Crystallization of indium tin oxide nanoparticles: from cooperative behavior to individuality.

The crystallization pathway of indium tin oxide nanoparticles during solvothermal synthesis in benzyl alcohol was investigated. The synthesis was stopped after different reaction times in the range of 1-24 h, and the structural and morphological characteristics of the products were analyzed by powder X-ray diffraction, electron microscopy, and UV/Vis spectroscopy. Interestingly, the crystallization mechanism does not proceed along a simple nucleation and growth pathway, but involves a two-step process. In the first 12 h an intermediate phase is formed, which consists of nanocrystallites 3-6 nm in size stabilized by an organic matrix. In this organic-inorganic network the nanoparticles are aligned into superstructures, but without any crystallographic orientation. After 12 h the intermediate phase is abruptly transformed into indium tin oxide nanoparticles with the bixbyite structure and with crystallite sizes of about 10-12 nm. This step is accompanied by the disappearance of the organic phase and the loss of the superstructure.

Colloids↗
PubMed2006

Organic reaction pathways in the nonaqueous synthesis of metal oxide nanoparticles.

Nonaqueous-solution routes to metal oxide nanoparticles are a valuable alternative to the known aqueous sol-gel processes, offering advantages such as high crystallinity at low temperatures, robust synthesis parameters and ability to control the crystal growth without the use of surfactants. In the first part of the review we give a detailed overview of the various solution routes to metal oxides in organic solvents, with a strong focus on surfactant-free processes. In most of these synthesis approaches, the organic solvent plays the role of the reactant that provides the oxygen for the metal oxide, controls the crystal growth, influences particle shape, and, in some cases, also determines the assembly behavior. We have a closer look at the following reaction systems in this order: 1) metal halides in alcohols, 2) metal alkoxides, acetates, and acetylacetonates in alcohols, 3) metal alkoxides in ketones, and 4) metal acetylacetonates in benzylamine. All these systems offer some peculiarities with respect to each other, providing many possibilities to control and tailor the particle size and shape, as well as the surface and assembly properties. In the second part we present general mechanistic principles for aqueous and nonaqueous sol-gel processes, followed by the discussion of reaction pathways relevant for nanoparticle formation in organic solvents. Depending on the system several mechanisms have been postulated: 1) alkyl halide elimination, 2) elimination of organic ethers, 3) ester elimination, 4) C--C bond formation between benzylic alcohols and alkoxides, 5) ketimine and aldol-like condensation reactions, 6) oxidation of metal nanoparticles, and 7) thermal decomposition methods.

Journal Article↗
PubMed2006

Oriented attachment and mesocrystals: non-classical crystallization mechanisms based on nanoparticle assembly.

In this review, we highlight particle based crystallization pathways leading to single crystals via mesoscopic transformation. In contrast to the classical mechanism of atom/molecule mediated growth of a single crystal, the particle mediated growth and assembly mechanisms are summarized as "non-classical crystallization", including exiting processes like oriented attachment and mesocrystal formation. Detailed investigations of non-classical crystallization mechanisms are a recent development, but evidence for these pathways is rapidly increasing in the literature. A major driving force for these investigations originates from biomineralization, because it seems that these crystallization routes are frequently applied by natural organisms. We give a non-exhaustive literature survey on these two mechanisms with a focus on recent examples and studies, which are dedicated to a mechanistic understanding. Furthermore, conditions are introduced for which these non-classical crystallization mechanisms can be expected, as they are always an alternative reaction pathway to classical crystallization.

Adsorption↗
PubMed2005

Growth and assembly of crystalline tungsten oxide nanostructures assisted by bioligation.

Here, we present a systematic study on the influence of the bioligand deferoxamine mesylate on the crystallization and assembly behavior of tungsten oxide in a soft-chemistry process. Without deferoxamine mesylate, this approach yields pseudo-single crystalline tungstite nanoplatelets consisting of a large number of crystallographically almost perfectly aligned primary crystallites. In the presence of a constant amount of deferoxamine, the particle morphology drastically changes with temperature, ranging from wormlike organic-inorganic hybrid nanostructures to single-crystalline tungsten oxide nanowires, highlighting the role of the bioligand in controlling the crystal growth and assembly behavior. The nanowires have a uniform diameter of about 1.3 nm, an aspect ratio of more than 500, and the structural flexibility of tungsten oxide. The presented process is based on the combination of biomimetic construction principles with nonaqueous sol-gel chemistry, thus combining the advantages of both tools, excellent control over particle morphology and high crystallinity at low temperature.

Journal Article↗
PubMed2005

Ligand functionality as a versatile tool to control the assembly behavior of preformed titania nanocrystals.

