Self-assembly patterning of silica colloidal crystals.

We developed a self-assembly process of silica particles to fabricate desired patterns of colloidal crystals having high feature edge acuity and high regularity. A micropattern of colloidal methanol prepared on a self-assembled monolayer in hexane was used as a mold for particle patterning, and slow dissolution of methanol into hexane caused shrinkage of molds to form micropatterns of close-packed SiO2 particle assemblies. This result is a step toward the realization ofnano/micro periodic structures for next-generation photonic devices by a self-assembly process.

Journal Article↗

PubMed2004

Self-assembly patterning of colloidal crystals constructed from opal structure or NaCl structure.

We developed a novel self-assembly process to fabricate an orderly array of particle wires constructed from a close-packed colloidal crystal without preparation of patterned templates. A substrate was immersed vertically into a SiO2 colloidal solution, and the liquid surface moved downward upon evaporation of solution. Particles formed a mono-/multiparticle layer, which was cut by the periodic drop-off of solution. The orderly array of particle wires was successfully fabricated, showing the suitability of the self-assembly process for the fabrication of nano-/microstructures constructed from nano-/microparticles or blocks. The mechanism of the assembly process and control of thickness, width, and interval of particle wires were further discussed. Moreover, an array of particle wires constructed not from close-packed face-centered cubic (or hexagonal close packed) structure but from two kinds of particles was realized to fabricate an array of particle wires with NaCl structure by this self-assembly process.

Journal Article↗