One-dimensional assemblies of platinum nanoparticles on a graphite surface using nonionic/ionized mixed hemicylindrical micelle templates.

One-dimensional (1-D) self-assemblies of Pt nanoparticles on a graphite surface have been synthesized via a template-directed sintering process of individual nanoparticles, using nonionic/cationic mixed hemicylindrical micelle templates of dodecyldimethylamine oxide surfactant at graphite/solution interfaces. The dimension and morphology of Pt nanoparticles can be widely controlled by the concentration of Pt ions equivalent to the mixing ratio of nonionic and cationic species in the surfactant micelle. This approach could be extended to fabricate a wide range of self-assembling metallic nanostructures on surfaces using various nonionic/cationic mixed micelle-like self-assemblies carrying metal ions at interfaces, while providing a fundamental insight into a 1-D self-assembly from individual nanoparticles.

Journal Article↗
PubMed2005

Single-crystalline platinum nanosheets from nonionic surfactant 2-D self-assemblies at solid/aqueous solution interfaces.

Single-crystalline platinum nanosheets have been prepared via a new methodology based on the chemical reduction of a platinum salt (H2PtCl6) with hydrazine at a graphite/solution interface, using polyoxyethylene (20) sorbitan monostearate (Tween 60) based self-assembly (hemicylindrical micelle) templates. The platinum nanosheets with a uniform thickness of as thin as 3.5 +/- 1 nm are surface-smooth and continuous over relatively large length scales of micrometer sizes. In striking contrast to the Tween 60 based system, no Pt nanosheets are obtained with nonaethylene glycol monododecyl ether (C12EO9) and polyoxyethylene (23) dodecyl ether (C12EO23). No Pt nanosheets are also obtainable with a laterally homogeneous layer of Tween 60 formed at the silica/solution interface. These results indicate that surfactant Tween 60 molecules with a triple polyoxyethylene structure, as well as their hemicylindrical micelle templates, play an essential role for the formation of the Pt nanosheets. It is also suggested that the interfacially directed growth of Pt metals within the aqueous shells of the Tween 60 hemicylindrical micelles induces the thin Pt crystals as thick as the aqueous shells. The present approach could be extended to prepare a wide range of novel nanostructures of noble metals, using various micelle-like self-assemblies at interfaces.

Journal Article↗
PubMed2005

Synthesis of high surface area hydroxyapatite nanoparticles by mixed surfactant-mediated approach.

A new surfactant-mediated approach was developed to synthesize hydroxyapatite (HAp) nanoparticles with high surface areas by calcination of their precursors encapsulated with calcium stearate using mixed surfactant-containing reaction mixtures. Acidic aqueous solution of calcium phosphate was mixed with both or either nonaoxyethylene dodecyl ether (C12EO9) and polyoxyethylene(20) sorbitan monostearate (Tween 60) and then was treated with aqueous ammonium at 25 degrees C. The C12EO9-based single surfactant system yielded an aggregate of platy HAp nanoparticles 20-40 nm in size, whereas the Tween 60-based single and mixed systems led to lath-shaped HAp nanoparticles 2-8 nm wide and encapsulated with calcium stearate. On calcination at 500 degrees C, the stearate-encapsulated HAp nanoparticles in the latter two systems were deorganized into high surface area HAp nanoparticles. Particularly, the HAp nanoparticles in the mixed system exhibited a specific surface area as high as 364 m2 g(-1) that is roughly 3 times larger than 160 m2 g(-1) for those in the single system. The significantly high surface area for the former is attributed to much less adhesion of decapsulated HAp nanoparticles, which originated from the particle-separating effect of the C12EO9 molecules adsorbed on the outer surface of the stearate-encapsulated HAp nanoparticles to inhibit their agglomeration or interfacial coordination. The present results demonstrate that the mixed use of two different surfactants as a source of encapsulating and templating agent and a particle-separating agent is specifically effective for the synthesis of high surface area HAp nanoparticles.

Journal Article↗
PubMed2002

Development and evaluation of a simple calorimeter for the measurement of resting metabolism.

1. A simple calorimeter based on the measurement of oxygen uptake has been developed. 2. A respiratory simulator was used to evaluate oxygen uptake at different flow rates. A known concentration of mixed gases flows into the calorimeter via the respiratory simulator. Oxygen concentration and flow rate were measured and stored to memory for further analysis. 3. Results indicate that large errors occur at low flow rates, but that the error is less than 5% under normal conditions. 4. This device can be used to measure oxygen uptake under resting conditions.

Calorimetry, Indirect↗