Biomedical subjects

Ulrich Lohbauer

Publications and source records attributed to Ulrich Lohbauer.

14 recordsLinked to original sources

PubMed2006

Strength and fatigue performance versus filler fraction of different types of direct dental restoratives.

The aim of this study was to evaluate the mechanical properties, such as Young's moduli, fracture strengths (FS), and flexural fatigue limits of todays resin composite dental restoratives. All materials have been subdivided into flowable, aesthetic hybrid and nano-filled hybrid composites as marketed by dental manufacturers and analyzed in terms of the actual filler configurations. Specimen bars have been manufactured in reference to ISO 4049 standard, light-cured for 20 s, and stored in distilled water before testing. The elastic moduli (EM), FS, and flexural fatigue limits (FFL) were measured after 14 days storage by using the four-point bending test. The FFL was determined for 10(4) cycles. The fatigue data were analyzed by using the "staircase" approach and statistically treated by ANOVA analysis. Flowable materials with a reduced filler content exhibited the lowest Young's moduli, compared with those measured for higher filled materials. A linear relationship has been found between elastic moduli and filler loading (r(2) = 0.798). Correlations of FS and fatigue data to different filler fractions could not be proved. FS ranged between 61.3 and 124.9 MPa. After 10(4) cycles of fatigue loading, the FS suffered from a decrease between 45.2 and 61.7%. However, materials providing high initial strengths do not obviously reveal the best fatigue resistance. A marketing-based grouping of direct restorative materials has no meaning toward laboratory testing of mechanical properties.

Dental Restoration, Permanent↗

PubMed2005

Characterisation of resin-dentine interfaces by compressive cyclic loading.

The aims of this in vitro study were to evaluate the ultra-morphological changes in resin-dentine interfaces after different amounts of thermomechanical load (TML), and to determine the corresponding microtensile bond strengths (microTBS). Enamel/dentine discs with a thickness of 2 mm were cut from 24 human third molars and bonded with four adhesives involving different adhesion approaches: Syntac (Ivoclar Vivadent; used as multi-step etch-and-rinse adhesive), Clearfil SE Bond (Kuraray; two-step self-etch adhesive), Xeno III (Dentsply DeTrey; mixed all-in-one self-etch primer adhesive system), and iBond (Heraeus Kulzer; non-mixed all-in-one self-etch adhesive). The resin-dentine discs were cut into beams (width 2 mm; 2 mm dentine, 2 mm resin composite) and subsequently subjected to cyclic TML using ascending amounts of mechanical/thermal cycles (20 N at 0.5 Hz of mechanical load and 5-55 degrees C of thermal cycles: for 0/0, 100/3, 1,000/25, 10,000/250, 100,000/2,500 cycles). Loaded specimens were either cut perpendicularly in order to measure microTBS (n=20; crosshead speed: 1 mm/min) or were immersed in an aqueous tracer solution consisting of 50 wt% ammoniacal silver nitrate and processed for ultra-morphological nanoleakage examination using transmission electron microscopy (TEM). microTBS were significantly decreased by increasing amounts of TML for all adhesives (p<0.05). Bond strengths after 0 vs. 100,000 thermomechanical cycles were: Syntac: 41.3/30.1 MPa; Clearfil SE Bond 44.8/32.5 MPa; Xeno III 27.5/13.7 MPa; iBond 27.0/6.2 MPa. Relatively early, a certain amount of nanoleakage was observed in all groups by TEM, which was more pronounced for Xeno III and iBond. The incidence of nanoleakage remained stable or was even reduced with increasing load cycles for all adhesives except iBond, where exact failure origins were detected within the adhesive and at the top of the hybrid layer.

Adhesiveness↗

PubMed2005

The effect of different light-curing units on fatigue behavior and degree of conversion of a resin composite.

