PubMed2004

Effect of carbamide peroxide bleaching agents on tensile strength of human enamel.

OBJECTIVES: The aim of this study was to evaluate the effects of low concentrations of carbamide peroxide bleaching agents (CP) on the ultimate tensile strength of enamel (UTS). METHODS: Resin composite structure was built-up on the bonded occlusal surface of 12 sound third molars to facilitate specimen preparation for microtensile testing. The bonded teeth were sectioned in a bucco-lingual direction in slices approximately 0.7 mm thick. Each slice was trimmed with a fine diamond bur to reduce the buccal, internal slope enamel of the cusps to a dumb-bell shape with a cross-sectional area at the 'neck' of less than 1 mm2. The sample was randomly divided into six groups of 10 specimens each: Control (C-untreated); Opalescence 10% (O10), Opalescence 15% (O15), Opalescence 20% (O20), Whiteness 10% (W10) and Whiteness 16% (W16). Specimens in each group received the application of the CP for 6 h/day, at 37 degrees C, during 14 days and were stored in artificial saliva in between each application. After the bleaching regimen, specimens were tested with the microtensile method at 0.5 mm/min. Data were analyzed by ANOVA and Tukey test (5%). RESULTS: Mean tensile strengths were (MPa): C = 47.5 +/- 6.2a; O10 = 37.6 +/- 5.8b; O15 = 33.2 +/- 6.0b; O20 = 31.2 +/- 3.5b; W10 = 32.5 +/- 6.1b; W16 = 30.6 +/- 7.7b. Specimens subjected to the bleaching regimen presented significantly lower UTS than the control group. No differences were found among the type and concentration of the bleaching agents. SIGNIFICANCE: Results suggested that bleaching enamel with CP could significantly reduce its UTS within a 14 days treatment.

Analysis of Variance↗

PubMedDate not supplied

Peroxide bleaching agent effects on enamel surface microhardness, roughness and morphology.

The aim of this study was to evaluate the surface roughness, microhardness and morphology of human enamel exposed to six bleaching agents (at baseline and post-treatment). Human dental enamel samples were obtained from human third molars and randomly divided into seven groups (n = 11): control, Whiteness Perfect--10% carbamide peroxide (10% CP), Colgate Platinum--10% CP, Day White 2Z--7.5% hydrogen peroxide (7.5% HP), Whiteness Super--3% CP, Opalescence Quick--35% CP and Whiteness HP--35% HP. Bleaching agents were applied according to manufacturers' instructions. The control group remained not treated and stored in artificial saliva. Microhardness testing was performed with a Knoop indentor and surface roughness was analyzed with a profilometer. Morphologic observations were carried out with scanning electron microscopy (SEM). Results were statistically analyzed by two-way analysis of variance and Tukey's test (5%), and revealed a significant decrease in microhardness values and a significant increase in surface roughness post-bleaching. Changes in enamel morphology after bleaching were observed under SEM. It was concluded that bleaching agents can alter the microhardness, roughness and morphology of dental enamel surface.

Carbamide Peroxide↗

PubMedDate not supplied

Influence of carbamide peroxide-based bleaching agents on the bond strength of resin-enamel/dentin interfaces.

In this bond strength study, a bleaching agent containing 10% carbamide peroxide was applied over composite-teeth bonded interfaces of two adhesive systems applied to enamel and dentin. Sixteen human third molars were used for bonding procedures. Single Bond (SB) and Clearfil SE Bond (CB) were applied to enamel and dentin according to the manufacturers' instructions. A resin composite cube-like structure was incrementally built on the bonded surfaces. The restored teeth were sectioned into 0.7 mm thick slices that were trimmed at enamel or dentin bonded interfaces to an hourglass shape with a cross-sectional area of approximately 0.5 mm2. Specimens were assigned to 8 groups (n = 10) according to the following factors under study: dental substrate (enamel and dentin); adhesive system (SB and CB) and treatment (10% carbamide peroxide and not bleached/control). The bleaching gel (Opalescence) was applied at the bonded interfaces for 6 hours during 14 days and after daily treatment specimens were stored in artificial saliva. Unbleached specimens were stored in artificial saliva for 14 days. Specimens were tested for tension and the data were analyzed by three-way ANOVA and Tukey's test (p < 0.05). Enamel tensile bond strength of CB was reduced after carbamide peroxide application. The bleaching treatment did not alter dentin bond strength of both adhesives. The results suggest that bleaching significantly affects bond strength of CB to enamel, but no influence on bond strength to dentin was noted for both adhesive systems.

Analysis of Variance↗

PubMedDate not supplied

Effect of peroxide-based bleaching agents on enamel ultimate tensile strength.

This study evaluated the effects of peroxide bleaching regimens on the ultimate tensile strength (UTS) of human enamel. A resin composite block was built-up on the bonded occlusal surface of 14 extracted, sound, erupted third molars to enable posterior preparation for the microtensile test. The bonded teeth were serially sectioned in a buccal-lingual direction into approximately 0.7-mm thick slices. Each slice was trimmed with a fine diamond bur to reduce the area of the buccal, internal slope of the cusps to a dumb-bell shape with a cross-sectional area of less than 1 mm2. The samples were randomly divided into seven groups (n = 10): unbleached control group and bleached groups treated with six bleaching regimens. The specimens were tested in tension at 0.5 mm/minute and the data were analyzed by ANOVA and Tukey test. Specimens from the control group presented 51.3 +/- 8.6 MPa, while the UTS of bleached enamel ranged from 22.0 +/- 5.6 to 36.3 +/- 9.1 MPa. All bleaching procedures significantly reduced enamel UTS (p < 0.05). Differences were also observed among treatments. The results suggested that bleaching regimens can significantly reduce enamel UTS.

Analysis of Variance↗