Nanoparticle powders composed of surface-functionalized anatase crystals with diameters of about 3 nm self-organize into different structures upon redispersion in water. The assembly is directed by a small amount of a low-molecular-weight functional ligand (the "assembler") adsorbed on the surface of the nanoparticles. The ligand functionality determines the anisotropy of the resulting structures. Multidentate ligands, such as trizma ((HOCH(2))(3)CNH(2)) and serinol ((HOCH(2))(2)CNH(2)), with a chargeable terminal group preferentially induce the formation of anisotropic nanostructures several hundreds of nanometers in total length, whereas all the other investigated ligands (ethanolamine H(2)N(CH(2))(2)OH, glycine hydroxamate H(2)NCH(2)CONHOH, dopamine (OH)(2)C(6)H(3)(CH(2))(2)NH(3)Cl, tris (HOCH(2))(3)CCH(3)) mainly lead to uncontrolled agglomeration. Experimental data suggests that the anisotropic assembly is a consequence of the water-promoted desorption of the organic ligands from the {001} faces of the crystalline building blocks together with the dissociative adsorption of water on these crystal faces. Both processes induce the preferred attachment of the titania nanoparticles along the [001] direction. The use of polydentate and charged ligands to functionalize the surface of nanoparticles thus provides a versatile tool to control their arrangement on the nanoscale.

Adsorption↗
PubMed2005

A general nonaqueous route to binary metal oxide nanocrystals involving a C-C bond cleavage.

A widely applicable solvothermal route to nanocrystalline iron, indium, gallium, and zinc oxide based on the reaction between the corresponding metal acetylacetonate as metal oxide precursor and benzylamine as solvent and reactant is presented. Detailed XRD, TEM, and Raman studies prove that, with the exception of the iron oxide system, where a mixture of the two phases magnetite and maghemite is formed, only phase pure materials are obtained, gamma-Ga(2)O(3), zincite ZnO, and cubic In(2)O(3). The particle sizes lie in the range of 15-20 nm for the iron, 10-15 nm for the indium, 2.5-3.5 nm for gallium, and around 20 nm for zinc oxide. GC-MS analysis of the final reaction solution after removal of the nanoparticles showed that the composition is rather complex consisting of more than eight different organic compounds. Based on the fact that N-isopropylidenebenzylamine, 4-benzylamino-3-penten-2-one, and N-benzylacetamide were the main species found, we propose a detailed formation mechanism encompassing solvolysis of the acetylacetonate ligand, involving C-C bond cleavage, as well as ketimine and aldol-like condensation steps.

Journal Article↗
PubMed2005

Synthesis of yttria-based crystalline and lamellar nanostructures and their formation mechanism.

A nonaqueous synthetic route for the preparation of a regular crystalline yttria mesostructure is presented. The reaction between yttrium alkoxides and benzyl alcohol results in the formation of a highly ordered lamellar nanocomposite consisting of yttria layers with a confined thickness of about 0.6 nm, separated from each other by organic layers of intercalated benzoate molecules. Doping with europium leads to strong red luminescence. The nanostructure formation proceeds via two reactions. A C--C bond formation occurs between benzyl alcohol and the isopropanolate ligand. At the same time, yttrium oxide catalyzes two low-temperature hydride-transfer reactions to form benzoic acid and toluene from benzyl alcohol via benzaldehyde, thus limiting the growth of the thickness of the lamellae.

Alcohols↗
PubMed2004

Nonaqueous and halide-free route to crystalline BaTiO3, SrTiO3, and (Ba,Sr)TiO3 nanoparticles via a mechanism involving C-C bond formation.

A novel nonaqueous route for the preparation of nanocrystalline BaTiO(3), SrTiO(3), and (Ba,Sr)TiO(3) has been developed. In a simple one-pot reaction process, the elemental alkaline earth metals are directly dissolved in benzyl alcohol at slightly elevated temperatures. After the addition of Ti(O(i)Pr)(4), the reaction mixture is heated to 200 degrees C, resulting in the formation of a white precipitate. XRD measurements prove the exclusive presence of the perovskite phase without any other crystalline byproducts such as BaCO(3) or TiO(2). TEM investigations reveal that the BaTiO(3) nanoparticles are nearly spherical in shape with diameters ranging from 4 to 5 nm. The SrTiO(3) particles display less uniform particle shapes, and the size varies between 5 and 10 nm. Lattice fringes observed in HRTEM measurements further prove the high crystallinity of the nanoparticles. Surprisingly, GC-MS analysis of the reaction solution after hydrothermal treatment shows that hardly any ether formation occurs during the BaTiO(3) synthesis. Instead, the presence of 4-phenyl-2-butanol in stoichiometric amounts gives evidence that the formation mechanism proceeds mainly via a novel pathway involving C-C bond formation between benzyl alcohol and the isopropanolate ligand.

Journal Article↗
PubMed2002

Benzyl alcohol and transition metal chlorides as a versatile reaction system for the nonaqueous and low-temperature synthesis of crystalline nano-objects with controlled dimensionality.

The reaction of transition metal chlorides with benzyl alcohol leads at low temperatures to oxidic nanostructures with low-dimensional particle shapes such as nearly spherical titania anatase nanoparticles, vanadium oxide nanorods, and tungsten oxide nanoplatelets. The process is simple, allows a scale-up in gram quantities, and leads to highly crystalline materials. Ethanol solutions containing tungsten oxide nanoparticles exhibit blue luminescence upon UV irradiation at room temperature.

Journal Article↗