Hydroxyapatite growth on anodic TiO2 nanotubes.

In the present work, we study the growth of hydroxyapatite formation on different TiO(2) nanotube layers. The nanotube layers were fabricated by electrochemical anodization of titanium in fluoride-containing electrolytes. To study various nanotube lengths, layers with an individual tube diameter of 100 nm were grown to a thickness of approximately 2 mum or 500 nm. The ability to form apatite on the nanotube layers was examined by immersion tests combined with SEM, XRD and FT-IR investigations. For reference, experiments were also carried out on compact anodic TiO(2) layers. The results clearly show that the presence of the nanotubes on a titanium surface enhances the apatite formation and that the 2-mum thick nanotube layer triggers deposition faster than the thinner layers. Tubes annealed to anatase, or a mixture of anatase and rutile are clearly more efficient in promoting apatite formation than the tubes in their "as-formed" amorphous state.

Coated Materials, Biocompatible↗
PubMed2005

Self-organized nanotubular oxide layers on Ti-6Al-7Nb and Ti-6Al-4V formed by anodization in NH4F solutions.

The present work reports the fabrication of self-organized porous oxide-nanotube layers on the biomedical titanium alloys Ti-6Al-7Nb and Ti-6Al-4V by a simple electrochemical treatment. These two-phase alloys were anodized in 1M (NH(4))(2)SO(4) electrolytes containing 0.5 wt % of NH(4)F. The results show that under specific anodization conditions self-organized porous oxide structures can be grown on the alloy surface. SEM images revealed that the porous layers consist of arrays of single nanotubes with a diameter of 100 nm and a spacing of 150 nm. For the V-containing alloy enhanced etching of the beta phase is observed, leading to selective dissolution and an inhomogeneous pore formation. For the Nb-containing alloy an almost ideal coverage of both phases is obtained. According to XPS measurements the tubes are a mixed oxide with an almost stoichiometric oxide composition, and can be grown to thicknesses of several hundreds of nanometers. These findings represent a simple surface treatment for Ti alloys that has high potential for biomedical applications.

Alloys↗