PHEMA as a keratoprosthesis material.
Explore the source record for details and available documents.
Biocompatible Materials↗
Biomedical subjects
S Vijayasekaran
Publications and source records attributed to S Vijayasekaran.
Histology of AlphaCor skirts: evaluation of biointegration.
PURPOSE: To report histologic findings in 14 AlphaCor artificial corneas implanted during clinical trials and subsequently explanted from human subjects following complications, so as to evaluate biointegration within the device skirt. METHODS: Explants were fixed and sectioned in paraffin. Histologic findings related to the device skirt were compared with earlier histologic results from animal studies and correlated with clinical histories. RESULTS: Two devices had been removed due to complications related to the optic alone, 11 following stromal melting overlying the biointegratable sponge skirt and 1 due to a retroprosthetic membrane. All devices demonstrated normal skirt porosity. Biointegration was similar to that found in animal studies but qualitatively appeared reduced in the affected areas in patients with overlying stromal melting prior to explantation. Patients with a longer history of melting prior to explantation demonstrated presence of inflammatory cells around the device. CONCLUSIONS: Histologic findings of the AlphaCor skirt in humans are consistent with earlier animal studies. This study confirms that biointegration by host fibroblastic cells, with collagen deposition occurs after AlphaCor implantation in humans. In cases in which stromal melting had occurred, biointegration is seen to be reduced. On correlating preoperative clinical factors with biointegration observed histologically, preoperative vascularization appears not to be required for AlphaCor biointegration.
Aged↗
Retinal toxicity of intravitreal tenecteplase in the rabbit.
AIM: To investigate the retinal toxicity of intravitreal injection of a novel fibrinolytic tenecteplase in rabbit eyes. METHODS: Tenecteplase (25-350 micro g in 0.1 ml BSS) was injected into the vitreous cavity of normal rabbit eyes. Control (fellow) eyes received 0.1 ml of BSS. One day, 1 week, and 2 months post-injection, the eyes were examined by slit lamp biomicroscopy, indirect ophthalmoscopy, and electroretinography, and then harvested for histopathological examination. RESULTS: No evidence of retinal toxicity was seen with tenecteplase doses up to and including 50 micro g. At a dose of 150 micro g ophthalmoscopy was normal, but histology showed mild retinal damage in the inner nuclear layer and electroretinography showed a temporary reduction in B-wave amplitude. At doses of 200 micro g and above, there was evidence of retinal toxicity on electroretinography, ophthalmoscopy, and histology. Ophthalmoscopic findings included vitreal fibrosis, retinal necrosis and tractional retinal detachment and light microscopy revealed necrosis of retinal pigment epithelium and other retinal layers. Damage was centred around the injection site but was more widespread with the higher doses. CONCLUSION: A dose of 50 micro g tenecteplase appears safe for intravitreal injection in the rabbit. Tenecteplase could have potential applications in the treatment of submacular haemorrhage and retinal vein occlusion.
Animals↗
Is it necessary to screen for hearing loss in the paediatric population with osteogenesis imperfecta?
The aim of the study was to assess the necessity of a screening service to detect early hearing loss in the paediatric population with osteogenesis imperfecta. Twenty-two children were assessed over a 5-year period. Five children (22.7%) had normal hearing. Fourteen (63.6%) had conductive hearing loss, with 12 children in this group having otitis media with effusion (OME); all had resolution of hearing loss with appropriate therapy. Two children had persistent conductive losses unrelated to OME. Three children (13.6%) had sensorineural hearing loss, with one being detected at the age of 1 year. Existing evidence suggests that hearing loss associated with osteogenesis imperfecta has its onset in the second to third decade of life. Contrary to this, hearing loss was detected in 77.3% (17) of this population with a median and mean age of 9 years. This study would suggest that routine screening is worthwhile in children with osteogenesis imperfecta.
Adolescent↗
Feasibility of continuous transthoracic cardiac imaging using a novel ultrasound transducer.
