PubMed2006

Effect of simulated pulpal pressure on all-in-one adhesive bond strengths to dentine.

OBJECTIVES: To evaluate the durability of all-in-one adhesive systems bonded to dentine with and without simulated hydrostatic pulpal pressure (PP). METHODS: Flat dentine surfaces of extracted human molars were prepared. Two all-in-one adhesive systems, One-Up Bond F (OBF) (Tokuyama Corp., Tokyo, Japan), and Fluoro Bond Shake One (FBS) (Shofu Co., Kyoto, Japan) were applied to the dentine surfaces under either a PP of 0 or 15cm H(2)O. Then, resin composite build-ups were made. The specimens bonded under pressure were stored in 37 degrees C water for 24h, 1 and 3 months under 15cm H(2)O PP. Specimens not bonded under pressure were stored under zero PP. After storage, the specimens were sectioned into slabs that were trimmed to hourglass shapes and subjected to micro-tensile bond testing (muTBS). The data were analysed using two-way ANOVA and Holm-Sidak HSD multiple comparison tests (alpha=0.05). RESULTS: The muTBS of OBF fell significantly (p<0.05) when PP was applied during bonding and storage, regardless of storage time. In contrast, although the muTBS of OBF specimens bonded and stored without hydrostatic pressure storage fell significantly over the 3 months period, the decrease was less than half as much as specimens stored under PP. In FBS bonded specimens, although there was no significant difference between the muTBS with and without hydrostatic pulpal pressure at 24h, by 1 and 3 months of storage under PP, significant reductions were seen compared with the control group without PP. CONCLUSION: The muTBS of OBF bonded specimens was lowered more by simulated PP than by storage time; specimens bonded with FBS were not sensitive to storage time in the absence of PP, but showed lower bond strengths at 1 and 3 months in the presence of PP.

Composite Resins↗

PubMed2006

Mechanical properties and bond strength of dual-cure resin composites to root canal dentin.

OBJECTIVES: To evaluate the regional mechanical properties of dual-cure resin composites and their regional bond strengths to root canal dentin. METHODS: One of the following dual-cure resin composites was placed in artificial post spaces: Unifil Core (UC), Clearfil DC Core (DC), Build-It FR (BI), Clearfil DC Core-automix (DCA), and photo-cured for 60s. After 24h storage, each specimen was serially sliced to harvest eight hour-glass shaped specimens for measurement of regional ultimate tensile strength (UTS), and the remaining eight semi-circular slabs were polished for the measurement of Knoop Hardness Number (KHN). For the microtensile bond strength (muTBS) test, post cavities were prepared in human premolar roots, and the cavity surfaces treated with Clearfil SE Bond and photo-cured for 10s. The post spaces were then filled with one of the above resin composites and photo-cured for 60s. After 24h storage, each specimen was serially sliced into 8, 0.6x0.6 mm-thick beams for the muTBS test. The data were divided into coronal and apical regions and analyzed using ANOVA and post hoc test (alpha=0.05). RESULTS: UTS and KHN were affected by the type of dual-cure resin composite and region (p<0.0001). There was no relationship between UTS and KHN for each material. The auto-mix type of resin composite possessed superior UTS to that of the hand-mix type. muTBS among the four composite materials were not significantly different at both apical and coronal regions (p>0.05). Regional differences in bond strengths were found for all materials (p<0.05). SIGNIFICANCE: The UTS and KHN of the dual-cure resin composites varied among each material, however, differences in the mechanical properties of the resin core materials did not affect their adhesion to root canal dentin.

Composite Resins↗

PubMed2006

Adhesive restoration of endodontically treated teeth--current research.

UNLABELLED: Restoring endodontically-treated teeth using adhesively cemented fibre posts is becoming popular in general practice. Clinical studies have been promising, however failures can occur, usually because of de-bonding of the post. Current research, aimed at identifying factors that could improve the adhesion of fibre posts, is described. CLINICAL RELEVANCE: Adhesively-retained fibre posts are becoming a popular choice for the restoration of endodontically treated teeth. Dental practitioners should be knowledgeable on the rationale behind these restorations, factors that can lead to failure, and ongoing developments.