OBJECTIVES: The aim of this study was to investigate the effect of different light-curing units and irradiation modes on the mechanical fatigue strength and degree of conversion of a restorative resin composite. METHODS: Conventional halogen, plasma arc and blue LED light-curing units were used for polymerization of a resin composite (Tetric) Ceram, Ivoclar, Vivadent, Liechtenstein). Initial fracture strength (FS) and flexural fatigue limit (FFL) as well as degree of conversion (DC) were measured. The FFL was determined under cyclic loading for 10(5) cycles in terms of a staircase approach. The specimens were stored for 14 days in 37 degrees C distilled water prior to testing. The curing efficiency was observed with Fourier transform infrared micromultiple internal reflectance spectroscopy. The measurements were carried out at 0.5 and 2.5 mm distance from the directly irradiated surface after 14 days storage in dark and dry conditions at 37 degrees C. RESULTS: The highest FS, FFL and DC were observed from high energy curing devices and from extended curing intervals. The conventional halogen light exhibited the most homogenous in-depth curing efficiency along with a low loss of mechanical resistance under cyclic fatigue. SIGNIFICANCE: Evaluation of flexural fatigue limit and curing efficiency correlate in terms of decreased mechanical strength due to insufficient light-curing intervals or light intensities. Initial promising fracture strengths do not correlate with a clinically more relevant fatigue loading and with the in-depth degree of conversion, both accounting for a significantly reduced strength performance.

Analysis of Variance↗

PubMed2005

Evaluation of resin composite materials. Part I: in vitro investigations.

PURPOSE: To evaluate different resin-based composites using a variety of in vitro investigation methods to predict their clinical behavior. METHODS: Materials selected for this study were Heliomolar radiopaque (microfilled), Tetric Ceram, Pertac II (minifilled hybrids), Ariston pHc (ion releasing hybrid), and Solitaire I (hybrid with porous fillers). The evaluated in vitro criteria were three-body wear according to the ACTA method, microtensile bond strengths to enamel and dentin, flexural strength (four-point bending strength), flexural fatigue behavior (flexural fatigue limit), and calcium ion release (for Ariston pHc). RESULTS: Concerning wear resistance, Ariston pHc (20.5 microm after 200,000 cycles) was inferior to the other materials (13.7-15.9 microm). Microtensile bond strengths to dentin were similar for Heliomolar (32.0 MPa), Tetric Ceram (30.4 MPa; both bonded with Syntac Classic), and Pertac II (30.8 MPa; bonded with EBS Multi) being above Solitaire I (22.5 MPa; bonded with Solidbond) being above Ariston pHc (13.2 MPa; bonded with Ariston Liner). Enamel bond strengths for Heliomolar (40.0 MPa), Tetric Ceram (36.5 MPa), and Pertac II (38.9 MPa) were significantly higher than for Solitaire I (26.6 MPa) which was above Ariston pHc (7.2 MPa). Heliomolar, Tetric Ceram, and Pertac II revealed higher micro-TBS to enamel than to dentin, Ariston showed the contrary, and Solitare exhibited no difference between enamel and dentin micro-TBS. Solitaire I exhibited a lower initial flexural strength than the other materials, the computed fatigue strength of the material even dropped to the level of glass ionomer cements (17.9 MPa). Long-term calcium release data for Ariston exhibited a continuously high calcium release becoming lower at the end of the observation beyond 21 months.

Acrylic Resins↗

PubMed2004

In situ non-invasive spectral discrimination between bone cell phenotypes used in tissue engineering.

Raman micro-spectroscopy was used to discriminate between different types of bone cells commonly used in tissue engineering of bone, with the aim of developing a method of phenotypic identification and classification. Three types of bone cells were analysed: human primary osteoblasts (HOB), retroviral transfected human alveolar bone cells with SV40 large T antigen (SV40 AB), and osteoblast-like human osteosarcoma derived MG63 cell line. Unsupervised principal component analysis (PCA) and linear discriminant analysis (LDA) of the Raman spectra succeeded in discriminating the osteosarcoma derived MG63 cells from the non-tumour cells (HOB and SV40 AB). No significant differences were observed between the Raman spectra of the HOB and SV40 AB cells, confirming the biochemical similarities between the two cell types. Difference spectra between tumour and non-tumour cells suggested that the spectral discrimination is based on the fact that MG63 osteosarcoma derived cells are characterised by lower concentrations of nucleic acids and higher relative concentrations of proteins compared to the non-tumour bone cells. A supervised classification model (LDA) was built and showed high cross-validation sensitivity (100%) and specificity (95%) for discriminating the MG63 cells and the non-tumour cells, with 96% of the cells being correctly classified either as tumour or non-tumour derived cells. This study proves the feasibility of using Raman spectroscopy to identify in situ phenotypic differences in living cells.

Cell Line↗

PubMed2004

The effect of six years of water storage on resin composite bonding to human dentin.