BACKGROUND: The feasibility of hands-free transthoracic continuous ultrasonic cardiac imaging has not been demonstrated previously. We developed a 2.5-MHZ spherical transducer mounted in an external housing to permit steering in 360 degrees (CONTISON). The external housing was attached to the chest wall using an adhesive patch. METHODS AND RESULTS: The transducer was placed in the third or fourth interspace at the left sternal border to permit imaging of the left ventricle (LV) in its short axis and attached to the chest wall. The transducer then was attached to an ultrasound machine. Ten normal subjects and 20 patients with previous myocardial infarction were studied. The following maneuvers were performed at the beginning of the study: (1) The patient was rotated from the supine position (0 degrees ) in 20 degrees increments to the left lateral decubitus position (90 degrees ). The echocardiogram was displayed continuously and was recorded on videotape (parasternal short-axis view) at 0 degrees, 20 degrees, 40 degrees, 60 degrees, 80 degrees, and 90 degrees. (2) The patient was returned to the supine position and an echocardiogram was obtained. The patient was then seated up 20 degrees, 40 degrees, 60 degrees, 80 degrees, and 90 degrees by using the controls on the bed. (3) The patient then was returned to the supine position and the echocardiogram was displayed continuously on the monitor. The echocardiogram was recorded every 15 minutes for a period of 4 hours. All segments of the LV were visualized in the supine position and during lateral rotation (0 degrees -90 degrees ). Thus, body position did not affect the image. All segments of the LV were visualized during sitting up (0 degrees -90 degrees ), and all segments were visualized during the 4 hours of imaging. The patients were able to move around without distortion of the image. CONCLUSION: The CONTISON transducer permitted continuous imaging of LV wall motion. Body position did not affect interpretation of wall motion. This device has potential applicability in monitoring LV function in the intensive care setting.
Adult↗
Development and clinical assessment of an artificial cornea.
Keratoprosthesis research has been a gradual, rather fragmentary process with advances being made by isolated groups of researchers. This has arisen partly because of poor funding in the area; research groups which have achieved commercial support have often had constraints upon the full disclosure of their findings. Despite these difficulties there has been real progress over the last decade by several independent groups. This article concentrates upon our own development of a hydrogel core-and-skirt keratoprosthesis, the Chirila KPro, in order to illustrate the scientific and clinical problems common to keratoprosthesis research. Pilot data from a clinical trial is presented and the priorities for future research are discussed.
Animals↗
Calcification of poly(2-hydroxyethyl methacrylate) hydrogel sponges implanted in the rabbit cornea: a 3-month study.
Poly(2-hydroxyethyl methacrylate) (PHEMA) hydrogels have been used in the past as ocular implants. In a recent development, PHEMA sponges have shown suitable properties as materials for the peripheral component of an artificial cornea (keratoprosthesis). However, the propensity of PHEMA to calcify could threaten the long-term stability of the implanted devices. In an attempt to improve the understanding of the calcification mechanism, the dynamics, extent, and nature of calcified deposits within PHEMA sponges implanted in the cornea were investigated in this study, and the possible correlation between necrosis of cells and calcification was critically examined. Samples of a PHEMA sponge were implanted in rabbit corneas and explanted at predetermined time points (2, 4, and 12 weeks). The samples were examined by microscopy (light, transmission, scanning) and energy dispersive analysis of X-rays. Histological assessment and semiquantitative analysis of the amount of calcium deposited was performed using image analysis. An in vitro experiment was also performed by incubating sponge samples for 2 weeks in a solution of calcium and phosphate ions at a ratio similar to that in hydroxyapatite, in the absence of cells. Calcification was not seen in the 2- and 4-week explants, however, small deposits were detected in two of the 12-week explants, both within and on the sponge's constituent polymer particles. The deposit volumes represented 0.094% and 0.21%, respectively, of the total sponge volumes. Calcium deposits were present in large amounts both within the constituent polymer particles and on the surface of the sponges incubated in the abiotic calcifying solution. Cooperative mechanisms are suggested for the calcification of PHEMA sponges in vivo. The initial event may occur at a molecular level, when plasma proteins are adsorbed onto the polymer surface and bound through chelation to the calcium ions present in the medium. After their natural degradation, these structures may act as nucleation sites for calcium phosphate crystallization. Concurrently, the calcium ions can diffuse into the hydrogel particles and then the spontaneous precipitation of calcium phosphate may be caused by supersaturation due to the lower content of water in polymer, an effect which is likely predominant in vitro. The second event is the recruitment of phagocytic cells to clear calcium debris. Degeneration of these cells may then form nucleation sites for secondary calcification.
