PubMed2004

Biodegradable polyesters reinforced with surface-modified vegetable fibers.

Flax fibers are investigated as reinforcing agents for biodegradable polyesters (Bionolle and poly(lactic acid) plasticized with 15 wt.-% of acetyltributyl citrate, p-PLLA). The composites are obtained either by high temperature compression molding fiber mats sandwiched between polymer films, or by batch mixing fibers with the molten polymer. Fibers in composites obtained by the latter method are much shorter (140-200 microm) than those of the mats (5,000 microm). Flax fibers are found to reinforce both p-PLLA and Bionolle (i.e. tensile modulus and strength increase) when composites based on fiber mats are investigated. Conversely, analogous composites obtained by batch mixing show poor mechanical properties. The observed behavior is attributed to the combined effect of fiber length and fiber-matrix adhesion. If flax fibers with a modified surface chemistry are used, the strength of short fiber composites is seen to improve significantly because the interface strengthens and load is more efficiently transferred. Appropriate surface modifications are performed by heterogeneous acylation reactions or by grafting poly(ethylene glycol) chains (PEG, molecular weight 350 and 750). The highest tensile strength of p-PLLA composites is reached when PEG-grafted flax fibers are used, whereas in the case of Bionolle the best performance is observed with acylated fibers.

Adipates↗

PubMedDate not supplied

Heterogeneous acylation of flax fibers. Reaction kinetics and surface properties.

Flax fibers composed mainly of cellulose were subjected to heterogeneous valerylation reaction. The progress of the chemical modification was assessed by transmission FTIR. The heterogeneous esterification reaction followed first-order kinetics, and a plateau was reached already after 30 min. The intensity of the FTIR hydroxyl absorption band (nu = 3400 cm(-1)) did not appreciably decrease during the acylation reaction, showing that only a small fraction of the fiber hydroxyls was involved in the reaction. The degree of valerate substitution (DS) at the fiber surface (50 A thick layer) was evaluated by means of ESCA. Surface valerylation increased with reaction time and leveled off at DS around 1 after 30 min, in agreement with the FTIR data. The chemically modified fibers maintain the Cellulose I crystal structure and the original crystallinity degree up to the longest reaction time investigated (180 min). Dynamic contact angle measurements showed that surface hydrophobicity as indicated by advancing contact angle rapidly increased upon valerylation reaching a plateau after about 10 min. Chemical modification does not appreciably alter fiber thermal stability (by TGA) and morphology (by SEM).

Acylation↗

PubMedDate not supplied

Structural study of poly(L-lactic acid) spherulites.

Spherulites of poly(L-lactic acid) (PLLA) and of its blends with atactic poly(3-hydroxybutyrate) (a-PHB, from 10 to 75 wt %) were investigated by microfocus X-ray diffraction using synchrotron radiation. Radial scans in 5 microm steps with 3 microm beam diameter were performed. In PLLA, tens of identical diffraction images were collected. The unit cell a-axis was radially oriented, and the other axes lacked any specific orientation. In contrast, all PLLA/a-PHB blends showed a periodic change of diffraction pattern with increasing distance from the spherulite center. In all cases, the a-axis lay along the radius, while the b- and c-axes rotated about a with a defined periodicity. The unit cell twisting frequency increased with a-PHB content and closely matched the band spacing observed by polarized optical microscopy, which changed from 250 to 60 microm when the amount of a-PHB increased from 10 to 75 wt %. Concomitantly, a gradual broadening of all X-ray reflections was observed.

Crystallization↗

PubMedDate not supplied

Biodegradation of chemically modified flax fibers in soil and in vitro with selected bacteria.

The extent and rate of degradation of flax (Linum usitatissimum) fibers, both in the native state and after surface chemical modification (acetylation or poly(ethylene glycol), PEG, grafting), was investigated under laboratory conditions in two different biodegrading environments. Degradation of the fibers under aerobic conditions by the action of the microorganisms present in soil is assessed with the ASTM 5988-96 method by monitoring carbon dioxide evolution. In vitro biodegradation experiments were carried out by exposing the fibers to a pure culture of Cellvibrio fibrovorans bacteria and measuring the mass loss as a function of time. Despite the complexity of the system, the results of degradation in soil were satisfactorily reproducible, although the absolute rates were found to change in different experiments using the same soil. The degradation rate of acetylated fibers in soil nearly equals that of unmodified fibers, whereas in the pure culture, acetylated fibers biodegrade slower than native fibers. The opposite happens with the PEG-grafted fibers, which degrade slower than unmodified flax in soil and at a comparable rate upon in vitro exposure to the bacterial culture. The different biodegradation kinetics observed in the two biodegrading environments were attributed to differences of biocenoses, abiotic factors, and biodegradation assessing methods. Nevertheless, the final extent of biodegradation was the same for modified and unmodified fibers both in soil and in the pure culture, showing that the surface chemical modifications applied do not significantly affect biodegradability of the flax fibers.

Biodegradation, Environmental↗

PubMedDate not supplied

Cocrystallization of random copolymers of omega-pentadecalactone and epsilon-caprolactone synthesized by lipase catalysis.

Random copolymers were prepared by Candida antarctica lipase B (Novozyme-435) catalyzed copolymerization of omega-pentadecalactone (PDL) with epsilon-caprolactone (CL). Over the whole composition range PDL-CL copolymers are highly crystalline (melting enthalpy by differential scanning calorimetry, above 100 J/g; crystallinity degree by wide-angle X-ray scattering, WAXS, 60-70%). The copolymers melt at temperatures that linearly decrease with composition from that of poly(omega-pentadecalactone) (PPDL; 97 degrees C) to that of poly(epsilon-caprolactone) (PCL; 59 degrees C). The WAXS profiles of PCL and PPDL homopolymers are very similar, except for the presence in PPDL of the (001) reflection at 2theta = 4.58 degrees that corresponds to a 19.3 angstroms periodicity in the chain direction. In PDL-CL copolymers the intensity of this reflection decreases with increasing content of CL units and vanishes at 50 mol % CL, as a result of randomization of the ester group alignment and loss of chain periodicity. PDL-CL copolymers crystallize in a lattice that gradually changes from that of one homopolymer to that of the other, owing to comonomer isomorphous substitution. Cocrystallization of comonomer units is also shown by a random PDL-CL copolymer obtained in a polymerization/transesterification reaction catalyzed by C. antarctica lipase B (Novozyme-435) starting from preformed PCL and PDL monomer.

Bacterial Proteins↗