PubMed2006

Photochemical electron transfer through [corrected] the interface of hybrid films of titania nano-sheets and mono-dispersed spherical mesoporous silica particles.

Photochemical Electron Transfer (ET) between an organic dye, the porphyrin derivative TMPyP, and an electron acceptor, methyl viologen MV2+, have been investigated at the interface of two different inorganic films, i.e., layered titania nano-sheets (TNS) and a monolayer film of spherical and mono-dispersed mesoporous silica (sMPS) particles (ca. 0.5 microm). TMPyP ions were intercalated within the sMPS nano-cavities to form (TMPyP-sMPS) while MV2+ ions were intercalated into the TNS interlayers to form (MV2+-TNS). The (TMPyP-sMPS) and (MV2+-TNS) films were then stacked on a silica substrate in this order to form a (MV2+-TNS)/(TMPyP-sMPS) film and, upon UV light irradiation, ET could be induced. However, when this film was stacked inversely, i.e., for the (TMPyP-sMPS)/(MV2+-TNS) films on a silica substrate, no photoinduced ET were observed. Interestingly, however, even for this photo-inactive inversely stacked film, ET could be generated by inserting a gold vapor-deposited layer between the (MV2+-TNS) and (TMPyP-sMPS) films. The conjugation conditions at the interface of the inversely stacked (TMPyP-sMPS)/(MV2+-TNS) hybrid film were, thus, confirmed to strongly affect the photoinduced electron transfers and their efficiencies.

Biocompatible Materials↗

PubMed2005

Layered double hydroxide hybrids with dicetylphosphate.

Dicetyl phosphate (DCP) ions incorporated into layered double hydroxide (LDH) clays to form a DCP/LDH hybrid were prepared and structurally characterized by X-ray diffraction analysis, scanning electron microscopy, thermogravimetry, and differential thermal analyses. DCP was concluded not only to form well-aligned bilayer structures along the vertical axis of the LDH layers but also to be arranged in a distorted hexagonal packing orientation in the lateral planes within the DCP/LDH hybrid interlayers.

Journal Article↗

PubMed2005

Odd-even effect of the methylene chain number in the template polymerization of alpha,beta-diacetylenecarboxylates incorporated in layered double hydroxide clay.

The present investigation reports on the significant differences observed in the efficiency of the polymerization depending on the odd- or even-numbered methylene chains of diacetylenecarboxylates, CH3(CH2)(m-1)C[triple bond]C-C[triple bond]C(CH2)(n-1)CO2- (mono-[m,n]), incorporated in layered double hydroxide (LDH) clay. Upon gamma-ray irradiation of the diacetylenecarboxylates, or mono-[m,n], in LDH clay, polymer hybrids or poly-[m,n]/LDH, which exhibited coloring from light orange to violet, were obtained. The color of the poly-[m,n]/LDH hybrids was strongly dependent on the extent of the polymerization degrees. Moreover, the polymerization degrees were controlled by the number of methylene spacers n between the carboxyl and diacetylene groups. An odd-numbered n for the methylene chain of mono-[m,n] was found to be the determining factor in the efficient polymerization of these self-assembling aggregates within the interlayers of LDH clay.

Letter↗

PubMed2005

Photoinduced one-electron reduction of MV2+ in titania nanosheets using porphyrin in mesoporous silica thin films.

Composite films of a meso-(tetramethylpyridinium)porphyrin (TMPyP) hybrid incorporated in mesoporous silica (MPS) and cast on a methyl viologen (MV2+)/titania nanosheet hybrid were synthesized and a light-induced charge separation between the two could be observed. These composite thin films were able to initiate a one-electron reduction of the MV2+ ions accompanied by the simultaneous decomposition of the TMPyP organic dye within the mesoporous silica channels.

Journal Article↗

PubMed2005

Reversible color changes in lamella hybrids of poly(diacetylenecarboxylates) incorporated in layered double hydroxide nanosheets.

The present study is an investigation of a reversible thermal color change induced in lamella hybrids of poly(diacetylenecarboxylates) incorporated in layered double hydroxide (LDH) nanosheets. These poly-[m,n]/LDH hybrids prepared by the photo- or gamma-ray-induced polymerization of diacetylenecarboxylates, i.e., CH(3)(CH(2))(m)()(-)(1)CC-CC(CH(2))(n)()(-)(1)CO(2)(-) (mono-[m,n]), and intercalated in LDH lamella sheets, were observed to develop colors ranging from yellow to blue. The change in color was found to depend greatly on the alkyl carbon numbers of the mono-[m,n] (m,n = 10,11; 5,11; 10,5; 16,1) values. Moreover, the conformational alignment of the mono-[m,n] within the LDH was observed to be a crucial factor in color development, which was greatly affected by the intercalation degrees and extent of poly(ene-yne) linkage elongation of the polymers. For the poly-[m,n]/LDH hybrids investigated, a reversible color change was found to occur repeatedly and remarkably for the poly-[10,11]/LDH hybrid. This color change occurred at temperatures between ca. 20 and 80 degrees C back and forth from purple red to bright orange, in stark contrast to the irreversible color change for poly-[10,11] without LDH. Moreover, DSC and Raman spectroscopic studies of the LDH hybrids showed that the thermochromic temperature corresponded to the phase transition temperature of 80 degrees C. XRD analysis also indicated that the poly-[m,n]/LDH hybrid could retain its lamella structure during such thermochromic color changes, enabling conformational recovery in the polymer chains by a cooling down of the hybrids to temperatures lower than the transition temperature, while the nonhybrid poly-[10,11] powders exhibited an irreversible color change at 60 degrees C, above which the polymer powder turned amorphous.

Journal Article↗

PubMed2003

Reversible light-driven structural changes between the mono- and bilayer stacking alignments in 4-octadecyloxystilbazolium arylcarboxylate films.

The present investigation deals with the light-driven morphological changes in multilamella films of N-methyl-4-octadecyloxystilbazolium arylcarboxylates (C18OStz+X-) cast on glass slides. The results of XRD analysis show a photostimulated layer expansion and shrinkage of the stacked thin films along the c-axis under alternative illumination at >350 and 254 nm, respectively. It was revealed that such lamellar changes could be switched either way by a reversible transformation between the mono- and bilayer units in these stacked multilamella films. Moreover, such controlled structural adjustments in the alignment could be initiated by the photocyclodimerization of the stilbazolium moieties of the arylcarboxylate salts; i.e., a monolayer-to-bilayer transformation could be induced at a stage of only 10% cyclodimer formation. The photoinduced patterning on the surface of the films was also analyzed by SEM and fluorescence microscopic investigations.

Journal Article↗