Animals↗
Synthesis, physical characterization, and biological performance of sequential homointerpenetrating polymer network sponges based on poly(2-hydroxyethyl methacrylate).
A limitation in the use of hydrophilic poly(2-hydroxyethyl methacrylate) (PHEMA) sponges as implantable devices is their inherently poor mechanical strength. This precludes proper surgical manipulation, especially in the eye where the size of the implant is usually small. In this study a new method was developed to produce mechanically stronger PHEMA sponges. Sequential homointerpenetrating polymer network (homo-IPN) sponges were made by using HEMA as the precursor for generating both the first network and the successive interpenetrated networks. Following the formation of network I, the sponge was squeezed to remove the interstitial water, soaked in the second monomer (also HEMA), and squeezed again to remove the excess monomer from the pores before being subjected to the second polymerization leading to the formation of network II. Two two-component IPN sponges (K2 and K4) with increasing HEMA content in the network II and a three-component IPN sponge (K3) were produced, and their properties were compared to those of a homopolymer PHEMA sponge (control). Apart from elongation, the tensile properties were all significantly enhanced in the IPN sponges; the water content was the same as in the control sponge, except for sponge K4, which was lower. Light microscopy revealed similar pore morphologies of the control and IPN sponges K2 and K3, and the majority of the pores were around 25 microm. Sponge K4 displayed smaller pores of around 10 microm. Cellular invasion into the sponges was examined in vitro (incubation with 3T3 fibroblasts) and in vivo (implantation in rabbit corneas). Although the in vitro assay detected a change in the cell behavior in the early stage of invasion, which was probably due to the formation of IPNs, such changes were not reflected in the longer term in vivo experiment. There was a proper integration of sponges K2 and K3 with the corneal stroma, but much less cellular invasion and no neovascularization in sponge K4. We concluded that IPN formation is a valid method to enhance the strength of PHEMA sponges, provided that the content of HEMA in the successive networks is not too high.
Animals↗
Development of a poly(2-hydroxyethyl methacrylate) orbital implant allowing direct muscle attachment and tissue ingrowth.
PURPOSE: To develop a poly(2-hydroxyethyl methacrylate) orbital implant that allows tissue ingrowth and direct muscle attachment to minimize the risk of extrusion and to enhance cosmesis. METHODS: Assessment of clinical outcomes and histologic findings after implantation of 18 prototype prostheses into rabbits. The implants were not wrapped with other tissues or materials. RESULTS: One case of infection was observed but there were no extrusions, with up to 21 months follow-up. Biocolonization was confirmed histologically. Good movement was observed when a cosmetic shell was fitted. CONCLUSIONS: The prototype prosthesis appears promising, with particular advantages being the direct attachment of extraocular muscles, good cosmesis and movement, and a low complication rate in this pilot study.
Animals↗
Correlation of histological findings with gadolinium enhanced MRI scans during healing of a PHEMA orbital implant in rabbits.
