PubMed1996

Dentin contamination protection after mechanical preparation for veneering.

PURPOSE: To evaluate in vivo the efficacy in preventing post-operative sensitivity and bacterial invasion of primed dentin that was left unprotected for 4 days after laminate veneer preparation. MATERIALS AND METHODS: Twelve vital, periodontically involved anterior teeth were prepared for experimental laminate veneers and divided into three groups: (1) Control group, in which the prepared surfaces were left unprotected after preparation; (2) Prepared dentin surfaces were cleaned with Tubulicid Red Label and covered with Tubulitec Primer; (3) All-Bond 2 Primer was applied to the prepared dentin surface. Post-operative sensitivity was evaluated immediately and a second appointment, 4 days later. The teeth were then extracted and examined by SEM. RESULTS: The application of a primer (Groups 2 and 3) prevented all sensitivity. After 4 days, the teeth in Group 1 were still sensitive to air blasts. Bacterial penetration into the unprotected tubules was observed in Group 1, but not in Groups 2 and 3.

Adult↗

PubMed1995

Contraction gaps in Class II restorations with self-cured and light-cured resin composites.

PURPOSE: To evaluate in vitro the cervical gap formation in composite restorations in which an increment of autopolymerizing composite was interposed between the light-cured filling material and the dentin bonding system. Two different self-cured materials and two different adhesives were used and compared. MATERIALS AND METHODS: In 40 Class II cavity preparations with the gingival margins in dentin or cementum, an increment of either of two different autopolymerizing composites, Palfique or Bisfil 2B, was interposed between the light-cured filling material (Palfique Estelite) and either of two different dentin bonding systems, All-Bond and Superbond D (20 restorations each). The specimens were immersed in toluidine blue dye. A section was taken from each specimen and examined under an optical microscope. The extent of dye penetration was measured. The specimens were then stored in water for 1-4 months and replicas of the sections were examined by SEM. RESULTS: Good marginal adaptation was observed for All-Bond/Bisfil 2B in all the restorations. All-Bond/Palfique showed good adaptation in 7 out of 10 cases, the failures occurring between bonding agent and composite. Superbond D/Palfique and Superbond D/Bisfil 2B showed marginal gap formation in 8 out of 10 and in all the restorations respectively. In the latter, four gaps occurred between bonding agent and dentin. As a consequence, a very significant difference (P<0.001) was found between All-Bond and Superbond treatments; no significant difference was found between Bisfil 2B and Palfique in each group treated with either All-Bond or Superbond. After 1-4 months storage in water, hygroscopic expansion of the restorative materials reduced the total number of gaps and the efficacy of the treatments was no more significantly different.

Composite Resins↗

PubMed1994

Smear layer removal by root canal irrigants. A comparative scanning electron microscopic study.

The effect of six endodontic irrigants on smear layers created by hand instrumentation was evaluated in vitro in the middle and apical sections of 53 root canals. The irrigants evaluated were: 1% and 5% sodium hypochlorite, a combination of 24% phosphoric acid and 10% citric acid, 0.2%, 17%, and 3% ethylenediaminetetraacetic acid. After instrumentation and treatment with the respective irrigants, the root canal specimens were examined by scanning electron microscopy to determine the presence or absence of smear layer. The two sodium hypochlorite solutions did not remove the smear layer, even when 5% sodium hypochlorite was scrubbed on the dentinal walls. The 0.2% ethylenediaminetetraacetic acid solution was more effective than sodium hypochlorite, but it did not completely remove the smear layer, especially at the orifices of the dentinal tubules. The other three solutions effectively removed the smear layer, but no significant difference was found between them (p > 0.05). The solution of 3% ethylenediaminetetraacetic acid was as effective as phosphoric-citric acid and 17% ethylenediaminetetraacetic acid. Ethylenediaminetetraacetic acid, however, did not show the marked demineralizing effect on the dentinal walls and tubules as the acidic solution.

Adult↗

PubMed1991

[Resistance of cavity walls of composite filled teeth].

The purpose of this study was to evaluate whether etching, bonding and filling with composite a cavity increase tooth resistance to fracture, considering that in posterior teeth stressed cusps are likely to bend. MOD conservative cavities (isthmus width/intercuspal distance = 0.25) were made in 10 extracted upper premolars, filled with P30 (3M) and tested by using a MTS machine. A metal bar (5 mm in diameter and 10 mm in length) was employed to load the cusps and their fracture resistance was recorded. The control group consisted of 16 extracted upper premolars: MOD cavities were made in only 9 teeth, then filled with amalgam. As a result, MOD cavities treated with Scotchbond, filled with P30 and tested by a MTS machine don't seem to be more resistant to a static load than cavities filled with amalgam.

Bicuspid↗

PubMed1989