PubMed2000
All biomaterials used for total joint surgery are subjected to wear mechanisms. Morse taper junctions of modular hip revision implants are predilection sites for both fretting and crevice corrosion, dissociation and breakage of the components. The aim of this study is to quantify wear and study metallurgical changes of Morse taper junctions of in-vitro and in-vivo loaded modular revision stems. Three modular revision stems (MRP-Titan, Peter Brehm GmbH, Germany) were loaded by a servohydraulic testing machine. The loads and conditions used exceeded by far the values required by ISO-standard 7206. The tests were performed with maximum axial loads of 3,500 N to 4,000 N over 10-12 x 10(6) cycles at 2 Hz. Additionally, the female part of the taper junctions were coated with blood and bone debris. The free length of the implant was set to 200 mm. One other MRP stem was investigated after retrieval following 5.5 years of in-vivo use. All contact surfaces of the modular elements were assessed by visual inspection, optical microscopy and scanning electron microscopy (SEM). The degree of plastic deformation of the male part of the morse taper junction was determined by contouroscopy. None of the morse taper junctions broke or failed mechanically. Corrosion and wear affected all tapers, especially at the medial side. The retrieved implant showed no cracks and the amount of debris measured only one third of that for the stems tested in-vitro. The present retrieval and laboratory investigations have proven, that the morse taper junctions of the MRP-titanium stem are stable and resistant to relevant wear mechanisms. The longevity of the junctions for clinical use is given. If an optimal taper design is selected, the advantages of modular femoral components in total hip revision arthroplasty will outweigh the possible risks.