Moon Jeong Park

Publications and source records attributed to Moon Jeong Park.

6 recordsLinked to original sources

PubMed2006

Transient solidlike behavior near the cylinder/disorder transition in block copolymer solutions.

A nearly symmetric polystyrene-block-polyisoprene diblock copolymer dissolved at a concentration of 40% in styrene-selective solvents exhibited a cylinder-to-disorder transition upon heating. The solvents used were diethyl phthalate (DEP) and 75:25 and 50:50 mixtures of DEP with di-n-butyl phthalate (DBP). In DEP, the most styrene-selective of the three solvents, rheological measurements indicated a distinct plateau in the temperature-dependent elastic modulus across the 8 degrees C interval above the order-disorder transition temperature, T(ODT) = 116 degrees C. Previous small-angle neutron scattering measurements in this regime indicated the equilibrium phase to be a liquidlike solution of approximately spherical micelles. An isothermal frequency sweep in this regime indicated a very long relaxation time. Annealing eventually led to the recovery of liquidlike rheological response, over a time scale of hours. Qualitatively similar phenomena were also observed in 75:25 DEP/DBP and 50:50 DEP/DBP solutions, except the fact that the temperature window of the transient response is narrow and the time scale for the recovery diminishes significantly. Neither small-angle X-ray scattering nor static birefringence gave any clear signature of the transient structure. The structure that leads to the transient rheological response is attributed to micellar congestion due to the slow relaxation of anisotropic micelles into an equilibrium distribution of micelles. Possible origins of the remarkable solvent selectivity dependence are also discussed.

Butadienes↗

PubMed2006

Effect of the casting solvent on the morphology of poly(styrene-b-isoprene) diblock copolymer/magnetic nanoparticle mixtures.

We investigate the effect of the casting solvent on the phase behavior of a cylinder-forming poly(styrene-b-isoprene) (PS-b-PI) diblock copolymer mixed with marginally selective gamma-Fe2O3 nanoparticles. Notably, for the mixtures of PS-b-PI/gamma-Fe2O3 nanoparticles cast with toluene, which is a neutral solvent for both PS and PI blocks, the latticelike aggregates of gamma-Fe2O3 nanoparticles, originating from magnetic dipole interactions, induce an intriguing transition from hexagonal cylinders to body-centered cubic spheres via undulated cylinders whereas the neat block copolymer does not show such an order-order transition. In contrast, when PI-selective hexane is used, the nanoparticles are selectively incorporated into the PI domains, and the microphase-separated hexagonal cylinder morphology gradually loses its long-range order upon increasing the nanoparticle concentration. The structural information obtained from small-angle X-ray scattering is also in good agreement with transmission electron microscopy images and differential scanning calorimetry results.

Journal Article↗

PubMed2005

Interplay between cubic and hexagonal phases in block copolymer solutions.

The phase behavior of a symmetric styrene-isoprene (SI) diblock copolymer in a styrene-selective solvent, diethylphthalate, was investigated by in situ small-angle X-ray scattering on isotropic and shear-oriented solutions and by rheology and birefringence. A remarkable new feature in this phase diagram is the coexistence of both body-centered cubic (bcc) and hexagonally close-packed (hcp) sphere phases, in a region between close-packed spheres (cps) and hexagonally packed cylinders (hex) over the concentration range phi approximately 0.33-0.45. By focusing on the transitions among these various ordered phases during heating and cooling cycles, we observed a strong hysteresis: supercooled cylinders persisted upon cooling. The stability of these supercooled cylinders is quite dependent on concentration, and for phi > or = 0.40, the supercooled cylinders do not revert to spheres even after quiescent annealing for 1 month. The spontaneous formation of spheres due to the dissociation of cylinders is kinetically hindered in this case, and the system is apparently not amenable to any pretransitional fluctuations of cylinders prior to the cylinder-to-sphere transition. This contrasts with the case of cylinders transforming to spheres upon heating in the melt. The application of large amplitude shear to the supercooled cylinders is effective in restoring the equilibrium sphere phases.

Journal Article↗

PubMed2004

Temperature-dependent micellar structures in poly(styrene-b-isoprene) diblock copolymer solutions near the critical micelle temperature.

The temperature dependence of the micelle structures formed by poly(styrene-b-isoprene) (SI) diblock copolymers in the selective solvents diethyl phthalate (DEP) and tetradecane (C14), which are selective for the PS and PI blocks, respectively, have been investigated by small angle neutron scattering (SANS). Two nearly symmetric SI diblock copolymers, one with a perdeuterated PS block and the other with a perdeuterated PI block, were examined in both DEP and C14. The SANS scattering length density of the solvent was matched closely to either the core or the corona block. The resulting core and corona contrast data were fitted with a detailed model developed by Pedersen and co-workers. The fits provide quantitative information on micellar characteristics such as aggregation number, core size, overall size, solvent fraction in the core, and corona thickness. As temperature increases, the solvent selectivity decreases, leading to substantial solvent swelling of the core and a decrease in the aggregation number and core size. Both core and corona chains are able to relax their conformations near the critical micelle temperature due to a decrease in the interfacial tension, even though the corona chains are always under good solvent conditions.

Journal Article↗

PubMed2004

Origin of the thermoreversible fcc-bcc transition in block copolymer solutions.

The thermoreversible fcc-bcc transition in concentrated block copolymer micellar solutions is shown to be driven by decreases in the aggregation number as the solvent penetrates the core, leading to a softer intermicelle potential. Small-angle neutron scattering measurements in a dilute solution are used to quantify the temperature-dependent micellar characteristics. The observed phase boundary is in excellent agreement with recent simulations of highly branched star polymers.

Journal Article↗

PubMed2004

Gelation of PEO-PLGA-PEO triblock copolymers induced by macroscopic phase separation.

The gelation behavior of aqueous solutions of poly(ethylene oxide-b-(DL-lactic acid-co-glycolic acid)-b-ethylene oxide) (PEO-PLGA-PEO) triblock copolymer containing short hydrophilic PEO end blocks is investigated using dynamic light scattering, rheology, small-angle neutron scattering (SANS), and differential scanning calorimetry (DSC). For polymer concentrations between 5 and 35 wt %, four distinct regions of the turbidity change depending on temperature were observed. Interestingly, in the turbid solution region, gel phase is formed for polymer concentrations above 14 wt % and an extremely slow relaxation was detected. In fact, a power law, which takes into account the dynamics of percolation clusters, dominates the correlation function. In rheological measurements, the local maximum in G' is observed at around the temperature of maximum turbidity. We further found that G" > G' and G' is highly dependent on frequency at the gel state implying viscoelastic characteristics, which is quite different from general concepts of gels, typically formed by the micellar packing. SANS profiles showing multiple peaks in the sol state rather than in the gel state as well as a DSC exotherm at the temperature of gels can also serve as the evidence of different gel states. Based upon the experimental data obtained in the present study, a new gelation mechanism induced by the macroscopic phase separation of triblock copolymers containing short hydrophilic PEO end blocks such as PEO-PLGA-PEO is proposed. The effect of the type ofhydrophobic middle blocks on the gelation is also discussed.

Journal Article↗