Biomedical subjects
Publications and source records attributed to Ronald L Sakaguchi.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
The aim of this study was to evaluate the changes in viscoelastic properties of a UDMA-based dental resin as a function of time after initial light exposure. Specimens of a UDMA/TEGDMA (70:30 wt%) resin were irradiated by a visible-light-curing unit. Immediately after the irradiation, the light-cured specimen was stored in the dark for different times from 1 to 120 h at 37 degrees C, and characterized by means of DMA, DSC, and FTIR spectroscopy. The irradiated specimen exhibited a bimodal shape in the form of two rapid declines in log E' corresponding to glass transition with a plateau between the two declines. Two distinct peaks were seen in tan delta versus temperature. The thermal reaction of the incompletely cured sample with residual groups trapped by the fast reaction during irradiation is responsible for the plateau. After storage, significant changes were observed in dynamic mechanical parameters, DSC exotherm, and degree of conversion. Storage modulus continued to increase during the 4 h of storage and leveled off thereafter. Peak heights of tan delta versus temperature were also influenced by storage. Degree of conversion increased from 75 +/- 2% immediately after irradiation to 87 +/- 3% after 120 h storage. The changes of the properties of this dental resin system when stored at 37 degrees C after irradiation are clinically important in terms of stability, durability, and performance after initial polymerization.
OBJECTIVES: The purpose of this study was to determine the minimal extent of cure required by the base of a Class 2 resin composite restoration (Z250, 3M ESPE, St Paul, MN, USA) that allows it to support the rest of the restoration and maintain its marginal seal under simulated clinical conditions. METHODS: Resin composite (Z250, 3M ESPE, St Paul, MN, USA) was placed incrementally or in bulk into Class 2 preparations in extracted human molar teeth and exposed to various light-curing energy densities. The restorations were subjected to 1000 thermal cycles (5-55 degrees C) and 500,000 fatigue cycles from 18 to 85 N using a stainless-steel sphere. Marginal integrity was evaluated using visual rating (ridit analysis) and microleakage. Degree of conversion (DC) and Knoop hardness (KHN) were determined at the occlusal and gingival surfaces using a reusable tooth template with identical preparation dimensions. Percentage of maximum DC and KHN were determined. Mechanical properties were tested in resin composite bars having similar KHN values as the resin composite at the gingival margins. RESULTS: Energy density had a significant effect on gingival marginal defects as determined by ridit analysis but not on microleakage. Water had a significant dissolving effect on gingival margin integrity at very low degrees of conversion and energy densities (4000 mJ/cm2). There was no overall significant effect of thermal-mechanical stressing on gingival marginal defects or microleakage. SIGNIFICANCE: Based on ridit analysis, a recommended lower limit of gingival margin acceptability in the bulk-filled Z250 resin composite restoration was created by 80% of maximum conversion, 73% of maximum hardness and approximately 70% of maximum flexural strength and modulus in the gingival marginal area.
STATEMENT OF PROBLEM: The comfort and effectiveness of athletic mouth guards are believed to depend on their degree of fit to oral tissues. Vacuum-forming machines are simpler and less expensive than pressure-forming machines. However, it is thought that vacuum-formed mouth guards often do not exhibit adequate adaptation. PURPOSE: The purpose of this study was to evaluate the effects of cast residual moisture and temperature on the fit of athletic mouth guards made with a vacuum-forming machine. MATERIAL AND METHODS: A metal master model simulating the cross section of the maxillary molar region was used to form 20 working plaster casts. The casts represented 4 (5 specimens each) conditions before the forming of the mouth guard specimens: storing in a wet environment at room temperature and storing in a dry environment at room temperature, 5 degrees C, and 40 degrees C. Mouth guard specimens were fabricated with ethylene vinyl acetate sheets (3.8-mm thick) with the use of a vacuum-forming machine. Test casts were created by pouring hand-mixed type III dental stone into each of the mouth guard specimens. The differences in the sagittal cross-sectional heights at the line angle area of the test casts and the working casts were compared. This was achieved by superimposing their 3-dimensional images scanned by a laser scanner. The air permeability was also measured for the hand-mixed stone casts under wet and dry conditions, the vacuum-mixed stone cast, and the high-strength stone specimen. This was achieved by measuring the volume of transmitted air passing through the specimen in the testing tube. One-way analysis of variance with the Scheffé post hoc test (P <.05) was applied to determine the conditions of the working cast required to achieve the best fit. RESULTS: With regard to the fit of the mouth guard specimens to the working cast, those with dry and heated working casts showed a significantly better fit than those with wet working casts (P<.05). A significantly larger volume of transmitted air was found in the dry stone specimen (P<.05) followed by the dry high-strength stone cast and then the wet stone cast. CONCLUSION: Within the limitations of this study, residual moisture in the working cast was the most critical factor in determining the fit of the mouth guard made by vacuum-forming machines. The best fit was achieved when the working cast was thoroughly dried and its surface temperature was elevated.
OBJECTIVES: The goal of this study was to evaluate the potential for using dynamic mechanical analysis of tubular geometry in a three-point flexure fixture for monitoring the storage modulus development of a light-activated polymer matrix composite. METHODS: Composite samples were inserted into PTFE tubes and tested in a three-point bend fixture in a dynamic mechanical analyzer (DMA) at 200 Hz with 20 microm amplitude. Samples were light activated for 60s (385 mW/cm(2) at the composite surface) and storage modulus (E') was measured continuously for the seven light-activated composites studied (one microfill, four hybrids and two unfilled resins). Cores of composite were removed from the PTFE sheath after 13.5 min and evaluated with the same parameters in the DMA. A finite element model of the test configuration was created and used to estimate operating parameters for the DMA. Degree of conversion (DC) was measured using micro-Fourier Transform Infrared (FTIR) spectroscopy for the microfilled composite samples and one hybrid 13.5 and 60 min after light activation. RESULTS: The E' for a generic hybrid and microfilled composite was 13,400+/-1100 and 5900+/-200 MPa, respectively, when cured within the tube and then removed and tested in the DMA. DC was 54.6% for the hybrid and 60.6% for the microfill. A linear regression of E' for the sheath and core vs core alone (r(2)=0.986) indicated a linear scaling of the sheath and core values for E' enabling a correction for estimated E' values of the composite core. SIGNIFICANCE: This method estimates the storage modulus growth during light-activated polymerization of highly filled dimethacrylates. Although the approach is phenomenological in that quantitative measurements of E' are not made directly from the DMA, estimates of early polymerization kinetics appear to be validated by three different approaches.