28 three-periodic nets with two kinds of vertex and one kind of edge are identified. Some of their crystallographic properties and their natural tilings are described. Restrictions on site symmetry and coordination number of such nets are discussed and examples of their occurrence in crystal structures are given.
A metal-organic great rhombicuboctahedron (termed MOP-18) was functionalized with extended alkyl chains and crystallized. It has 12 rigid square-shaped Cu2(CO2)4 paddle-wheel building units and 24 5-dodecoxybenzene-1,3-dicarboxylate links. MOP-18 is soluble in a variety of organic solvents, such as tetrahydrofuran, chloroform, and toluene, which enabled its assembly on graphite substrate and its observation by scanning tunneling microscopy.
Twelve zeolitic imidazolate frameworks (ZIFs; termed ZIF-1 to -12) have been synthesized as crystals by copolymerization of either Zn(II) (ZIF-1 to -4, -6 to -8, and -10 to -11) or Co(II) (ZIF-9 and -12) with imidazolate-type links. The ZIF crystal structures are based on the nets of seven distinct aluminosilicate zeolites: tetrahedral Si(Al) and the bridging O are replaced with transition metal ion and imidazolate link, respectively. In addition, one example of mixed-coordination imidazolate of Zn(II) and In(III) (ZIF-5) based on the garnet net is reported. Study of the gas adsorption and thermal and chemical stability of two prototypical members, ZIF-8 and -11, demonstrated their permanent porosity (Langmuir surface area = 1,810 m(2)/g), high thermal stability (up to 550 degrees C), and remarkable chemical resistance to boiling alkaline water and organic solvents.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
Saturation H2 uptake in a series of microporous metal-organic frameworks (MOFs) has been measured at 77 K. Saturation pressures vary between 25 and 80 bar across the series, with MOF-177 showing the highest uptake on a gravimetric basis (7.5 wt %) and IRMOF-20 showing the highest uptake on a volumetric basis at 34 g/L. These results demonstrate that maximum H2 storage capacity in MOFs correlates well to surface area, and that feasible volumetric uptakes can be realized even in highly porous materials.
Explore the source record for details and available documents.
The dihydrogen adsorption isotherms of eight metal-organic frameworks (MOFs), measured at 77 K up to a pressure of 1 atm, have been examined for correlations with their structural features. All materials display approximately Type I isotherms with no hysteresis, and saturation was not reached for any of the materials under these conditions. Among the six isoreticular MOFs (IRMOFs) studied, the catenated materials exhibit the largest capacities on a molar basis, up to 9.8 H(2) per formula unit. The addition of functional groups (-Br, -NH(2), -C(2)H(4)-) to the phenylene links of IRMOF-1 (MOF-5), or their replacement with thieno[3,2-b]thiophene moieties in IRMOF-20, altered the adsorption behavior by a minor amount despite large variations in the pore volumes of the resulting materials. In contrast, replacement of the metal oxide units with those containing coordinatively unsaturated metal sites resulted in greater H(2) uptake. The enhanced affinities of these materials, MOF-74 and HKUST-1, were further demonstrated by calculation of the isosteric heats of adsorption, which were larger across much of the range of coverage examined, compared to those of representative IRMOFs. The results suggest that under low-loading conditions, the H(2) adsorption behavior of MOFs can be improved by imparting larger charge gradients on the metal oxide units and adjusting the link metrics to constrict the pore dimensions; however, a large pore volume is still a prerequisite feature.
Metal-organic frameworks (MOFs) show high CO2 storage capacity at room temperature. Gravimetric CO2 isotherms for MOF-2, MOF-505, Cu3(BTC)2, MOF-74, IRMOFs-11, -3, -6, and -1, and MOF-177 are reported up to 42 bar. Type I isotherms are found in all cases except for MOFs based on Zn4O(O2C)6 clusters, which reveal a sigmoidal isotherm (having a step). The various pressures of the isotherm steps correlate with increasing pore size, which indicates potential for gas separations. The amine functionality of the IRMOF-3 pore shows evidence of relatively increased affinity for CO2. Capacities qualitatively scale with surface area and range from 3.2 mmol/g for MOF-2 to 33.5 mmol/g (320 cm3(STP)/cm3, 147 wt %) for MOF-177, the highest CO2 capacity of any porous material reported.
A variable temperature (5-300 K) single crystal Laue neutron diffraction study has been conducted, and the gas absorption sites within hydrogen-loaded Zn(4)O(1,4-benzenedicarboxylate) have been located.
Covalent organic frameworks (COFs) have been designed and successfully synthesized by condensation reactions of phenyl diboronic acid {C6H4[B(OH)2]2} and hexahydroxytriphenylene [C18H6(OH)6]. Powder x-ray diffraction studies of the highly crystalline products (C3H2BO)6.(C9H12)1 (COF-1) and C9H4BO2 (COF-5) revealed expanded porous graphitic layers that are either staggered (COF-1, P6(3)/mmc) or eclipsed (COF-5, P6/mmm). Their crystal structures are entirely held by strong bonds between B, C, and O atoms to form rigid porous architectures with pore sizes ranging from 7 to 27 angstroms. COF-1 and COF-5 exhibit high thermal stability (to temperatures up to 500 degrees to 600 degrees C), permanent porosity, and high surface areas (711 and 1590 square meters per gram, respectively).