BACKGROUND/AIMS: To investigate a poly(2-hydroxyethyl methacrylate) (PHEMA) orbital implant with a spongy anterior hemisphere and a smooth gel posterior hemisphere, by histology correlated with magnetic resonance images. METHODS: Following enucleation, eight rabbits received PHEMA implants to which the muscles were directly sutured, and underwent gadolinium enhanced magnetic resonance imaging (MRI) from 3 to 52 weeks. After the rabbits were killed, the implants were removed, cut in a plane corresponding to the scan, and processed for light and electron microscopy. RESULTS: All eight rabbits retained their implant to the end of the study period without complications. The scans demonstrated muscle attachment to the anterior half of the implant, and enhancement was seen on injection of gadolinium chelate. Histology confirmed muscle attachment, and cellular and vascular ingrowth. Over time, a transformation from reactive inflammatory to relatively non-vascular scar tissue was seen within the implant. Calcium deposits in one implant were detected by imaging and histology. CONCLUSION: The implants are readily visualised on MRI. Muscle attachment and fibrovascular ingrowth into the anterior hemisphere are seen, while encapsulation of the posterior hemisphere is minimal. Histological findings confirm the progress of the healing response, with initial inflammation and marked vascularisation, developing later into quiescent scar tissue predominantly of fibroblasts.
Animals↗
Biodegradation in vitro and retention in the rabbit eye of crosslinked poly(1-vinyl-2-pyrrolidinone) hydrogel as a vitreous substitute.
To elucidate the relatively short retention of crosslinked poly(1-vinyl-2-pyrrolidinone) hydrogels in the eye when used as potential vitreous substitutes, a 14C-labeled hydrogel was produced and subjected to both in vitro biodegradation assays and in vivo experiments. The polymer was synthesized by the free-radical copolymerization of 99% 1-vinyl-2-pyrrolidinone with 1% 14C-methyl methacrylate in the presence of ethylene glycol dimethacrylate (0.1%) as crosslinking agent. The in vitro protocol for assessing the biodegradation included the incubation of hydrogel with hydrolases (trypsin or collagenase), followed by examination of changes in its physical characteristics and by monitoring its residual radioactivity, as well as by detection of possible degradation products. Within the maximum duration of experiments (4 weeks), none of the procedures indicated biodegradation of polymer. The hydrogel was also injected into the vitreous humor of rabbits and followed up to 4 weeks. Residual radioactivity measurements of the vitreous contents indicated that 50% of the polymer was removed by the end of this period. Histopathologic examination revealed cell infiltrates of the mononuclear phagocyte system in both vitreous and retinal tissue. A possible phagocyte-mediated mechanism for the dissipation of hydrogel is discussed.
Animals↗
Chorioretinal venous anastomoses: effect of different laser methods and energy in human eyes without vein occlusion.
BACKGROUND: This study was performed to determine the laser energy required to rupture both Bruch's membrane and retinal veins reliably in order to create a venous chorioretinal anastomosis. METHODS: A histological examination was conducted of argon green and YAG laser applications to the retina made prior to enucleation in eight eyes with large intraocular melanomas. RESULTS: Argon laser application of 50 microns in size and 0.1 s duration to intervascular areas of the retina will reliably rupture Bruch's membrane at a power level of at least 1.5 W. If the argon laser spot is placed overlying a retinal vein, a power level of up to 2.5-3.0 W will rupture Bruch's membrane in 60%, with only 34% of the retinal veins showing evidence of rupture. The YAG laser with power levels of 3-4 mJ will reliably rupture the retinal vein in cases where it has not previously been ruptured by the argon laser. CONCLUSION: When attempting to create a chorioretinal venous anastomosis in an eye with a non-ischaemic central retinal vein occlusion, Bruch's membrane should be ruptured first by placing the argon laser application at the side of the retinal vein before an attempt to rupture the retinal vein itself is made in case haemorrhage from the ruptured vein obscures the view. A power level of at least 2.5 W should be used. If the argon laser is unsuccessful in rupturing the retinal vein, a YAG laser (3-4 mJ) is effective.
Adult↗
Cell viability and inflammatory response in hydrogel sponges implanted in the rabbit cornea.