Adhesives↗

PubMed2006

Effect of curing method and storage condition on fluoride ion release from a fluoride-releasing resin cement.

The purpose of this study was to evaluate fluoride ion release from a resin-modified glass ionomer cement (Fuji IILC improved, FLC) and a fluoridated resin cement (Panavia F, PF) following different curing methods and storage conditions. The specimens, which were either light-cured (LC) or chemical-cured (CC), were stored in either distilled water (DW) or demineralizing solution (DS; pH 4.5) for 1, 3, 7, 15, 30, 60, and 90 days. Fluoride ion release was measured using a fluoride ion-specific electrode. Data (n = 5) were statistically analyzed using one- and three-way ANOVA (p = 0.05). A "burst effect" was observed in the first week from both materials. However, fluoride ion release from FLC was seven times higher than that from PF. Storage in demineralizing solution accelerated the amount of fluoride release from both materials. In addition, LC yielded a lower amount of fluoride ion release from both materials, as compared to CC. It was concluded that both curing mode and storage medium influenced the amount of fluoride release from the tested materials.

Analysis of Variance↗

PubMed2006

Effect of resin coating on adhesion of composite crown restoration.

The purpose of this study was to evaluate the effect of a resin coating technique on the microtensile bond strength (microTBS) of resin cement to dentin in composite crown restorations. Crown preparations were done on human molars. A resin coating material, Hybrid Bond, was immediately applied to the prepared dentin and light-cured, while the tooth without resin coating acted as the control. An impression of the resin-coated tooth was taken, and a composite crown fabricated on the working cast. The composite crown was then bonded with a resin cement, Chemiace II. MicroTBSs were measured at a crosshead speed of 1 mm/min, and the resin-coated group yielded significantly higher microTBSs than the non-coated group (p < 0.05). In terms of microTBS values between the axial and occlusal surfaces, no regional differences in resin-dentin bond strength were detected (p < 0.05). It was concluded that resin coating with Hybrid Bond significantly improved the microTBS of resin cement to dentin in composite crown restorations.

Analysis of Variance↗

PubMed2006

Effect of incremental filling technique on adhesion of light-cured resin composite to cavity floor.

The purpose of this study was to evaluate the effect of various incremental filling techniques on adhesion between composite and cavity floor using light-cured resin composite. Black ABS resin and hybrid resin composite were used as mold materials--instead of dentin--for the preparation of cavities, and standardized to 5x5x5 mm. Each cavity was then treated with a bonding system (Clearfil SE bond). Resin composite (Clearfil Photo Core) was placed on the bonding resin using different incremental filling techniques or in bulk and irradiated for a total of 80 seconds using a halogen light unit. Specimens were subjected to the micro-tensile bond test at a crosshead speed of 1 mm/min. Data were analyzed by two-way ANOVA. The results indicated that an incremental filling technique was more effective in improving adhesion to the cavity floor than a bulk filling technique.

Acrylic Resins↗

PubMed2006

Influence of elasticity on gap formation in a lining technique with flowable composite.

The purpose of this study was to investigate the effect of flowable composites as liners for direct composite restorations, with key focus on the elastic moduli of flowable and condensable composites. After treating the composite mold cavity surface with an adhesive system, one of the flowable composites was placed as a 1 mm-thick layer on the cavity floor and irradiated for 20 seconds. The rest of cavity was subsequently filled with a condensable composite and irradiated for 40 seconds. Gap formation at both interfaces--between the cavity floor and flowable composite, and between the flowable and condensable composites--was examined. No gaps were detected at the interface between the cavity floor and flowable composite. Gap percentage at the interface between the flowable and condensable composites was dependent on the difference in elastic modulus. It was concluded that flowable composite with high elastic modulus could inhibit gap formation between flowable and condensable composites.