The hindered rotor transitions of H(2) adsorbed in the chemically related and prototypical porous metal-organic frameworks IRMOF-1, IRMOF-8, IRMOF-11, and MOF-177 were studied by inelastic neutron scattering to gain information on the specifics of H(2) binding in this class of adsorbents. Remarkably sharp and complex spectra of these materials signify a diversity of well-defined binding sites. Similarities in the spectral features as a function of H(2) loading and correlations with recent crystallographic studies were used to assign transitions ranging in rotational barrier from <0.04 to 0.6 kcal/mol as corresponding to localized adsorption sites on the organic and inorganic components of these frameworks. We find that binding of H(2) at the inorganic cluster sites is affected by the nature of the organic link and is strongest in IRMOF-11 in accord with our adsorption isotherm data. The sites on the organic link have lower binding energies, but a much greater capacity for increases in H(2) loading, which demonstrates their importance for hydrogen uptake by these materials.
A metal-organic truncated octahedron (termed MOP-28) has been constructed from six rigid square-shaped Cu2(CO2)4 paddle-wheel building units and twelve 2,2':5',2' '-terthiophene-5,5' '-dicarboxylate (TTDC) linkers. TTDC linker in the cis,cis conformation provides the critical 90 degrees linkage for this unique construction. The porous structure of MOP-28 is maintained even after the removal of guest species, as evidenced by this compound's nitrogen sorption isotherm of Type I characteristics and unprecedented surface area (Langmuir surface area 1100 m2/g, BET surface area 914 m2/g) among materials composed of discrete molecules.
The primary adsorption sites for Ar and N2 within metal-organic framework-5, a cubic structure composed of Zn4O(CO2)6 units and phenylene links defining large pores 12 and 15 angstroms in diameter, have been identified by single-crystal x-ray diffraction. Refinement of data collected between 293 and 30 kelvin revealed a total of eight symmetry-independent adsorption sites. Five of these are sites on the zinc oxide unit and the organic link; the remaining three sites form a second layer in the pores. The structural integrity and high symmetry of the framework are retained throughout, with negligible changes resulting from gas adsorption.
Increased attention is being focused on metal-organic frameworks as candidates for hydrogen storage materials. This is a result of their many favorable attributes, such as high porosity, reproducible and facile syntheses, amenability to scale-up, and chemical modification for targeting desired properties. A discussion of several strategies aimed at improving hydrogen uptake in these materials is presented. These strategies include the optimization of pore size and adsorption energy by linker modification, impregnation, catenation, and the inclusion of open metal sites and lighter metals.
Explore the source record for details and available documents.
A strategy based on assembling metal ions and organic carboxylate links has been applied for the design and synthesis of a new class of porous, truncated tetrahedral and heterocuboidal polyhedra, whose pore size and functionality can be systematically varied. The synthesis of this series of metal-organic polyhedra (MOPs) employs sulfate-capped oxygen-centered iron-carboxylate trimers, Fe3O(CO2)3(-)(SO4)3, as rigid nodes separated by linear (phenyl, biphenyl, terphenyl, and tetrahydropyrene) or trigonal (benzenetriphenyl) links to yield five highly crystalline polyhedra of general formula [NH2(CH3)2]8[Fe12O4(-)(SO4)12(link)x(py)12].G (x = 6 for linear or 4 for trigonal, py = pyridine, G = guests). In this series, the size of each polyhedron has been varied from 20.0 to 28.5 A (on edge), and the corresponding pore diameter from 7.3 to 13.3 A. Gas sorption isotherms were measured for three members of this series to reveal significant uptake of gases (N2, Ar, CO2, H2, CH4) and benzene and exhibit Type I sorption behavior that is indicative of permanent porosity. The apparent surface areas for these compounds range from 387 to 480 m(2)/g.
Cationic and mixed-valent forms of Fe3O(CO2)6 trigonal prismatic clusters have been linked by ditopic links, namely, 1,4-benzenedicarboxylate (1,4-BDC) and 1,3-benzenedicarboxylate (1,3-BDC), to produce two 3-periodic metal-organic frameworks (MOFs), [Fe3O(1,4-BDC)3 (DMF)3][FeCl4] x (DMF)3 (MOF-235) and Fe3O(1,3-BDC)3 (py)3 x (py)0.5(H2O)1.5 (MOF-236) (DMF = N,N-dimethylformamide, py = pyridine), respectively. These MOFs exemplify a new, high-symmetry topology termed acs which we identify here as the default arrangement for linking trigonal prisms together.