In the quest for the development of a functional keratoprosthesis, the biocompatibility of the porous skirt material in the Chirila keratoprosthesis (KPro) was investigated. The population of live and dead cells within, and the inflammatory response to, a tissue-integrating poly(2-hydroxyethyl methacrylate) (PHEMA) sponge were studied. Samples of the hydrogel sponge were implanted in rabbit corneas and explanted at predetermined time points up to 12 weeks. The explanted sponges were subjected to cell viability assay using two types of fluoroprobes, 5-chloromethylfluorescein diacetate and ethidium homodimer-1. A semiquantitative analysis was performed to assess the number of dead cells within the sponge and in the area of corneal stroma proximal to the sponge. Five rabbits were used for each end point (2, 4 and 12 weeks). To investigate the inflammatory response to the sponge, immunocytochemistry, using specific antibodies to rabbit macrophages, enzyme histochemistry of chloroacetate esterase (to detect neutrophils) and transmission electron microscopy (TEM) were also employed at 24 h, 2, 4 and 12 weeks after implantation. Four weeks after implantation, fewer viable cells were observed in the sponge when compared to the 2-week implant. However, the proportion of viable cells increased dramatically by 12 weeks. The proportion of nonviable cells decreased gradually with time; central sponge contained 34+/-11 % dead cells after 2 weeks, and 15+/-4.3% after 12 weeks. The staining of inflammatory cells demonstrated the presence of macrophages and neutrophils up to 12 weeks after implantation. TEM confirmed the presence of these cell types and others. including eosinophils and myofibroblasts, as well as blood capillaries. The presence of a significant number of viable cells at each time point and the uniform reduction of the nonviable cell proportion with time suggests that the sponge is a conducive environment supporting a prolific, viable cellular colonization. Dead cells observed in the first instance indicate a normal injury pattern. However, the presence of a small but significant proportion of invading inflammatory cells 12 weeks after implantation confirms a characteristic pattern of wound healing within the sponges.
Animals↗
Clinical results of implantation of the Chirila keratoprosthesis in rabbits.
AIMS/BACKGROUND: An ideal keratoprosthesis (KPro) would closely resemble a donor corneal button in terms of its surgical handling, optics, and capacity to heal with host tissue in order to avoid many of the complications associated with the KPros which are currently in clinical use. This study was carried out to assess the long term clinical outcomes on implantation of the core and skirt poly(2-hydroxyethyl methacrylate) KPro in animals. METHODS: 20 KPros were made and implanted as full thickness corneal replacements into rabbits and followed for up to 21 months to date. RESULTS: 80% of the prostheses have been retained, with a low incidence of complications such as cataract, glaucoma, and retroprosthetic membrane formation which are frequently associated with KPro surgery. CONCLUSIONS: KPros of this type may offer promise in the treatment of patients for whom penetrating keratoplasty with donor material carries a poor prognosis. Refinement of the KPro and further animal trials, including implantation into abnormal corneas, are however mandatory before human implantation could be planned.
Animals↗
Implantation of PHEMA keratoprostheses after alkali burns in rabbit eyes.
PURPOSE: We have previously examined histologically the healing of a PHEMA core-and-skirt keratoprosthesis (the Chirila KPro) as a full-thickness implant in healthy animal corneas. The present study was carried out to determine whether a diseased cornea could also generate biocolonization of the skirt region of a KPro. METHODS: Ten KPros were placed as full-thickness corneal implants under conjunctival flaps in 10 alkali-burned rabbit corneas. Histological findings at intervals from 2 weeks to 6 months postoperatively were compared with earlier findings in 10 rabbits that had received identical KPros without prior alkali injury. RESULTS: Despite severe corneal injury and the reduced keratocyte population present, there were no clinically detected complications in 60%. Histological findings established that, compared with healthy host tissue, skirt biocolonization and KPro-cornea healing after an alkali burn were impaired, with evidence of epithelial downgrowth in 40%. One animal required euthanasia earlier than the planned end point, but no KPro extrusions occurred. CONCLUSION: Biocolonization of a KPro skirt is reduced but not prevented in an alkali-induced corneal inflammation model. Although no extrusions occurred, close follow-up and anticollagenolytic medication would be required to minimize the complication rate.