The aim of this in vitro study was to evaluate dentin bond strength and marginal adaptation of direct resin composite fillings after different storage times. Three hundred sixty cavities were prepared in discs of freshly extracted human third molars and filled with resin composites. Multistep self-etching adhesives (Syntac Classic, A.R.T. Bond, both with and without total etching), three-step etch-and-rinse adhesives (Scotchbond Multi-Purpose Plus, EBS), and two-step etch-and-rinse adhesives (Prime and Bond 2.0, Syntac Single-Component) were used for bonding. After 1, 90, and 2190 days of water storage and 24 h thermocycling (1150 cycles), push-out testing was performed. From the 6-year group, replicas were made after 1 day, 90 days, and 1, 2, 3, 4, 5, and 6 years, and examined regarding marginal adaptation under an SEM (x 200 magnification). In all groups under investigation, push-out bond strengths remained stable after 90 days; however, the strengths significantly decreased after 6 years of water storage. The two-step systems exhibited lower bond strengths than three-step systems after 6 years. Marginal analysis revealed a significant loss regarding the percentage of perfect margins having been stable after 2 years for the three-step etch-and-rinse systems. Overall, the older three-step systems proved to be more effective than the simplified adhesives Syntac Single-Component and Prime and Bond 2.0 with regard to bond strength and marginal adaptation.

Adhesives↗

PubMed2004

Toughening of dental glass ionomer cements with reactive glass fibres.

A fibre reinforced glass ionomer cement (FRGIC) for dental applications was loaded with 20 vol% short fibres (430 microm) with a glass composition in the system SiO(2)-Al(2)O(3)-CaF(2)-Na(3)AlF(6). The fracture toughness and the total energy release rate were examined. A 20% anisotropic fibre alignment was observed, perpendicular to the loading direction. An increase of fracture toughness of 140% and of total energy release rate of 440% was achieved compared to the unreinforced glass ionomer cement. Matrix-fibre interface reaction is supposed to exert the major influence on mechanical behaviour of FRGIC by controlling fibre pull-out and thus the total energy release rate.

Anisotropy↗

PubMed2004

Influence of c-factor and layering technique on microtensile bond strength to dentin.

OBJECTIVE: Due to polymerisation shrinkage of resin-based composites, a high configuration factor in deep Class I cavities leads to a certain amount of stress when the material is bonded. The aim of this in vitro study was to evaluate the influence of c-factor and different layering approaches on bonding to dentin with three different adhesive systems. MATERIALS AND METHODS: Dentin bond strengths of Z250 bonded with OptiBond FL, Single Bond, and One Up Bond F were measured on flattened dentin surfaces without cavity walls and on the cavity floor of Class I cavities (10 layering concepts). The resin composite increments were applied horizontally, vertically and obliquely, both with and without a flowable liner. The tests were carried out in a microtensile apparatus at a crosshead speed of 1 mm/min after 24 h of storage at 37 degrees C in water. Mean bond strengths were analysed using the Wilcoxon test and multiple comparisons according to the Mann-Whitney U-test. Specimens having failed prior to the bond strength test were included as 0 MPa. RESULTS: The groups bonded on flat surfaces exhibited significantly higher bond strengths than specimens cut from filled cavities. Within the cavity groups, OptiBond FL and Single Bond exhibited no significant differences, however, being above One Up Bond F. Within the groups of each adhesive, major differences between the layering concepts were detectable. Bulk technique led to low dentin adhesion at the cavity floor, above all for Single Bond and One Up Bond F. Horizontal layers resulted in significantly higher bond strengths than did vertical or oblique. Lining with a flowable composite did not promote bond strength for OptiBond FL. For the other adhesives, a lining improved adhesion when vertical or oblique layers were applied, for horizontal increments no effect was evident. CONCLUSIONS: The c-factor is an influencing factor for dentin adhesion. However, using an appropriate layering technique, high bond strengths to deep cavity floors can be achieved.

Bisphenol A-Glycidyl Methacrylate↗

PubMed2003

Evaluation of the fatigue behavior of the resin-dentin bond with the use of different methods.

