Dislocation-controlled perforated layer phase in a PEO- b-PS diblock copolymer.
Small angle x-ray analyses show that the shear-induced hexagonal perforated layer phase in a poly(ethylene oxide)- b-polystyrene diblock copolymer consists of trigonal (R3;m) twins and a hexagonal (P6(3)/mmc) structure, with trigonal twins being majority components. Transmission electron microscopy reveals that the hexagonal structure is generated through sequential intrinsic stacking faults on the second layer from a previous edge dislocation line, while the trigonal twins are formed by successive intrinsic stacking faults on neighboring layers due to the plastic deformation under mechanical shear.
Journal Article↗