PubMed2006

Direct in situ observation of dynamic transport for electrolyte components by NMR combined with electrochemical measurements.

Electrochemical studies provide broad, but not cation- or anion-specific information on the migration of charged ions. However, individual ion diffusion (as a weighted average of charged and neutral ions) can be measured using pulsed-gradient spin-echo (PGSE) NMR. In this paper, the lithium transport in an electrolyte including a lithium salt was measured using electrophoretic NMR (ENMR) with non-blocking electrodes. A propylene carbonate (PC) solution doped with LiN(SO(2)CF(3))(2) (LiTFSI) was inserted in a homemade NMR cell equipped with Li/Li electrodes. The drift migrations of lithium cation ((7)Li), anion ((19)F), and solvent ((1)H) were measured independently under potentials of up to 3.0 V. Greatly enhanced dynamic lithium transport was observed for the first time in the bulk electrolyte under an electric field closely related to real conditions in a rechargeable lithium battery.

Letter↗
PubMed2006

Lithium secondary batteries using modified-imidazolium room-temperature ionic liquid.

Highly reversible, safe lithium secondary batteries that use imidazolium-cation-based room-temperature ionic liquid as an electrolyte and lithium metal as an anode material were realized by the molecular design. To achieve higher reduction stability, an electron-donating substituent was introduced to promote charge delocalization in the imidazolium cation of room-temperature ionic liquids.

Letter↗
PubMed2005

Distinct difference in ionic transport behavior in polymer electrolytes depending on the matrix polymers and incorporated salts.

Two different electrolyte salts, lithium bis(trifluoromethanesulfonyl)imide (LiTFSI), and a room temperature ionic liquid, 1-ethyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide (EMITFSI), were incorporated into network polymers to obtain ion-conductive polymer electrolytes. Network polymers of poly(ethylene oxide-co-propylene oxide) (P(EO/PO)) and poly(methyl methacrylate) (PMMA) were chosen as matrixes for LiTFSI and EMITFSI, respectively. Both of the polymer electrolytes were single-phase materials and were completely amorphous. Ionic conductivity of the polymer electrolytes was measured over a wide temperature range, with the lowest temperatures close to or below the glass transition temperatures (Tg). The Arrhenius plots of the conductivity for both of the systems exhibited positively curved profiles and could be well fit to the Vogel-Tamman-Fulcher (VTF) equation. The conductivity of the PMMA/EMITFSI electrolytes was higher at most by 3 orders of magnitude than that of the LiTFSI/P(EO/ PO) electrolytes at ambient temperature. When the ideal glass transition temperature, T0 (one of the VTF fitting parameters), was compared with the Tg, a difference in the ionic conduction was apparent in these systems. In the P(EO/PO)/LiTFSI electrolytes, the T0 and Tg increased in parallel with salt concentration and the T0 was lower than the Tg by ca. 50 degrees C. On the contrary, the difference between the T0 and the Tg increased with increasing content of PMMA in the PMMA/EMITFSI electrolytes, with the observed difference in the concentration range studied reaching up to ca. 100 degrees C. The conductivity at the Tg, sigma(Tg), for the LiTFSI/P(EO/PO) electrolytes was on the order of 10(-14-)10(-13) S cm(-1) and increased with increasing salt concentration, whereas that for the PMMA/EMITFSI polymer electrolytes reached 10(-7) S cm(-1) when the concentration of PMMA was high. The ion transport mechanism was discussed in terms of the concepts of coupling/decoupling and strong/fragile for the two different polymer electrolytes.

Journal Article↗