The clinical performance of directly bonded resin composites is fundamentally dependent on durable adhesion to prevent gap formation over time. The goal of this investigation was to evaluate the effectiveness of various dentin adhesives by means of quasistatic and dynamic dentin bond strengths, and also to determine marginal and internal gap formation after loading in an artificial oral environment. Three hundred thirty human third molars were used within four weeks of extraction. Adhesives used were A.R.T. Bond, OptiBond FL, Scotchbond Multi-Purpose Plus, Single Bond, Prime & Bond NT, and One Up Bond F for bonding of one resin composite (Z 250). Buccal and lingual aspects of 90 teeth were ground flat to expose dentin, then resin composite cylinders were bonded. Initial bond strengths (n = 10) and adhesive fatigue limits (n = 20) were determined with the use of a shear test apparatus. One hundred eighty conical cavities were prepared into dentin discs and filled with the same materials. After 21 days of storage, initial push-out bond strengths (n = 10) and adhesive fatigue limits (n = 20) were measured. Sixty molars with MO cavities (n = 10) with margins below the cement-enamel junction were filled. Before and after thermomechanical loading (100000 x 50 N and 2500 x thermocycling between + 5 and + 55 degrees C), marginal gap formation and internal adaptation (only after loading) were analyzed under a SEM (x 200). The one-bottle systems showed higher shear bond strengths when evaluated statically and dynamically. However, cyclic fatigue push-out bond strengths resulted in higher values for older multistep systems. Marginal and internal gap analysis confirmed the results, in favor of older adhesive systems (p <.05; Mann-Whitney U test).

Composite Resins↗

PubMed2003

Flexural fatigue behavior of resin composite dental restoratives.

OBJECTIVE: The aim of this study was to evaluate the mechanical properties of resin composite dental restoratives under quasi-static and cyclic loading. METHODS: Four-point-bending bars of 10 different resin composite materials were manufactured according to ISO standard and stored for two weeks in distilled water. The fracture strength (FS) was measured with the four-point-bending test in an universal testing machine. The flexural fatigue limits (FFL) for 10(5) cycles were determined under equivalent loading. All specimens were tested and fatigued in water at 37 degrees C. The data were analyzed using ANOVA, Weibull statistics of FS and the 'staircase' approach of FFL. Fractographic analysis was performed using SEM. RESULTS: The initial flexural strength values for the resin composite materials varied from 55.4 MPa for Solitaire up to 105.2 MPa for Filtek Z250. The mean flexural fatigue limit for 10(5) cycles ranged between 37 and 67% of the initial strength. SEM analysis of the fractured surfaces suggests two kinds of failure mechanisms for initial and fatigue fracture. SIGNIFICANCE: The fatigue behavior of resin composite materials does not correlate with initial strength values. Materials providing high initial strengths do not obviously reveal the best fatigue resistance. Flexural fatigue measurement of resin composite materials should be viewed as a useful tool to evaluate long term mechanical properties.

Analysis of Variance↗

PubMed2003

Reactive fibre reinforced glass ionomer cements.

The mechanical properties of glass ionomer cements used in restorative dentistry reinforced by chopped glass fibres were investigated. Reactive glass fibres with a composition in the system SiO(2)-Al(2)O(3)-CaF(2)-Na(3)AlF(6) and a thickness of 26 microm were drawn by a bushing process. The manufacturing parameters were optimized with respect to maximum strength of the glass fibre reinforced ionomer cements. Powder to liquid ratio, pre-treatment of the glass, grain size distribution and fibre volume fraction were varied. Glass fibre and cement were characterized by X-ray diffraction, transmission electron microscopy and energy dispersive spectroscopy techniques, respectively. The highest flexural strength of the reinforced cement (15.6 MPa) was found by compounding 20 vol% reactive fibres and extending the initial dry gelation period up to 30 min. Microscopic examination of the fractured cements indicated a distinct reactive layer at the fibre surface. A pronounced fibre pull out mode gives rise to an additional work-of-fracture contributed by pulling the fibres out of the fracture surface.

Compressive Strength↗

PubMed2003

Time-dependent strength and fatigue resistance of dental direct restorative materials.

