Adhesion between Nanoscale Rough Surfaces.

Nanoscale surface roughness strongly affects the adhesion force between surfaces. In this investigation, a model that more accurately describes the size of an asperity based on the measurable parameters of root-mean-square (rms) roughness and the distance between the asperities is derived. The radius of the asperity from the proposed model is much larger than the radius used in previous approaches, considering the same surface with nanoscale roughness. Using the proposed geometry and previously suggested models, this paper elucidates the contributions from contact and noncontact interactions of a particle adhered to a surface with nanoscale roughness (approximately less than 20 nm rms). For most surfaces considered, the contact interaction of the asperity and the adhering particle are found to dominate the interaction. In the second paper of this series, the proposed model is compared to the experimentally determined force of adhesion in systems with nanoscale roughness. Copyright 2000 Academic Press.

Journal Article↗
PubMed2000

Adhesion between Nanoscale Rough Surfaces.

In this investigation, the adhesion between particles and plates with root-mean-square, rms, surface roughness of 0.17-10.5 nm was measured by atomic force microscopy. Measurements obtained with particles both larger and smaller than the surface asperities are presented. Results indicate adhesion force decreases sharply with increasing surface roughness in the nanometer scale (<2 nm), followed by a gradual and slow decrease with further increase in roughness. Existing models were found to significantly underestimate adhesion force. Hence, a new model based on a geometry that considers both the height and breadth of asperities yielding an increased asperity radius compared to previous approaches, as detailed in Part I of this series, is applied using both van der Waals and elastic deformation/work of adhesion based approaches. For the system studied in this investigation, the adhesion forces predicted by the proposed model are considerably more accurate than those predicted by past models. Copyright 2000 Academic Press.

Journal Article↗
PubMed2000

Synthesis of Microporous Silica Spheres.

Spherical microporous silica powders with a narrow size distribution have been prepared by a precipitation technique involving the hydrolysis reaction of a silicon alkoxide in ethanol. The formation of the important microporosity has been investigated following two templating methods: the co-hydrolysis and condensation of two alkoxides, one of which presents porogen function, and the adsorption of an organic compound (glycerol) as the porogen. In both processes, the organic porogen is removed by a simple calcination. In the first method, the addition of more than 20 mol% of the porogen alkoxide, necessary for generating enough microporosity, disturbs completely the condensation process resulting in microporous, nonuniform silica particles of large size distribution. The best result has been obtained with the glycerol method where submicrometer-sized silica spheres with a very narrow size distribution and about 40 vol% porosity have been synthesized. The presence of glycerol during the synthesis considerably affects the precipitation mechanism, resulting in a larger mean particle size. The use of an aggregative growth model has successfully been employed to explain the effect of the porogen during particle formation. The precipitation mechanism of silica involves the aggregation between particles of similar size until a critical size is reached, resulting in a uniform particle size distribution. In the presence of glycerol, it has been shown that a second aggregative growth between still-nucleating primary particles and large particles occurred with increasing reaction time. This second aggregative growth appears at an intermediate stage of the precipitation process and is due to both the precipitation of smaller primary particles and the destabilization of the colloidal stability of the system. This explains why the final particle size reached in this system is larger compared to silica particles synthesized without glycerol and shows how glycerol is incorporated in the silica particles. The synthesis of silica microporous spheres of narrow size distribution, by varying particle size and porosity, should yield a wide range of aqueous silica slurries for particular chemical mechanical polishing applications. Copyright 2000 Academic Press.

Journal Article↗