PubMed Health⌕ Search

Biomedical subjects

Vikrant N Urade

Publications and source records attributed to Vikrant N Urade.

2 recordsLinked to original sources

Simulation and interpretation of 2D diffraction patterns from self-assembled nanostructured films at arbitrary angles of incidence: from grazing incidence (above the critical angle) to transmission perpendicular to the substrate.

A method to calculate the location of all Bragg diffraction peaks from nanostructured thin films for arbitrary angles of incidence from just above the critical angle to transmission perpendicular to the film is reported. At grazing angles, the positions are calculated using the distorted wave Born approximation (DWBA), whereas for larger angles where the diffracted beams are transmitted though the substrate, the Born approximation (BA) is used. This method has been incorporated into simulation code (called NANOCELL) and may be used to overlay simulated spot patterns directly onto two-dimensional (2D) grazing angle of incidence small-angle X-ray scattering (GISAXS) patterns and 2D SAXS patterns. The GISAXS simulations are limited to the case where the angle of incidence is greater than the critical angle (alpha(i) > alpha(c)) and the diffraction occurs above the critical angle (alpha(f) > alpha(c)). For cases of surfactant self-assembled films, the limitations are not restrictive because, typically, the critical angle is around 0.2 degrees but the largest d spacings occur around 0.8 degrees 2theta. For these materials, one finds that the DWBA predicts that the spot positions from the transmitted main beam deviate only slightly from the BA and only for diffraction peaks close the critical angle. Additional diffraction peaks from the reflected main beam are observed in GISAXS geometry but are much less intense. Using these simulations, 2D spot patterns may be used to identify space group, identify the orientation, and quantitatively fit the lattice constants for SAXS data from any angle of incidence. Characteristic patterns for 2D GISAXS and 2D low-angle transmission SAXS patterns are generated for the most common thin film structures, and as a result, GISAXS and SAXS patterns that were previously difficult to interpret are now relatively straightforward. The simulation code (NANOCELL) is written in Mathematica and is available from the author upon request.

Journal Article↗

Synthesis of thermally stable highly ordered nanoporous tin oxide thin films with a 3D face-centered orthorhombic nanostructure.

Thin films of nanoporous tin oxide with a 3D face-centered orthorhombic nanostructure have been synthesized by self-assembly that is controlled by post-coating thermal treatment under controlled humidity. In contrast to the conventional evaporation-induced self-assembly (EISA), the films here have no ordered nanostructure after dip-coating. However, the initial coatings are formed under conditions that inhibit significant hydrolysis and condensation for extended periods. This allows the use of postsynthesis thermal vapor treatments to completely control the formation of the nanostructure. With EO106-PO70-EO106 (Pluronic F127) triblock copolymer as the template, highly ordered nanostructures were generated by exposing the disordered films to a stream of water vapor at elevated temperature, which rehydrates the films and allows the formation of the thermodynamically favored phase. Further exposure to water vapor drives the condensation reaction through the elimination of HCl. The X-ray diffraction pattern from the nanostructure was indexed in the space group Fmmm as determined by analysis of 2D small-angle X-ray scattering patterns at various angles of incidence. The nanostructure is then stabilized and made nanoporous by extended controlled thermal treatments. After self-assembly and template removal, the films are thermally stable up to 600 degrees C and retain an ordered, face-centered orthorhombic nanostructure.

Letter↗