Elastic modulus (EM), initial fracture strength (FS) and flexural fatigue limit (FFL) of dental restorative materials were measured in a simulated oral environment to correlate mechanical response under the influence of water with the chemical nature of the test materials under investigation. One resin composite (RC; Tetric Ceram, Ivoclar-Vivadent Corp., Liechtenstein), an ion-leaching resin composite (ILRC; Ariston pHc, Ivoclar-Vivadent Corp., Liechtenstein) a compomer (CO; Dyract AP, Dentsply Corp., USA) and a glass-ionomer cement (GIC; Ketac Molar, 3MEspe Corp., Germany) were tested. Static EM, FS and dynamic FFL experiments were performed. The FFL was determined under cyclic loading for 10(5) cycles in terms of a staircase approach. The materials were stored for 1, 8, 30, 90 and 180 days in 37 degrees C distilled water, respectively. The RC degraded over time due to water adsorption followed by failure within the resin matrix. The ILRC suffered from a pronounced decrease in FS as well as in FFL due to a constant ion-leaching and macroscopic crack growth. CO failed over time due to resin-filler interface cracking. The GIC exhibited improved mechanical performance over time due to a post-hardening mechanism. The results reveal the necessity for substantial preclinical evaluation of direct restorative materials. The material parameters under investigation are capable of predicting clinical performance over time.

Journal Article↗

PubMed2003

Fatigue behavior of the resin-resin bond of partially replaced resin-based composite restorations.

PURPOSES: (1) To evaluate different pre-treatment modes for partial resin-based composite repair using a shear bond strength fatigue design on aged specimens, and (2) to investigate the effect of these pre-treatments on aged and partially replaced Class II resin-based composite restorations. MATERIALS AND METHODS: (Study 1) 150 composite discs (Tetric Ceram) were light-cured, secondary cured, and stored in water for 365 days. The specimens were randomly assigned to five pretreatment groups (n=30): (1) Roughening with a finishing diamond bur + dentin bonding system (DBS, Syntac Classic), (2) Roughening with a silicon carbide bur + DBS, (3) Roughening with a silicon carbide bur + DBS + Tetric Flow, (4) silica-coating (CoJet) + DBS, and (5) silica-coating + dentin bonding agent + Tetric Flow. The disks were restored with fresh repair composite cylinders and after 24-hour water storage, initial bond strengths (n=10) and fatigue bond strengths (n=20; 5,000 cycles in shear mode) were evaluated and fracture modes determined under a SEM. (Study 2): 40 Class II restorations (EBS Multi/Pertac II) were placed in extracted human third molars. The specimens were stored for 365 days and then replaced partially by removing the proximal box and leaving the occlusal part. The partial repairs (Pertac II) were placed after identical pre-treatment modes A-E (n=8). After thermomechanical loading (100,000 x 50 N, simultaneously x2,500 at 5 degrees C/55 degrees C), marginal quality between old and fresh composite was evaluated by SEM at x200 magnification and dye penetration was observed by light microscopy under x50 magnification. RESULTS: Initial repair bond strengths were significantly higher for the groups with additional application of flowable composite compared to composite only (P<0.05; Mann Whitney U test). Diamond finishing revealed the lowest bond strengths. Fatigue bond strengths exhibited the worst results for Group 1 as well, but were similar for Groups 2-5. In the Class II partial repair simulation, Groups 3 and 5 with additional flowable lining exhibited significantly better marginal quality and significantly lower leakage, whereas the other groups revealed up to 100% separation between aged and freshly applied composite.

Composite Resins↗

PubMed2002

Lifetime prediction of CAD/CAM dental ceramics.

The dynamic fatigue method was used to obtain subcritical crack growth parameters n and A for a commercial feldspathic dental porcelain and for a lanthanum-glass-infiltrated alumina glass ceramic. Five stress rates d sigma/dt ranging from 50 to 0.01 MPa s(-1) were applied. The inert strength values were calculated with the use of Weibull statistics and maximum-likelihood approaches for the Weibull parameter m. Strength-probability-time (SPT) diagrams were derived for both materials. The alumina glass composite showed a high fracture strength sigma(0) (442 MPa) at a failure probability of P(F) = 63.2% and a high resistance against subcritical crack growth (n = 36.5). The development of strength under fatigue conditions was calculated for exemplary 1 year. The strength of the alumina glass material dropped to 228 MPa within this period. This fact is due to a low content of infiltrated lanthanum glass phase in the composite material (25 wt%). In contrast, for the high-silica-glass-containing porcelain a distinct decrease of strength sigma(0) from initial 133 to 47 MPa after 1 year was predicted. This, mainly because of a low crack growth resistance (n = 16.8) of the feldspathic porcelain. Much lower strength values were calculated, assuming a failure probability of P(F) = 5%. The decrease is mainly caused by the sensitivity of high-glass-containing ceramics against water corrosion.

Aluminum Oxide↗