Negligible magnetism in excellent structural quality Cr(x)Ti(1-x)O(2) anatase: contrast with high-T(C) ferromagnetism in structurally defective Cr(x)Ti(1-x)O(2).

We reexamine the mechanism of ferromagnetism in doped TiO(2) anatase, using epitaxial Cr:TiO(2) with excellent structural quality as a model system. In contrast to highly oriented but defective Cr:TiO(2) (approximately 0.5 micro(b)/Cr), these structurally superior single crystal films exhibit negligible ferromagnetism. Similar results were obtained for Co:TiO(2). We show for the first time that charge-compensating oxygen vacancies alone, as predicted by F-center mediated exchange, are not sufficient to activate ferromagnetism. Instead, the onset of ferromagnetism correlates with the presence of structural defects.

Journal Article↗
PubMed2005

Intrinsic ferromagnetism in insulating cobalt doped anatase TiO2.

Using complementary experiments we show that the room temperature ferromagnetism observed in anatase Co:TiO(2) films is not carrier mediated, but coexists with the dielectric state. TEM and x-ray absorption spectroscopy reveal a solid solution of Co in anatase, where Co is not metallic but in the +2 state substituting for Ti. Measurements at 300 K yield a M(S) of 1.1 mu(B)/Co atom, while all films are highly insulating. The evidence of intrinsic ferromagnetism in the dielectric ground state of Co:TiO(2) leads to new considerations for the origin of ferromagnetism in transition metal doped oxides.

Journal Article↗
PubMed1988

Analytical electron microscopy study of high Tc superconductor YBa2Cu3O7.

The high Tc superconducting material YBa2Cu3O7 shows a complex relationship between microstructure and oxygen content, which are controlled by length of heat treatment, atmosphere, and quench rate. An AEM investigation studying changes in the oxygen near edge features was undertaken. Electron energy loss spectroscopy (EELS) measurements have the important advantage that they can be made on single crystal grains, allowing orientation-dependent studies. Both ion-milled and crushed samples with varying O2 content were analyzed. The structure of YBaCu3O7 was determined by neutron diffraction to be orthorhombic with distinct Cu-O chains along the b-axis as well as Cu-O planes in the a-b plane. Therefore, by looking for a crystallographic dependence of the oxygen K-edge one might be able to distinguish inequivalent oxygen atoms by their core level binding energy and correlate site occupancy with varying O2 content. The EELS results on the oxygen K-edge are strongly dependent on oxygen content, most noticeably when the c-axis is parallel to the electron beam.