Molecular hydrogen storage in binary THF-H2 clathrate hydrates.

The hydrogen storage capacity of binary THF-H(2) clathrate hydrate has been determined as a function of formation pressure, THF composition, and time. The amount of hydrogen stored in the stoichiometric hydrate increases with pressure and exhibits asymptotic (Langmuir) behavior to approximately 1.0 wt % H(2). This hydrogen concentration corresponds to one hydrogen molecule occupying each of the small 5(12) cavities and one THF molecule in each large 5(12)6(4) cavity in the hydrate framework. Contrary to previous reports, hydrogen storage was not increased upon decreasing the THF concentration below the stoichiometric 5.6 mol % solution to 0.5 mol %, at constant pressure, even after one week. This provides strong evidence that THF preferentially occupies the large 5(12)6(4) cavity over hydrogen, for the range of experimental conditions tested. The maximum amount of hydrogen stored in this binary hydrate was about 1.0 wt % at moderate pressure (<60 MPa) and is independent of the initial THF concentration over the range of conditions tested.

Journal Article↗

PubMed2006

Molecular hydrogen occupancy in binary THF-H2 clathrate hydrates by high resolution neutron diffraction.

We have determined the time-space average filling of hydrogen molecules in a binary tetrahydrofuran (THF)-d(8) + D(2) sII clathrate hydrate using high resolution neutron diffraction. The filling of hydrogen in the lattice of a THF-d(8) clathrate hydrate occurred upon pressurization. The hydrogen molecules were localized in the small dodecahedral cavities at 20 K, with nuclear density from the hydrogen approximately spherically distributed and centered in the small cavity. With a formation pressure of 70 MPa, molecular hydrogen was found to only singly occupy the sII small cavity. This result helps explain discrepancies about the hydrogen occupancy in the THF binary hydrate system.

Furans↗