Acrylic Resins↗

PubMed2006

Coronal leakage inhibition in endodontically treated teeth using resin-coating technique.

The purpose of this study was to evaluate coronal leakage inhibition using a resin-coating technique after endodontic treatment. Thirty-six human incisors were cut at the cementoenamel junction, and endodontic obturations were performed. The specimens were randomly divided into three groups according to post space preparation (10 mm depth), resin coating, and temporization. For the resin coating, the dentin surface was coated with either a combination of Clearfil SE Bond and Protect Liner F (SE/PLF) or RZII (RZ). Then, the specimens were stored in 37 degrees C distilled water for 24 hours and placed in 1% methylene blue solution for 48 hours. After which, the specimens were sectioned faciolingually along the root canal and the length of dye penetration was measured from the cementoenamel junction. Three-way ANOVA revealed that the dye penetration scores were influenced by post space preparation, resin coating, and temporization. Resin coating with RZ significantly reduced the dye penetration score and SE/PLF completely eliminated dye penetration.

Analysis of Variance↗

PubMed2006

Regional bond strengths of a dual-cure resin core material to translucent quartz fiber post.

PURPOSE: To evaluate the microtensile bond strength (muTBS) of a dual-cure resin core material to different regions of translucent quartz fiber post in a post cavity using different surface treatments. METHODS: 30 translucent quartz fiber posts (Light-Post) were used and divided into six groups according to the surface treatments: (1) no surface treatment (Control); (2) photo-cure bonding agent, Clearfil Liner Bond 2V Bond A (PLB); (3) dual-cure bonding agent, Clearfil Liner Bond 2V Bond A+B (DLB); (4) BdA+B followed by light-cured for 20 seconds (DLB & LC); (5) silane coupling bonding agent, Clearfil Photobond with Porcelain Bond Activator (PB+PBA); (6) PB+PBA followed by light-cure for 20 seconds (PB+PBA&LC). Treated post were cemented into artificial post cavities using a dual-cure composite core material (Clearfil DC Core) and light-cured for 60 seconds from the top of the cavity. After 24-hour storage in water, each specimen was serially sliced into twelve 0.6 x 0.6 mm-thick beams for the muTBS test. The data were divided into three regions (upper/middle/bottom) and analyzed using two-way ANOVA and Dunnet's T3 multiple comparisons (alpha = 0.05). RESULTS: The highest bond strength was present in the silane coupling bonding agent group for all regions (P < 0.05). Application of the bonding agent to the post surface significantly improved the bond strength compared with control (P < 0.05). There were no significant differences in muTBS at all regions between the photo and dual-cure type bonding agents (P < 0.05). The bond strength significantly decreased at the bottom region when the post surface was treated with bonding agents (P < 0.05), whereas no regional differences in bond strength were found in the silane coupling bonding agent group (P > 0.05).

Composite Resins↗

PubMed2006

Bonding durability of a self-etching primer system to normal and caries-affected dentin under hydrostatic pulpal pressure in vitro.

PURPOSE: To evaluate the bonding durability of a self-etching primer system to normal and caries-affected dentin under hydrostatic pulpal pressure. METHODS: 18 extracted human molars with occlusal caries were used. Their occlusal dentin surfaces were ground flat to expose normal and caries-affected dentin using #600 SiC paper under running water. Clearfil SE Bond was placed on the dentin surface including the caries-affected dentin according to the manufacturer's instructions and then the crowns were built up with resin composite (Clearfil AP-X) under either a pulpal pressure of 15 cm H2O or none (control). The bonded specimens were stored in 100% humidity for 1 day (control) or for 1 week and 1 month with hydrostatic pulpal pressure. After storage, the specimens were serially sectioned into 0.7 mm-thick slabs and trimmed to an hour-glass shape with a 1 mm2 cross-section, isolated by normal or caries-affected dentin, and then subjected to the micro-tensile bond test. Data were analyzed by two-way ANOVA and Tukey's test (P< 0.05). RESULTS: Hydrostatic pulpal pressure significantly reduced the bond strength to normal dentin after 1-month storage (P< 0.05), but did not affect the bond strength to caries-affected dentin.

