Fatigue crack propagation behavior of ultra high molecular weight polyethylene under mixed mode conditions.

Analytical studies of the stresses on and within ultra high molecular weight polyethylene joint components suggest that damage modes associated with polyethylene fatigue failure are caused by a combination of surface and subsurface crack propagation. Fatigue crack propagation tests under mixed mode loading conditions were conducted on center-cracked tension specimens machined from extruded blocks of sterilized polyethylene in an attempt to determine how fatigue cracks change direction in this material. Cyclic testing was performed using a sinusoidal wave form at a frequency of 5 Hz and an R-ratio (minimum load/maximum load) of 0.15. Specimens had the notch oriented perpendicular to the direction of applied load and at angles of 60 degrees and 45 degrees to the loading direction. Numerical analyses were used to interpret the experimental test and to predict the fatigue behavior of polyethylene under mixed mode conditions. It was found that all cracks eventually propagated horizontally, regardless of the initial angle of inclination of the notch to the direction of applied cyclic load. In fact, the extent of the curvilinear crack growth was quite limited. An effective range of cyclic stress intensity factor was calculated for correlation with the rate of crack growth. The results followed a Paris relation, with crack growth rate linearly related to a power of the range of stress intensity, for all three crack orientations. The numerical analyses adequately modeled the experimental fatigue crack growth results.

Materials Testing↗

PubMed1994

Perioperative care of the pediatric trauma patient.

Children have specific emotional and physiological needs that are intensified when they sustain injuries that require surgery. Care of pediatric trauma patients includes the physiological considerations of airway management, hemodynamic stability, hypothermia, and physical size. Psychological considerations include enhancing coping skills, caring for children according to their developmental levels, and caring for family members. The perioperative nurse must be familiar with these pediatric trauma nursing principles to effectively meet the needs of children and their family members during times of trauma crisis.

Adolescent↗

PubMed1994

Post-irradiation aging of ultra-high molecular weight polyethylene.

A study was performed to determine the time-course of oxidative degradation and the extent to which the degradation proceeded through the bulk of ultra-high molecular weight polyethylene joint components that had been irradiated and stored on a shelf. Standardized cylindrical samples, taken from a single batch of extruded polyethylene, were cleaned, packaged, and sterilized according to protocols used for commercial joint-replacement components. After sterilization, the samples were stored in the packages for time-periods of one day to more than one year. At each interval studied, thin sections were cut as a function of depth into the bulk of the sample and were used to determine the density and the infrared spectra. Marked alterations in the density and the infrared spectra consistent with continuing oxidative degradation occurred throughout the year of storage on the shelf. The alterations were most severe near the surface of the samples.

Drug Stability↗

PubMed1994

An analysis of the head-neck taper interface in retrieved hip prostheses.

The purpose of this study was to examine the mating surfaces of femoral heads and stems for evidence of corrosion, and to evaluate the quality of the taper lock of modular hip prostheses. Forty-eight implants with three different designs were evaluated. Group I (26 implants) had a cobalt alloy head and cobalt alloy stem. Group II (ten implants) had a cobalt alloy head and a titanium stem. Group III (12 implants) had a cobalt alloy head with a titanium stem that was coupled in the factory via a shrink fit. The implants were examined under light microscopy and scanning electron microscopy. In cases where the femoral head was still assembled to the stem, pull-off testing was performed using an MTS machine. The average failure load for the pull-off tests for each group of prostheses was as follows: Group I (nine implants) 3,003 N +/- 623 N; Group II (six implants) 4453 N +/- 570 N; and Group III (12 implants) 6859 N +/- 3525 N. The Group III implants required a significantly greater pull-off force than those in Group I (p = 0.002). There was no evidence of corrosion in Group I. In Group II, crevice corrosion was noted in one taper interface and there was fretting in two other tapers. No corrosion was noted in Group III. Improving the tolerances of the mating surfaces may be a key factor in preventing corrosion. This would not only increase the forces that are necessary to debond the matting surfaces, but also decrease corrosion by reducing micromotion and fluid at the taper interface.

Adult↗

PubMed1992

Wear of polyethylene in total joint replacements. Observations from retrieved PCA knee implants.

Observations of wear damage were performed on 12 retrieved porous coated anatomic (PCA) tibial components, all of which were removed because of excessive polyethylene wear. Density measurements of the remaining polyethylene were obtained as a function of depth from the surface of the components. Comparison to previous results from similar studies of total condylar type knee components and total hip acetabular components revealed distinct differences between the types and severity of damage, emphasizing the influence of design factors on the corresponding wear damage. These results confirm previous conclusions that nonconforming articulating surfaces on thin polyethylene components will be at higher risk of damage than more conforming surfaces on thicker components. It also appears that the high cyclic loads to which polyethylene implants are subjected in vivo are most responsible for the degradation in properties of the material near the articulating surface, although the heat pressing of the articulating surface of the PCA components may contribute to the problem.

Aged↗

PubMed1982

Prosthetic programme after above-knee amputation in children with sarcomata.

A programme for early mobilisation using a temporary prosthesis was evaluated in 17 children who had had an amputation above the knee for sarcomata. The temporary prosthesis had a performed adjustable polypropylene quadrilateral socket which was able to accommodate changes in the size of the stump during the first few months after amputation. The adjustable sockets were assembled onto wooden knee-shank-foot units or onto modular components covered with foam. The wooden units were better for routine use as more adjustment was possible between the socket and the knee and because they were more durable in active children. Prosthetic fitting usually took one hour and was carried out 10 days after the amputation to coincide with the start of the chemotherapy programme. The prosthesis was cosmetically acceptable, easy to use and provided a simple and economical way of rehabilitating the amputees and restoring their morale. After two to three months a new prosthesis with a laminated socket suspended by a waistband was supplied. The skin tolerated the closer fit of this socket and the small fluctuations in the size of the stump that occurred with each course of chemotherapy were easily accommodated by varying the thickness of the stump sock. A self-suspending laminated socket was provided after completion of the chemotherapy. The permanent sockets were assembled onto wooden components but the girls usually preferred the modular system covered with foam. The chemotherapy and rehabilitation programmes were successfully co-ordinated so that the children spent as little time as possible away from their normal activities.

Adolescent↗

PubMed1972