Semicrystalline thermoplastic elastomeric polyolefins: Advances through catalyst development and macromolecular design.

We report the design, synthesis, morphology, phase behavior, and mechanical properties of semicrystalline, polyolefin-based block copolymers. By using living, stereoselective insertion polymerization catalysts, syndiotactic polypropylene-block-poly(ethylene-co-propylene)-block-syndiotactic polypropylene and isotactic polypropylene-block-regioirregular polypropylene-block-isotactic polypropylene triblock copolymers were synthesized. The volume fraction and composition of the blocks, as well as the overall size of the macromolecules, were controlled by sequential synthesis of each block of the polymers. These triblock copolymers, with semicrystalline end-blocks and mid-segments with low glass-transition temperatures, show significant potential as thermoplastic elastomers. They have low Young's moduli, large strains at break, and better than 90% elastic recovery at strains of 100% or less. An isotactic polypropylene-block-regioirregular polypropylene-block-isotactic polypropylene-block-regioirregular polypropylene-block-isotactic polypropylene pentablock copolymer was synthesized that also shows exceptional elastomeric properties. Notably, microphase separation is not necessary in the semicrystalline isotactic polypropylenes to achieve good mechanical performance, unlike commercial styrenic thermoplastic elastomers.

Journal Article↗
PubMed2005

Polysaccharide-induced order-to-order transitions in lyotropic liquid crystals.

We report on the order-to-order transitions of lyotropic liquid crystals formed by self-assembled monogylcerides and water in the presence of polysaccharides of various molecular weights. The phase diagram of monoglyceride-water-polysaccharide systems, their morphology, and the topology of liquid crystalline structures were determined by combining optical cross-polarization, oscillatory shear rheometry, and small-angle X-ray scattering. The presence of hydrophilic mono-, oligo-, and polysaccharides in the water domains of liquid crystalline phases resulted in a general decrease of the cubic-to-hexagonal transition temperature. Provided that the sugar could fit within the water channels, the decrease was observed to be dependent on the polysaccharide concentration but independent of its molecular weight. For isotropic bicontinuous cubic phases, monomeric sugars such as glucose were reported to shrink the lattice parameter of the structure without inducing phase transitions. However, when a polymeric form of glucose was used, such as dextran, transitions from the gyroidal Ia3d cubic phase to double diamond Pn3m cubic phases were observed at well-defined molecular weights of polysaccharide. These results were interpreted in terms of size exclusions of polymer sugars by the water domains of the liquid crystal phases as well as the different topologies of water channels. Molecular dynamics simulations of polysaccharides in the water environment were performed to support these findings.

Crystallization↗
PubMed2004

Synthesis of block copolymer segments containing different ratios of ethylene and 5-norbornen-2-yl acetate.

Block copolymerization of ethylene with 5-norbornen-2-yl acetate (1) by the nickel catalyst system [N-(2,6-diisopropylphenyl)-2-(2,6-diisopropylphenylimino)propanamide]Ni(eta1-CH2Ph)(PMe3) (2) and Ni(COD)2 (bis(1,4-cyclooctadiene)nickel) (3) produces a variety of block copolymer structures that demonstrate microphase separation. Typical block copolymerizations were carried out in an autoclave charged with a solution of the catalyst mixture and 1 (0.15 M) in toluene. The autoclave was sealed and exposed to PC2H4 = 50 psi for a period of time (T1). A pressure jump to PC2H4 = 1100 psi was then applied and the reaction allowed to proceed for another predetermined interval (T2). Independent experiments were performed to isolate and examine the molecular weight and comonomer composition of the first block. Narrow molecular weight distributions and the increase of polymer molecular weight with increases in T1 or T2 are consistent with a product in which an initial block is formed at low ethylene pressures and quantitatively converted to a block copolymer by the jump to high pressure. Transmission electron microscopy confirms that the materials are microphase separated.