Analysis of Variance↗

PubMed2006

Pulpal response to a newly developed MMA based resin cement for bonding tooth-colored indirect restorations.

PURPOSE: To evaluate the pulpal responses to a newly-developed MMA-based self-etch resin cement, when used as a luting agent for indirect resin composite restoration, and to compare the results with those obtained from a total-etch luting agent, glass-ionomer cement, and amalgam restoration. METHODS: 120 cervical cavities were prepared in monkey teeth and divided into four equal groups according to the restorative materials used: (1) the cavities were restored with resin composite inlays using a self-etch resin cement as a luting agent (M-Bond); (2) the cavities were also restored with resin composite inlays but using a total-etch resin cement as a luting agent (Super-Bond C & B); (3) the cavities were directly restored with glass-ionomer cement (Fuji II); or (4) the cavities were directly restored with amalgam (Dispersalloy). The restored teeth were extracted at 3, 30, or 90 days after restoration, then fixed in 10% neutral buffered formalin. The specimens were prepared using routine histopathological procedures. Five microm-thick sections were stained with hematoxylin and eosin or Brown & Brenn gram stain for bacterial observations. Histological responses in the pulpal tissue and bacterial penetration were observed under a light microscope and evaluated using standard scores. The results were statistically analyzed using the Kruskal-Wallis test (P< 0.05). RESULTS: At all time intervals, no significant differences of pulpal inflammatory responses between M-Bond and Super-Bond C&B were observed (P> 0.05). Both resin cements showed no serious pulpal responses, such as necrosis or abscess formation. In general, both MMA-based resin cements showed similar pulpal responses to those of glass-ionomer cement except for congestion of pulpal blood vessels at 3 days after restoration in which glass-ionomer cement exhibited a lower level than that of the MMA-based resin cements. For the group restored with amalgam, at 3 days after restoration, severe odontoblastic disorders and blood vessel congestions with a large infiltration of inflammatory cells were detected. At 30 and 90 days after restoration, slightly inflammatory irritations were observed irrespective of the materials used. Reparative dentin formation and bacterial penetration were found mostly in the group restored with amalgam.

Analysis of Variance↗

PubMed2005

Effect of prolonged photo-irradiation time of three self-etch systems on the bonding to root canal dentine.

OBJECTIVES: To evaluate the effect of photo-irradiation time to the adhesive on the regional bond strength of a dual-cure resin core material to root canal dentine using photo and dual-cure adhesives with self-etching primer. MATERIALS AND METHODS: Post spaces were prepared in extracted premolars and then the root canal dentine was treated with one of the following bonding procedures: (1) Clearfil SE Bond Primer/Bond (SE), (2) Nano-Bond Primer/Photo-cure adhesive (PNB), (3) Nano-Bond Primer/Dual-cure adhesive (DNB). Photo-irradiation was performed for 10 or 20s from a coronal direction. The post spaces were then filled with a dual-cure composite resin (Build-It FR) and light-cured for 60s. After 24h storage, each specimen was serially sliced into 8, 0.6 x 0.6mm-thick beams for the microTBS test. The bond strength data were divided into coronal and apical regions and analysed using three-way ANOVA and Games-Howell multiple comparison (alpha=0.05). RESULTS: The microTBS of the photo-cure adhesive resin, SE and PNB, significantly decreased (p<0.05) at the apical region when the photo-irradiation time was 10s. However, the bond strength of the SE group was significantly improved at both regions when photo-irradiation time was extended to 20s (p<0.05). There were no differences in microTBS of the photo-cure adhesive resin (PNB) cured for 20s and dual-cure adhesive resin (DNB) (p>0.05). CONCLUSION: Photo-cure adhesive was effective for application on root canal dentine when the photo-irradiation time was sufficient. Extension of photo-irradiation time to the adhesive improved the bond strength depending on the type of adhesive resin.

