Recently we showed that the quasistatic response of nonlinear mesoscopic elastic solids to stress can be explained by invoking the formation of dislocation-based incipient kink bands. In this Letter, using resonant ultrasound spectroscopy, we confirm that the dynamical behavior of these nonlinear elastic systems is due to the interaction of dislocations with the ultrasound waves, thus resolving a long-standing mystery.
The physical mechanism responsible for nonlinear elastic, hysteretic, and discrete memory response of nonlinear mesoscopic elastic solids has to date not been identified. We show, by nanoindenting mica single crystals, that this response is most likely due to the formation of dissipative and fully reversible, dislocation-based kink bands. We further claim that solids with high c/a ratios, which per force are plastically anisotropic, should deform by kinking, provided they do not twin. These kinking nonlinear elastic solids include layered ternary carbides, nitrides, oxides, and semiconductors, graphite, and the layered phases, such as mica, present in nonlinear mesoscopic elastic solids.
Dislocation-based deformation in crystalline solids is almost always plastic. Here we show that polycrystalline samples of Ti3SiC2 loaded cyclically at room temperature, in compression, to stresses up to 1 GPa, fully recover on the removal of the load, while dissipating about 25% (0.7 MJ x m(-3)) of the mechanical energy. The stress-strain curves outline fully reversible, rate-independent, closed hysteresis loops that are strongly influenced by grain size, with the energy dissipated being significantly larger in the coarse-grained material. At temperatures greater than 1,000 degrees C, the loops are open, the response is strain-rate dependent, and cyclic hardening is observed. This hitherto unreported phenomenon is attributed to the reversible formation and annihilation of incipient kink bands at room-temperature deformation. At higher temperatures, the incipient kink bands dissociate and coalesce to form regular irreversible kink bands. The loss factor for Ti3SiC2 is higher than most woods, and comparable to polypropylene and nylon. The technological implications of having a stiff, lightweight machinable ceramic that can dissipate up to 25% of the mechanical energy per cycle are discussed.