PubMed2006

Order and composition of methyl-carboxyl and methyl-hydroxyl surface-chemical gradients.

A detailed infrared and XPS characterization of surface-chemical gradients of dodecanethiol with 11-mercaptoundecanol or 11-mercaptoundecanoic acid self-assembled on gold, is reported. Gradients were prepared using a simple, two-step process previously reported from our laboratory, which involves a controlled immersion of a polycrystalline gold substrate in a dilute (5 microM) solution of one component and a subsequent back-filling with the other. FTIR measurements show that a single-component gradient of dodecanethiol is composed of disordered, liquidlike alkyl chain conformations. Such a gradient, when back-filled with a complementary thiol, having either a hydroxyl or carboxyl end-group, yields two-component gradients that show similar changes in wettability along their lengths. However, while gradients composed of methyl and hydroxyl end-groups show a well-ordered alkyl chain structure over their entire length, methyl-carboxyl gradients exhibit a greater conformational disordering toward the carboxyl-rich end.

Journal Article↗

PubMed2006

Submicrometer structure of surface-chemical gradients prepared by a two-step immersion method.

Lateral force microscopy and microdroplet density measurements have been used to examine the microstructure of surface-chemical gradients of thiols on gold, prepared by a two-step immersion method. A single-component coverage gradient, generated by gradual immersion of a gold surface into a solution of a single thiol, yielded islands of approximately 25 nm in diameter at the end that had only been briefly immersed, whereas an increasingly continuous film was formed along the gradient. After saturation with a second thiol with a different end group, the structure generated during the initial immersion step was found to persist.

Journal Article↗

PubMed2005

Effects of ionic strength and surface charge on protein adsorption at PEGylated surfaces.

PEGylated Nb2O5 surfaces were obtained by the adsorption of poly(L-lysine)-g-poly(ethylene glycol) (PLL-g-PEG) copolymers, allowing control of the PEG surface density, as well as the surface charge. PEG (MW 2 kDa) surface densities between 0 and 0.5 nm(-2) were obtained by changing the PEG to lysine-mer ratio in the PLL-g-PEG polymer, resulting in net positive, negative and neutral surfaces. Colloid probe atomic force microscopy (AFM) was used to characterize the interfacial forces associated with the different surfaces. The AFM force analysis revealed interplay between electrical double layer and steric interactions, thus providing information on the surface charge and on the PEG layer thickness as a function of copolymer architecture. Adsorption of the model proteins lysozyme, alpha-lactalbumin, and myoglobin onto the various PEGylated surfaces was performed to investigate the effect of protein charge. In addition, adsorption experiments were performed over a range of ionic strengths, to study the role of electrostatic forces between surface charges and proteins acting through the PEG layer. The adsorbed mass of protein, measured by optical waveguide lightmode spectroscopy (OWLS), was shown to depend on a combination of surface charge, protein charge, PEG thickness, and grafting density. At high grafting density and high ionic strength, the steric barrier properties of PEG determine the net interfacial force. At low ionic strength, however, the electrical double layer thickness exceeds the thickness of the PEG layer, and surface charges "shining through" the PEG layer contribute to protein interactions with PLL-g-PEG coated surfaces. The combination of AFM surface force measurements and protein adsorption experiments provides insights into the interfacial forces associated with various PEGylated surfaces and the mechanisms of protein resistance.

Adsorption↗

PubMed2005

Porcine gastric mucin (PGM) at the water/poly(dimethylsiloxane) (PDMS) interface: influence of pH and ionic strength on its conformation, adsorption, and aqueous lubrication properties.

We have investigated the influence of pH and ionic strength on the conformation of porcine gastric mucin (PGM) in bulk aqueous solution, its adsorption behavior onto poly(dimethylsiloxane) (PDMS) surfaces, and its lubricating behavior upon the self-mated sliding contact of a PDMS tribopair by means of circular dichroism (CD) spectroscopy, optical waveguide lightmode spectroscopy (OWLS), and pin-on-disk tribometry, respectively. In a low-concentration regime (1 mg/mL), where the formation of a mucus-gel is generally excluded, PGM is still observed to exhibit effective aqueous lubricating properties under specific conditions of acidic pH and low ionic strength. This behavior was closely correlated with specific conformations in the bulk solution as well as specific adsorption behavior at the water/PDMS interface. The lubrication mechanism of the self-mated sliding contact of PDMS by means of surface modification with PGM is discussed in terms of isoviscous-elastic/soft-elastohydrodynamic lubrication (soft-EHL).

Adsorption↗

PubMed2005

Printing chemical gradients.