Adhesiveness↗

PubMed2005

Elemental distributions and microtensile bond strength of the adhesive interface to normal and caries-affected dentin.

The aim of this study was to evaluate the microtensile bond strength (microTBS) and the elemental contents of the adhesive interface created to normal versus caries-affected dentin. Extracted human molars with coronal carious lesions were used in this study. A self-etching primer/adhesive system (Clearfil Protect Bond) was applied to flat dentin surfaces with normal and caries-affected dentin according to the manufacturer's instructions. After 24 h water storage, the bonded specimens were cross-sectioned and subjected to a microTBS test and electron probe microanalysis for the elemental distributions [calcium (Ca), phosphorus (P), magnesium (Mg), and nitrogen (N)] of the resin-dentin interface after gold sputter-coating. The microTBS to caries-affected dentin was lower than that of normal dentin. The demineralized zone of the caries-affected dentin-resin interface was thicker than that of normal dentin (approximately 3 microm thick in normal dentin; 8 microm thick in caries-affected dentin), and Ca and P in both types of dentin gradually increased from the interface to the underlying dentin. The caries-affected dentin had lost most of its Mg content. The distributions of the minerals, Ca, P, and Mg, at the adhesive interface to caries-affected dentin were different from normal dentin. Moreover, a N peak, which was considered to be the collagen-rich zone resulting from incomplete resin infiltration of exposed collagen, was observed to be thicker within the demineralized zone of caries-affected dentin compared with normal dentin.

Dental Caries↗

PubMed2005

Effect of acidic pretreatment combined with a silane coupling agent on bonding durability to silicon oxide ceramic.

This study examined the effect of different acidic treatments and the role of a phosphate monomer in a silane coupling agent on the durability of the dual-cure resin cement/silicon oxide bond. Ceramic blocks (Vita Celay Blanks) were cut into multiple 3 mm-thick slices and polished using 600 grit SiC paper. Two pairs were left untreated [controls (CTRL)], two pairs were treated with 40% phosphoric acid and rinsed with water for 30 s (PA), and another two pairs treated with 20% hydrofluoric acid followed by 30 s water rinsing (HF). Half the specimens were silanated with Tokuso Ceramics Primer (TCP) (Tokuyama) and the other half with TCP formulated without phosphate monomer (TCP-NoPM). All the pairs were bonded with Bistite II dual-cure resin cement (Tokuyama) and light cured. After 24 h water storage at 37 degrees C, 0.7 mm-thick slabs were serially sectioned. Immediately, after 6 months and after 1 year of water storage, two slabs were randomly selected from each subgroup, and sliced into beams (6 x 0.7 x 0.7 mm) for the microtensile bond strength (muTBS) test. The muTBS data were statistically analyzed using multiple Wilcoxon Signed Rank tests (p < 0.05). Failure modes were determined using a confocal laser-scanning microscope. Ceramic surface morphology after the different acidic treatments was examined using an SEM. After 1 day, in the case of silane treatment with TCP, there were no significant differences in muTBS between the control and acid-treated groups (p > 0.05), whereas with TCP-NoPM, the muTBS of the control was significantly lower than the acid-treated groups (p < 0.05). All the TCP and acid-treated TCP-NoPM groups exhibited significant reductions in muTBS after 6 months (p < 0.05). After 1 year, the muTBS of the acid-treated TCP groups were not significantly different from the control TCP group (p > 0.05). There was also no significant difference between the HF-treated TCP and TCP-NoPM groups (p > 0.05) after 1 year, all exhibiting greater than 10 MPa tensile bond strength. It is suggested that acidic pretreatment of the ceramic surface does not improve the durability of the dual-cure resin cement/silicon oxide ceramic bond when an acidic phosphate monomer is present as an activator in a ceramic primer.

