PubMed1994

Power density and external temperature of laser-treated root canals.

The purpose of this study was to determine the power and time parameters for an argon laser that would result in the removal of pulpal tissue without excessively elevating the external temperature of the root. External temperatures were measured by attaching thermistors to the surfaces of the teeth at the cemento-enamel junction (CEJ) areas and at the root apices. Results indicate that a 1-W power setting with a pulse duration of 0.1 sec and a 1 sec interval between pulses produced a mean temperature rise of 0.89 +/- 0.27 degrees C at the cemento-enamel junction area and a mean temperature increase of 2.04 +/- 0.47 degrees C at the apex. A 2-W power setting with a 0.1 sec pulse duration and a 1 sec interval between pulses resulted in a mean temperature increase of 1.58 +/- 0.45 degrees C at the CEJ and a mean temperature rise of 2.59 +/- 0.20 degrees C at the apex. Based upon the results of this study, it was concluded that an argon laser operating at 1 or 2 W of power with a 0.1 sec pulse duration could be used to remove pulpal tissue without creating an excessive increase in the external temperature of the tooth.

Dentin↗
PubMed1991

Degree of composite resin polymerization with visible light and argon laser.

A study was conducted to compare the degree of resin polymerization achievable using conventional visible light techniques and argon lasing. High performance liquid chromatography was used to extract unpolymerized resin from microfilled and small particle composite resin samples following photoactivation with visible light and the argon laser. It was determined that a significantly greater degree of microfilled resin polymerization was achievable following argon lasing compared to exposure to conventional visible light techniques. Although the small particle composite resin samples were polymerized as well as, or slightly better, with the argon laser, the differences were found to be insignificant. As a result, the argon laser should be considered a potentially advantageous method of initiating the polymerization of dental composite resin restorations.

Argon↗
PubMed1989

Enhancement of physical properties of resin restorative materials by laser polymerization.

A study was conducted to compare the compressive strength, diametral tensile strength, transverse flexural strength, and flexural modulus of a microfilled and a small particle composite resin restorative material following argon laser and conventional visible light polymerization techniques. All physical properties examined in this study were enhanced by laser polymerization. The diametral tensile strength of both types of restorative materials was significantly greater following laser polymerization, as were the transverse flexural strength and the flexural modulus of the microfilled resin restorative material. Additionally, these results were obtained with a laser polymerization time that was one-fourth that used for visible light activation. It was concluded that the argon laser is a potentially advantageous means of initiating the polymerization of dental composite resin restorations.

Acrylic Resins↗