Activation energy-activation volume master plots for ion transport behavior in polymer electrolytes and supercooled molten salts.

We demonstrate the use of activation energy versus activation volume "master plots" to explore ion transport in typical fragile glass forming systems exhibiting non-Arrhenius behavior. These systems include solvent-free salt complexes in poly(ethylene oxide) (PEO) and low molecular weight poly(propylene oxide) (PPO) and molten 2Ca(NO3)2.3KNO3 (CKN). Plots showing variations in apparent activation energy EA versus apparent activation volume VA are straight lines with slopes given by M = DeltaEA/DeltaVA. A simple ion transport mechanism is described where the rate determining step involves a dilatation (expressed as VA) around microscopic cavities and a corresponding work of expansion (EA). The slopes of the master plots M are equated to internal elastic moduli, which vary from 1.1 GPa for liquid PPO to 5.0 GPa for molten CKN on account of differing intermolecular forces in these materials.

Journal Article↗
PubMed2005

Defect-assisted conductivity in organic ionic plastic crystals.

In order to determine the role of defects (vacancies and extended lattice defects) in the conductivity mechanism of a well studied organic ionic plastic crystal electrolyte, conductivity and mean defect volumes were measured. The ionic conductivity of the salt showed a characteristic phase dependence. Defect volumes, as measured by positron annihilation lifetime spectroscopy, showed increasing rates of expansion with increasing rotational disorder. The dependence of ionic conductivity on defect volume was observed to be phase dependent. Increases in mean defect volume size below approximately 100 cm(3) mol(-1) did not always facilitate ionic conductivity. It was shown that the material undergoes a solid-solid phase transition to the most disordered phase (a plastic crystalline phase with the highest conductivity) when the mean defect volume becomes larger than the molar volume of either the rotating anionic or cationic species. Conductivity in this phase had the strongest dependence on defect volume. Critical volumes calculated from the free volume model of Cohen and Turnbull were unrealistically large.

Journal Article↗