Fluorine-substituted hydroxyapatite scaffolds hydrothermally grown from aragonitic cuttlefish bones.

Porous hydroxyapatite scaffolds with different levels of fluorine substitution (46% and 85%) on the OH sites were produced via hydrothermal transformation of aragonitic cuttlefish bones at 200 degrees C and calcination at temperatures up to 1200 degrees C. The increasing level of F substitution reduces the kinetics and probably the yield of the reaction. The incorporation of F in the lattice of hydroxypatite caused a lowering of the unit cell volume due to reduction of the length of the a-axis. The crystallites formed were close in size to bone-like apatite and were orientated along the a-axis rather than the c-axis. There was evidence of AB-type carbonated apatite.

Animals↗

PubMed2006

Bond-coating in plasma-sprayed calcium-phosphate coatings.

The influence of bond-coating on the mechanical properties of plasma-spray coatings of hydroxyatite on Ti was investigated. Plasma-spray powder was produced from human teeth enamel and dentine. Before processing the main apatite coating, a very thin layer of Al2O3/TiO2 was applied on super clean and roughened, by Al2O3 blasting, Ti surface as bond-coating. The experimental results showed that bond-coating caused significant increase of the mechanical properties of the coating layer: In the case of the enamel powder from 6.66 MPa of the simple coating to 9.71 MPa for the bond-coating and in the case of the dentine powder from 6.27 MPa to 7.84 MPa, respectively. Both tooth derived powders feature high thermal stability likely due to their relatively high content of fluorine. Therefore, F-rich apatites, such those investigated in this study, emerge themselves as superior candidate materials for calcium phosphate coatings of producing medical devices. The methods of apatite powder production and shaping optimization of powder particles are both key factors of a successful coating. The methods used in this study can be adopted as handy, inexpensive and reliable ways to produce high quality of powders for plasma spray purposes.

Apatites↗

PubMed2006

Hydrothermal growth of hydroxyapatite scaffolds from aragonitic cuttlefish bones.

Scaffolds of AB-type carbonated hydroxyapatite (HA) were successfully produced via hydrothermal transformation (HT) of aragonitic cuttlefish bones at 200 degrees C. The transformation was seemingly complete after 9 h of HT and no intermediate products were registered. Beyond low production cost, worldwide availability, and natural-biological origin of raw materials, the produced scaffolds preserved the initial structure of cuttlefish bone, featuring good biocompatibility in osteoblasts tests and ideal pore size ( approximately 80 microm in width and approximately 100 microm in height) and interconnectivity for supporting biological activities, such as bone tissue growth and vascularization. The highly channeled structure and the use of fresh cuttlefish bones favored the diffusion of the reaction solution towards the aragonite resulting in fast kinetics (after 1 h, hydroxyapatite was the dominant crystalline phase).

Animals↗

PubMed2005

Formation of hydroxyapatite onto glasses of the CaO-MgO-SiO2 system with B2O3, Na2O, CaF2 and P2O5 additives.

New bioactive glasses with compositions based on the CaO-MgO-SiO(2) system and additives of B(2)O(3), P(2)O(5), Na(2)O, and CaF(2) were prepared. The in vitro mineralization behaviour was tested by immersion of powders or bulk glasses in simulated body fluid (SBF). Monitoring of ionic concentrations in SBF and scanning electron microscopy (SEM) observations at the surface of the glasses were conducted over immersion time. Raman and infrared (IR) spectroscopy shed light on the structural evolution occurring at the surface of the glasses that leads to formation of hydroxyapatite.

Biocompatible Materials↗

PubMed2005

Scaffolds for bone restoration from cuttlefish.

Scaffolds of pure hydroxyapatite suitable for either direct clinical use or tissue-engineering applications were successfully produced via hydrothermal transformation of aragonite, obtained from fresh cuttlefish bones, at 200 degrees C followed by sintering. Beyond low production cost, worldwide availability and natural-biological origin of raw materials, the produced scaffolds have ideal pore size and interconnectivity features suitable for supporting biological activities, such as bone tissue growth and vascularization. Bioactivity in vitro tests were excellent: (a) rapid and pronounced formation of hydroxyapatite occurred when the scaffolds were immersed in simulated body fluid (SBF), and (b) outstanding proliferation of osteoblasts was registered. The produced scaffolds can be machined and shaped very easily at any stage of processing. Therefore, these ceramic scaffolds can satisfy both bioactivity demands and the requirements for shaping of tailor-made individualized implants, especially for randomly damaged bones.

Animals↗

PubMed2003

The fluorapatite-anorthite system in biomedicine.

Glasses and glass ceramics of fluorapatite-anorthite (eutectic composition) were produced and characterized in order to evaluate their potential application in biomedicine. Bio-reactivity was determined by in vitro tests by immersion of powders in simulated plasma liquids as well as by in vivo experiments by implantation in rabbits. According to the results, the investigated materials are bio-acceptable since no toxic or other harmful evidence was detected. Glass-ceramics showed remarkable inertness, whereas glasses spontaneously dissolved in SBF and after 1 week moderate formation of apatite was observed, that however ceased within a month.

Aluminum Silicates↗

PubMed1995

Wettability and interfacial interactions in bioceramic-body-liquid systems.

Wetting experiments, by the sessile drop technique, were carried out at 37 degrees C in air to determine the surface and interfacial interactions that take place in various solid bioceramics based on Al2O3, ZrO2(YPZ), SiO2, and TiO2 in contact with water, Ringer solution, artificial synovial fluid, calf serum, human plasma, and whole blood (+ EDTA). The surface energy of the liquids was measured by the ring method. The calculated values of the energy of interaction (work of adhesion) reveal that intermolecular forces act across the solid-liquid interfaces. The contribution of the dispersion and polar interactions to the surface energy of the polar liquids and the pure or mixed oxides was determined assuming that in the system of Mn-steel-liquids only dispersion forces act at the interface. It was found that the contribution of the polar interactions to the energy of interaction at the solid-liquid interface increases with the glassy phase content of the oxide that causes reduction of the measured contact angle.