PubMed2005

The biocompatibility of dibutyryl chitin in the context of wound dressings.

Dibutyryl chitin (DBC) is a modified chitin carrying butyryl groups at 3 and 6 positions; its peculiarity is that it dissolves promptly in common solvents, while being insoluble in aqueous systems. The high biocompatibility of dibutyryl chitin in the form of films and non-wovens has been demonstrated for human, chick and mouse fibroblasts by the Viability/Cytotoxicity assay, In situ Cell Proliferation assay, Neutral Red Retention assay, Lactate Dehydrogenase Release assay, MTS cytotoxicity assay, and scanning electron microscopy. DBC was hardly degradable by lysozyme, amylase, collagenase, pectinase and cellulase over the observation period of 48 days at room temperature, during which no more than 1.33% by weight of the DBC filaments (0.3 mm diameter) was released to the aqueous medium. DBC non-wovens were incorporated into 5-methylpyrrolidinone chitosan solution and submitted to freeze-drying to produce a reinforced wound dressing material. The latter was tested in vivo in full thickness wounds in rats. The insertion of 4x4 mm pieces did not promote any adverse effect on the healing process, as shown histologically. DBC is therefore suitable for contacting intact and wounded human tissues.

Amylases↗

PubMed2003

Alkaline chitosan solutions.

Rigid and transparent hydrogels were obtained upon pouring chitosan salt solutions into saturated ammonium hydrogen carbonate. Incubation at 20 degrees C for 5 days yielded chitosan carbamate ammonium salt, Chit-NHCO(2)(-)NH(4)(+) a chemical species that either by hydrolysis or by thermal treatment decomposed to restore chitosan in free amine form. Chitosans of different degrees of acetylation, molecular sizes and origins (squid and crustaceans) were used as hydrochloride, acetate, glycolate, citrate and lactate salts. Their hydrogels obtained in ammonium hydrogen carbonate yielded chitosan solutions at pH values as high as 9.6, from which microspheres of regenerated chitosans were obtained upon spray-drying. These materials had a modest degree of crystallinity depending on the partial acylation that took place at the sprayer temperature (168 degrees C). Citrate could cross-link chitosan and impart insolubility to the microspheres. Chloride on the contrary permitted to prepare microspheres of chitosan in free amine form. By the NH(4)HCO(3) treatment, the cationicity of chitosan could be reversibly masked in view of mixing chitosan with alginate in equimolar ratio without coacervation. The clear and poorly viscous solutions of mixed chitosan carbamate and alginate were spray-dried at 115 degrees C to manufacture chitosan-alginate microspheres having prevailing diameter approx 2 micron.

Alginates↗

PubMed2002

Natural and artificial chitosan-inorganic composites.

Taking inspiration from many chitin-inorganic composites in nature, a number of recent articles throw light on the manufacture of such composites based on calcium carbonate, calcium phosphate and silica. These novel materials are important in the field of blood-compatible materials, bone substitutes, and cements for bone repair and reconstruction. This approach provides an attractive alternative to the processing of inorganic thin films, especially in applications where substrates cannot be exposed to high temperatures.

Animals↗