We describe a method to exploit the mass-transfer limitations of microcontact printing for the fabrication of surfaces with well-defined, arbitrarily shaped composition variations. An analysis of the transport processes reveals that the printing of hexadecanethiol (HDT) from poly(dimethylsiloxane) is purely diffusion-controlled. Stamps with geometries that enhance surface-normal diffusion paths therefore allow not only the contours, but also the local density of self-assembled monolayers to be controlled. We use stamps with variable thickness and uniform ink concentration to print HDT density gradients on gold, depleting the stamps during the process. In the second step, a perfluorinated thiol fills the vacancies in the partial monolayer to form a two-component gradient that we analyze by means of X-ray photoelectron spectroscopy and spectroscopic ellipsometry. Linear and radial gradients are shown here as examples for a wide range of geometries that can be fabricated with high precision using the method.

Journal Article↗

PubMed2005

Relationship between interfacial forces measured by colloid-probe atomic force microscopy and protein resistance of poly(ethylene glycol)-grafted poly(L-lysine) adlayers on niobia surfaces.

Adsorbed layers of "comb-type" copolymers consisting of PEG chains grafted onto a poly(l-lysine) (PLL) backbone on niobium oxide substrates were studied by colloid-probe AFM in order to characterize the interfacial forces associated with coatings of varying architectures (PEG/PLL ratios and PEG chain lengths) and their relevance to protein resistance. The steric and electrostatic forces measured varied substantially with the architecture of the PLL-g-PEG copolymers. Varying the ionic strength of the buffer solutions enabled discrimination between electrostatic and steric-entropic contributions to the net interfacial force. For high PEG grafting densities the steric component was most prominent, but at low ionic strengths and high grafting densities, a repulsive electrostatic surface force was also observed; its origin was assigned to the niobia charges beneath the copolymer, as insufficient protonated amine groups in the PLL backbone were available for compensation of the oxide surface charges. For lower grafting densities and lower ionic strengths there was a substantial attractive electrostatic contribution arising from interaction of the electrical double layer arising from the protonated amine groups, with that of the silica probe surface (as under low ionic strength conditions, the electrical double layer was thicker than the PEG layer). For these PLL-g-PEG coatings the net interfacial force can thus be a markedly varying superposition of electrostatic and steric-entropic contributions, depending on various factors. The force curves correlate with protein adsorption data, demonstrating the utility of AFM colloid-probe force measurements for quantitative analysis of surface forces and how they determine interfacial interactions with proteins. Such characterization of the net interfacial forces is essential to elucidate the multiple types of interfacial forces relevant to the interactions between PLL-g-PEG coatings and proteins and to advance interpretation of protein adsorption or repellence beyond the oversimplified steric barrier model; in particular, our data demonstrate the importance of an ionic-strength-dependent minimum PEG layer thickness to screen the electrostatic interactions of charged interfaces.

Adsorption↗

PubMed2005

Diffusion of alkanethiols in PDMS and its implications on microcontact printing (muCP).

n-Alkanethiols HS-(CH2)n-CH3 such as hexadecanethiol (HDT, n = 15), octadecanethiol (ODT, n = 17), and eicosanethiol (ECT, n = 19) have been shown to provide highly protective etch resists on microcontact-printed noble metals. As the quality of the printed pattern strongly depends on the mobility of the ink compound, we focused on understanding the diffusion behavior of HDT, ODT, and ECT in poly(dimethylsiloxane) (PDMS) stamps. We used a commercial PDMS material (Sylgard184), which is commonly used for microcontact printing (muCP), and a custom-synthesized one with a higher modulus. On the basis of linear-diffusion experiments, which maintained realistic printing conditions, we showed that the ink transport in the stamp follows Fick's law of diffusion. We then determined the diffusion coefficient by analytical and numerical modeling of the diffusion experiments. Numerical calculations were carried out with the finite-difference method applying more realistic boundary conditions (ink adsorption). Values for the diffusion coefficients of the three ink compounds in the two different PDMS materials all are on the order of (4-7) x 10(-7) cm2 s(-1). The scope and limits of the mathematical models are discussed. To demonstrate the potential of such models for microcontact printing, we simulate multiple printing cycles of an inked stamp and compare the results with experimental data.

Journal Article↗

PubMed2004

Reduction of friction at oxide interfaces upon polymer adsorption from aqueous solutions.

Reduction of the interfacial friction for the contact of a silicon oxide surface with sodium borosilicate in aqueous solutions has been accomplished through the adsorption of poly(L-lysine)-graft-poly(ethylene glycol) on one or both surfaces. Spontaneous polymer adsorption has been achieved via the electrostatic attraction of the cationic polylysine polymer backbone and a net negative surface charge, present for a specific range of solution pH values. Interfacial friction has been measured in aqueous solution, in the absence of wear, and on a microscopic scale with atomic force microscopy. The successful investigation of the polymer-coated interfaces has been aided by the use of sodium borosilicate microspheres (5.1 microm diameter) as the contacting probe tip. Measurements of interfacial friction as a function of applied load reveal a significant reduction in friction upon the adsorption of the polymer, as well as sensitivity to the coated nature of the interface (single-sided versus two-sided) and the composition of the adsorbed polymer. These measurements demonstrate the fundamental opportunity for lubrication in aqueous environments through the selective adsorption of polymer coatings.

Journal Article↗