction, yielded heterogeneous surfaces with two linking groups, maleimide and succinimidyl ester. A typical example for the second case is the reaction of surface amines with N-succinimidyl-6-maleimidylhexanoate (SMH). Finally, a peptide, H-Gly-Arg-Gly-Asp-Ser-Pro-Cys-OH (GRGDSPC), was immobilized on the SMH-derived surface as a bridging structure through two linkages, cysteine thioether and glycine amide.

Aniline Compounds↗

PubMed2005

Synergistic interaction of topographic features in the production of bone-like nodules on Ti surfaces by rat osteoblasts.

The objective of this study was to study the responses of osteoblast-like cells to rough Titanium (Ti)-coated epoxy surfaces of differing topographic complexity. Four topographies were studied: polished (PO), coarse-blasted (CB), acid-etched (AE) and coarse-blasted+acid-etched (SLA). Rat osteoblasts were cultured on these surfaces and their morphology, thickness as well as the number and size of bone-like nodules measured. To determine cell shape and cell thickness, fluorescein-5-thiosemicarbazide was used to stain the cell components including the cell membrane, the stained cells were optically sectioned using epifluorescent microscopy and the optical sections were computationally reconstructed to obtain three-dimensional images in which cell volume and cell thickness could be determined. Similarly optical sections of bone-like nodules labeled with tetracycline were also reconstructed to determine their size. The different surface topographies were found to alter the thickness and morphology of osteoblasts cultured on these surfaces. Osteoblasts produced significantly more and larger nodules on SLA compared to other surfaces. Nevertheless and perhaps surprisingly, given the evidence in various cell populations that cell shape can affect cell differentiation, cell thickness was not directly correlated with an increase in bone-like nodule formation. Data were analyzed by factorial analysis of variance. In this way the primary effect of each surface treatment ( i.e. blasting and acid etching) could be assessed as well as their interaction. Both the acid etching and blasting processes significantly affected the number and size of bone-like nodules cultured on Ti surfaces. Moreover there were significant interaction effects indicating that surface topographic features can act synergistically to enhance bone formation. This result suggests that a useful approach to the optimization of surfaces for bone production could involve systematic investigation of combinations of processes each of which produces distinct surface topographical features.

Animals↗

PubMed2002

Use of Ti-coated replicas to investigate the effects on fibroblast shape of surfaces with varying roughness and constant chemical composition.

A two-stage replica technique with a subsequent titanium (Ti)-coating treatment was used to faithfully replicate topographies of polished, acid-etched, machined-like, finely blasted, coarsely blasted, coarsely blasted and acid-etched, and Ti plasma-sprayed Ti surfaces. The replicas were used to study the influence of different rough surface topographies on the response of human fibroblasts in vitro under conditions of constant surface chemistry for all surfaces. The surface topographies of the replicas were characterized using non-contact laser profilometry, scanning electron microscopy (SEM), and stereo-SEM, whereas surface chemistry was examined using X-ray photoelectron spectroscopy. Fibroblasts were trypsinized and plated onto the Ti-coated epoxy-resin replica surfaces for 24 h and observed with SEM. Fluorescein-5-thiosemicarbazide was used to stain the cell components including cell membrane, and the stained cells were optically sectioned using epifluorescent microscopy. The optical sections were computationally reconstructed to obtain three-dimensional images and cell volume and cell thickness determined. The different surface topographies were found to alter cell thickness and cell morphology. However, cell volume as computed from three-dimensional reconstructions was not affected by surface features. The results suggest that cells distort themselves to accommodate to rough surfaces but their volume is not significantly altered.

Cell Size↗