Acid Etching, Dental↗

PubMed2005

Shear bond strengths of indirect resin composites to hybrid ceramic.

A hybrid ceramic, Estenia, is a highly-filled composite for indrect use. The purpose of this study was to measure the shear bond strength between Estenia and six incremental materials: Estenia, Cesead II, Epricord, Gradia, Prossimo, and Solidex. Five specimens were prepared for each group, and all specimens were subjected to shear bond strength testing at a cross-head speed of 1 mm/min. Data were analyzed using two-way ANOVA and Dunnett's T3 test at 95% confidence level. The results indicated that the shear bond strength of Estenia to Estenia was significantly lower than that of any other combinations. Apart from storage condition that was found to influence shear bond strength statistically, thermal cycling of the specimens also tended to decrease the bond strength between Estenia and the incremental materials. It was concluded that regularly-filled composites are suitable to be used as an incremental material facing Estenia in combination technique.

Analysis of Variance↗

PubMed2005

Regional bond strength of four self-etching primer/adhesive systems to root canal dentin.

The purpose of this study was to evaluate the regional bond strength of a dual-cure resin core material to root canal dentin using four self-etching primer/adhesive systems. Post spaces were prepared in extracted premolars, and their root canal dentin was treated with one of the following self-etching primer/adhesive systems: ED Primer II and Clearfil Photobond, photo-cure/dual-cure systems of Clearfil Liner Bond 2V, or Clearfil SE Bond. Post spaces were filled with the dual-cure resin core material, and microtensile bond strength (microTBS) at the coronal and apical regions was measured after 24-hour storage. There were no regional differences in microTBS of the photo-cure and dual-cure systems of Clearfil Liner Bond 2V, while microTBS at the coronal region of Photobond and SE Bond groups were higher than those at the apical region. At the apical region, photo-cured Clearfil Liner Bond 2V exhibited significantly higher bond strength than those of the other systems.

Adolescent↗

PubMed2005

Effect of air-powder polishing on dentin adhesion of a self-etching primer bonding system.

The purpose of this study was to evaluate the effect of air-powder polishing with sodium bicarbonate (SB) or crystalline cellulose (CC) on the bond strength of a self-etching primer bonding system to dentin. Ground human dentin surfaces were prepared using 600-grit SiC paper. The teeth were divided into three groups according to dentin treatment: control, air-powder polishing with SB, and air-powder polishing with CC. The dentin surfaces were bonded with a self-etching primer bonding system, followed by a light-cured resin composite. microTBS test and SEM analysis were performed. The results of microTBS test indicated that air-powder polishing with SB affected bond strength to dentin, while that with CC did not influence bond strength. SEM observation of air-polished dentin surfaces showed that dentin surfaces air-polished with SB were roughened and covered with a smear layer, while those with CC were smooth and the smear layer was removed.

Air Abrasion, Dental↗

PubMed2005

Hardness and Young's modulus of transparent dentin associated with aging and carious disease.

This study investigated the changes in hardness and Young's modulus of the transparent layer of dentin associated with aging and the carious process. Eighteen extracted human molars with or without coronal caries were used in this study. The normal teeth were divided into two groups by age, and the carious teeth were divided into two groups of active or arrested caries. After polishing the specimens parallel to the long axis of the tooth, both hardness and Young's modulus were measured using a nanoindentation tester. The hardness and Young's modulus of the transparent layer in aged dentin were higher than the other portions of aged dentin. The transparent layer under carious lesions had a significantly lower hardness than the underlying normal dentin, whereas its Young's modulus was not significantly reduced. The hardness and Young's modulus of the transparent layer in active carious lesions were lower than those in arrested carious lesions.

Aging↗