Integrated municipal solid waste treatment using a grate furnace incinerator: the Indaver case.

An integrated installation for treatment of municipal solid waste and comparable waste from industrial origin is described. It consists of three grate furnace lines with flue gas treatment by half-wet scrubbing followed by wet scrubbing, and an installation for wet treatment of bottom ash. It is demonstrated that this integrated installation combines high recovery of energy (40.8% net) with high materials recovery. The following fractions were obtained after wet treatment of the bottom ash: ferrous metals, non-ferrous metals, three granulate fractions with different particle sizes, and sludge. The ferrous and non-ferrous metal fractions can both be recycled as high quality raw materials; the two larger particle size particle fractions can be applied as secondary raw materials in building applications; the sand fraction can be used for applications on a landfill; and the sludge is landfilled. For all components of interest, emissions to air are below the limit values. The integrated grate furnace installation is characterised by zero wastewater discharge and high occupational safety. Moreover, with the considered installation, major pollutants, such as PCDD/PCDF, Hg and iodine-136 are to a large extent removed from the environment and concentrated in a small residual waste stream (flue gas cleaning residue), which can be landfilled after stabilisation.

Air Pollutants↗

PubMed2006

Accelerated carbonation for treatment of MSWI bottom ash.

Leaching of heavy metals from MSWI bottom ash exceeds some of the Flemish limit values for recycling the material as granular construction application. In particular, leaching of Cu, Zn and Pb often exceeds the limit value, with Cu being the most critical. In order to recycle bottom ash, treatment is therefore required. The bottom ash studied was divided on-site into four fractions using a large-scale wet sieving installation: a sludge fraction (Ø 0-0.1mm), a sand fraction (Ø 0.1-2mm) and two gravel fractions (Ø 2-6 and 6-50mm). The two gravel fractions complied with the limit values after 3 months of natural ageing. The sand and sludge fraction did not reach the limit value for Cu. Four weeks of accelerated carbonation resulted in an important decrease of Cu leaching from these two fractions, although the limit value is still exceeded. In view of applying carbonation as one of the treatment methods in an integrated industrial application, two tests were additionally performed. The use of stack gas as carbonating medium was verified by setting up an accelerated carbonation experiment at the incineration plant. Also, the depth of carbonation was measured in a 10 cm thick sample of the sand fraction after different periods of treatment. After 3 months of natural ageing only the upper 4 cm underwent a significant carbonation, while after one week of accelerated carbonation the total sample was carbonated. A model was developed to predict these experimental results.

Carbon↗

PubMed2005

Carbonation of MSWI-bottom ash to decrease heavy metal leaching, in view of recycling.

The 0.1-2 mm fraction of a MSWI-bottom ash cannot be used as granular construction material because leaching of Cu exceeds Flemish limit values. In addition, leaching of Ba, Mo and Sb exceeds informal limit values. Leaching characteristics thus need to be improved. Carbonation was the chosen treatment method and this was performed by placing samples in a CO2 chamber. The CO2 percentage and the temperature of the chamber atmosphere, as well as the initial humidity of the samples, were varied to optimize carbonation parameters. Metal leaching was tested with the EN 12457 extraction test. Carbonation decreased Cu leaching from 3.3 to 1.0 mg/kg, but not yet to below the official limit value of 0.5 mg/kg. Leaching of Mo and Sb remained fairly constant or even increased after carbonation, but their limit values are only informal. Ba leaching decreased to below the informal limit value. Carbonation also caused Cr leaching to increase, in some cases to above the official limit value. Of the tested parameters, a CO2 percentage of 10% and a carbonation temperature of 50 degrees C in the atmosphere, together with ash humidity between 13% and 25% appeared to give the best leaching results. The main carbonation reactions took place within the first 24 h.