Animals↗
Keratoprosthesis results in animals: an update.
BACKGROUND: The report presented is an update on continuing development work on modified PHEMA core-and-shirt KPros in animals. METHODS: Two variations (improved wet-eye, and dry-eye) of a prototype core-and-skirt Chirila KPro are described. The clinical success rate on implantation of these versions of the Chirila KPro was assessed. RESULTS: It was found that a significant improvement in retention rate was shown in the improved model but that the dry-eye model failed early in two of the three implanted. CONCLUSIONS: The significance of the improved strength and the reasons for disappointing results with the early dry-eye KPros are discussed. Ongoing work is briefly outlined.
Animals↗
Histologic evaluation during healing of hydrogel core-and-skirt keratoprostheses in the rabbit eye.
PURPOSE: We developed two models that are modifications of our original poly(2-hydroxyethyl methacrylate) (PHEMA) core-and-skirt keratoprosthesis. In these keratoprostheses, the mechanical strength of the skirt has been considerably increased with divinyl glycol (DVG) as a cross-linking agent during polymerization. In one (KPro I), methyl methacrylate (MMA) was added as comonomer to increase cell adhesion, and in the other (KPro II), HEMA was polymerized with DVG without comonomer. The aim of this study was to evaluate the process of healing and biocolonization and to ascertain whether KPro I demonstrates better ingrowth than the mechanically stronger KPro II, after implantation in rabbit eyes. METHODS: Ten rabbits were used for each model and studied at five predetermined end points up to 26 weeks. The device was implanted as a full-thickness keratoprosthesis covered with a conjunctival flap. RESULTS: Neither prosthesis demonstrated extrusion or retroprosthetic membrane formation. There was no significant difference between the two types of prosthesis with respect to tissue ingrowth and surrounding tissue melting. Histologically, inflammation was not severe, but calcification was seen in most specimens. Evidence of biodegradation of the prosthesis also was seen. CONCLUSION: In our original keratoprosthesis, fibrovascular invasion had occurred into the prosthetic skirt, but wound dehiscence and low mechanical strength resulted in an unfavorable outcome. In this series, the mechanical properties were improved, and KPro II was stronger than KPro I. Therefore KPro II would be the preferred polymer combination for surgical manipulation. However, biodegradation and calcification require further investigation into the degree and significance of these adverse reactions.
Animals↗
Crosslinked poly(1-vinyl-2-pyrrolidinone) as a vitreous substitute.
A hydrogel with a high water content was produced and tested as a possible vitreous substitute. The polymer (poly[1-vinyl-2-pyrrolidinone]) (PVP) was synthesized by free radical bulk polymerization of 1-vinyl-2-pyrrolidinone (VP) in the presence of 0.25% divinyl glycol (DVG) as a crosslinking agent. The fully hydrated polymer, containing about 98% water, was clear, transparent, autoclavable, and easily injected through a small-gauge needle with minimum fragmentation, and without changes in its optical properties. Dynamic mechanical analysis of the hydrogel indicated a covalently crosslinked elastic network both before and after injection. The resilience of hydrogel decreased after being subjected to shear stress during the injection process. A cytotoxicity bioassay of the hydrogel in vitro, using cultured mouse (Balb/ c-3T3) fibroblasts, showed cytostatic but not cytocidal effects. The hydrogel was injected into the vitreous cavity of rabbits and followed up to 4 weeks. The gel was clinically well tolerated, however opacities in the vitreous body were observed following the insertion of the gel. Histopathological examination revealed no adverse reactions to the retina, but the presence of loose polymer particles indicated the possibility of the biodegradation of the polymer. These results suggest the potential use of crosslinked PVP hydrogels as vitreous substitutes, provided that their biodegradation is not significant, a matter that should be further investigated.
3T3 Cells↗