Effect of high-pressure ammonia treatment on the activity of Ge3N4 photocatalyst for overall water splitting.

The photocatalytic activity of beta-Ge(3)N(4) powder for overall water splitting is successfully enhanced by ammonia treatment at 823 K for 5-24 h at ammonia pressures of 20 MPa or greater. The surface and bulk nitrogen content in the treated samples varies according to the treatment temperature and treatment time, related to the stability of beta-Ge(3)N(4) powder under pressurized ammonia. The change in nitrogen content resulted in a change in the photocatalytic activity for overall water splitting. A beta-Ge(3)N(4) powder treated at 823 K for 5 h under ammonia at 20 MPa exhibited a photocatalytic activity 4 times higher than that of the as-synthesized powder, attributable to a decrease in the density of anion defects in the bulk and surface.

Journal Article↗
PubMed2005

Tetragonal nanocrystals from the Zr0.5Ce0.5O2 solid solution by hydrothermal method.

The formation of tetragonal Zr(0.5)Ce(0.5)O(2) solid solution nanocrystallites of 5 +/- 1 nm size by a hydrothermal method at 120 degrees C for 6 h was confirmed by careful Raman and XRD studies for the first time. It was characterized as the t' '-form with an axial ratio of c/a = 1 but with oxygen ion displacements. The as-prepared sample was hydrous in nature, which is responsible for the lattice expansion. However, most of the water held in the structure can be expelled by heating the sample above 600 degrees C. Above 1050 +/- 50 degrees C the t' '-form of tetragonal Zr(0.5)Ce(0.5)O(2) solid solution dissociates into two phases, cubic phase and the t-form of tetragonal phases.

Journal Article↗
PubMed2005

Direct fabrication of TiO2 nanoparticles deposited on hydroxyapatite crystals under mild hydrothermal conditions.

TiO2 nanoparticles-deposited on hydroxyapatite (HAp) have been successfully synthesized by direct (single step) hydrothermal treatments of a CaCO3 suspension in a H3PO4 solution with 10 vol% TAS-FINE (titanium amine complex) at 150 degrees C for 6 h or 120 degrees C for 12-24 h under nearly neutral pH conditions. The obtained products were characterized by XRD, SEM-EDX, visible, Raman, and TEM. The XRD and Raman results showed the formation of HAp and TiO2 anatase phases under these hydrothermal conditions. SEM and TEM observations revealed that anatase TiO2 nanoparticles with the size of about 10 nm were deposited on the surfaces of the HAp crystals.

Coated Materials, Biocompatible↗