Comment on "Band filling and interband scattering effects in MgB2: carbon versus aluminium doping".
Explore the source record for details and available documents.
Comment↗
Biomedical subjects
S L Bud'ko
Publications and source records attributed to S L Bud'ko.
Systematic effects of carbon doping on the superconducting properties of Mg(B1-xCx)(2).
The upper critical field, H(c2), of Mg(B1-xCx)(2) has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped MgB2 filaments were prepared, and for carbon levels below 4% the transition temperatures are depressed by about 1 K/% C and H(c2)(T=0) rises by about 5 T/% C. This means that 3.8% C substitution will depress T(c) from 39.2 to 36.2 K and raise H(c2)(T=0) from 16.0 to 32.5 T. These rises in H(c2) are accompanied by a rise in resistivity at 40 K from about 0.5 to about 10 microOmega cm.
Journal Article↗
Experimental evidence for anisotropic double-gap behavior in MgB2.
The behavior of a type II superconductor in the presence of a magnetic field is governed by two characteristic length scales, the London penetration depth and the coherence length. We present magnetization measurements on MgB2 powder showing an anisotropy in the upper critical field and hence the coherence length of 6. Using the technique of small angle neutron scattering we show that this anisotropy is not mirrored in the London penetration depth, which is almost isotropic. This result can be explained by the superconductivity residing in two distinct electronic bands of the material, only one of which is highly anisotropic.
Journal Article↗
Direct observation of spontaneous weak ferromagnetism in the superconductor ErNi2B2C.
Neutron measurements show that superconducting ErNi2B2C (T(C) = 11 K) develops antiferromagnetic spin density wave magnetic order (T(N) = 6 K), which squares up with decreasing temperature yielding a series of higher-order magnetic Bragg peaks with odd harmonics. Below T(WFM) = 2.3 K where magnetization indicates a net moment develops, even-order Bragg peaks develop which low field (approximately 3 Oe) polarized beam measurements show are magnetic in origin. The data directly demonstrate the existence of a net magnetization with a periodicity of 20a, confirming the microscopic coexistence of spontaneous weak ferromagnetism with superconductivity.
Journal Article↗
Anisotropy of superconducting MgB2 as seen in electron spin resonance and magnetization data.
We observed the conduction electron spin resonance (CESR) in fine powders of MgB2 both in the superconducting and normal states. The Pauli susceptibility is chi(s) = 2.0 x 10(-5) emu/mole in the temperature range of 450 to 600 K. The spin relaxation rate has an anomalous temperature dependence. The CESR measured below T(c) at several frequencies suggests that MgB2 is a strongly anisotropic superconductor with the upper critical field, H(c2), ranging between 2 and 16 T. The high-field reversible magnetization data of a randomly oriented powder sample are well described assuming that MgB2 is an anisotropic superconductor with H(ab)(c2)/H(c)(c2) approximately 6-9.
Journal Article↗
Thermodynamic and transport properties of superconducting Mg10B2.
Transport and thermodynamic properties of a sintered pellet of the newly discovered MgB2 superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition and magnetization data give similar values of the upper critical field, Hc2, with magnetization data giving dHc2/dT = 0.44 T/K at the transition temperature of Tc = 40.2 K. Close to the transition temperature, magnetization curves are thermodynamically reversible, but at low temperatures the trapped flux can be on the order of 1 T. The value of dHc/dT at Tc is estimated to be about 12 mT/K, a value similar to classical superconductors like Sn. Hence, the Ginzburg-Landau parameter kappa approximately 26. Estimates of the critical supercurrent density, Jc, using hysteresis loops and the Bean model, give critical current densities on the order of 10(5) A/cm2. Hence the supercurrent coupling through the grain boundaries is comparable to intermetallics like Nb3Sn.
Journal Article↗
Superconductivity in dense MgB2 wires.
MgB2 becomes superconducting just below 40 K. Whereas porous polycrystalline samples of MgB2 can be synthesized from boron powders, in this Letter we demonstrate that dense wires of MgB2 can be prepared by exposing boron filaments to Mg vapor. The resulting wires have a diameter of 160 microm, are better than 80% dense, and manifest the full chi = -1/4pi shielding in the superconducting state. Temperature-dependent resistivity measurements indicate that MgB2 is a highly conducting metal in the normal state with rho(40 K) = 0.38 microOmega cm. By using this value, an electronic mean-free path, l approximately 600 A can be estimated, indicating that MgB2 wires are well within the clean limit. Tc, Hc2(T), and Jc data indicate that MgB2 manifests comparable or better superconducting properties in dense wire form than it manifests as a sintered pellet.
Journal Article↗
Boron isotope effect in superconducting MgB2.
We report the preparation method of and boron isotope effect for MgB2, a new binary intermetallic superconductor with a remarkably high superconducting transition temperature T(c)(10B) = 40.2 K. Measurements of both temperature dependent magnetization and specific heat reveal a 1.0 K shift in T(c) between Mg11B2 and Mg10B2. Whereas such a high transition temperature might imply exotic coupling mechanisms, the boron isotope effect in MgB2 is consistent with the material being a phonon-mediated BCS superconductor.
Journal Article↗