Sharon Small | PubMed Health

PubMed2006

Comparative in vitro evaluation of microspherical embolisation agents.

This study describes the comparative performance of four commercially available microspherical embolisation products: Embosphere, Embogold, Contour SE and Bead Block. A series of in vitro evaluations were designed to assess the mechanical and biological characteristics of these biomaterials. Size distribution analysis revealed sieving techniques used to fractionate the embolics produced similar size distributions. The forces required to compress Embosphere, Embogold and Bead Block were in the range 21-27.5 kPa. Contour SE was significantly more compressible at approximately 5 kPa. However, recoverability of Contour SE required several minutes in contrast to the other products, a phenomenon attributed to its macroporous structure. When time taken to reach and remain in suspension was studied, results showed that the products quickly reached equilibrium with contrast agent. Bead Block was maintained in suspension for twice as long as the other products. Catheter deliverability was assessed and found to be dependent upon both microsphere and catheter, the best combination being Bead Block delivered via the Progreat catheter. Both the blood contacting SEM and plasma coagulation time showed none of the products were pro-thrombic or pro-coagulatory, each producing comparable results. Small differences in physical properties such as compressibility, could play an important role in delivery and effectiveness of vessel blockage. Currently all products are used routinely in clinical practice.

Acrylic Resins↗

PubMed2004

Synthesis and characterisation of cationically modified phospholipid polymers.

Phospholipid-like copolymers based on 2-(methacryloyloxyethyl) phosphorylcholine were synthesised using monomer-starved free radical polymerisation methods and incorporating cationic charge in the form of the choline methacrylate monomer in amounts varying from 0 to 30 wt%, together with a 5 wt% silyl cross-linking agent in order to render them water-insoluble once thermally cured. Characterisation using a variety of techniques including nuclear magnetic resonance spectroscopy, high-pressure liquid chromatography and gel permeation chromatography showed the cationic monomer did not interfere with the polymerisation and that the desired amount of charge had been incorporated. Gravimetric and differential scanning calorimetry methods were used to evaluate the water contents of polymer membranes cured at 70 degrees C, which was seen to increase with increasing cation content, producing materials with water contents ranging from 50% to 98%. Surface plasmon resonance indicated that the coatings swelled rapidly in water, the rate and extent of swelling increasing with increasing cation level. Dynamic contact angle showed that coatings of all the polymers possessed a hydrophobic surface when dry in air, characteristic of the alkyl chains expressed at the surface (>100 degrees advancing angle). Rearrangement of the hydrophilic groups to the surface occurred once wet, to produce highly wettable surfaces with a decrease in advancing angle with increasing cation content. Atomic force microscopy showed all polymer films to be smooth with no features in topographical or phase imaging. Mechanical properties of the dry films were also unaffected by the increase in cation content.

Biomimetic Materials↗