[FTIR spectroscopic studies of hydration effect on the molecular structure of polyether urethane].

The interaction between water molecules and the polar groups in linear polyether urethane was studied by FTIR and subtraction spectroscopy technique. Direct proofs of the combining of water molecule and carbonyl group were obtained. The reorganizations of the ether linkage, carbamate, and carbon-hydrogen chain after hydration were also observed. These results suggest that the FTIR and subtraction spectroscopy technique could be a useful tool to investigate the hydration mechanism of polymer materials.

English Abstract↗

PubMed2006

[Structural study on the transparency of cross-linked polyester polyurethane].

The polyurethane material with cross-linked structure was synthesized using half pre-polymerization method. IR, UV-Vis, TEM and XRD methods, and physical properties measurements indicate that different moulding temperatures influence the apparent transparence of polyurethane and abrasive performance, and the nature of these changes is related to the conditions of processand chemical reaction which lead to gradual micro-phase separation of the polyurethane molecules with different compositions, resulting in the domain-forming with the size of sub-micro-, micro- and even more than ten micro-meters. Such domains aggregate one another to form particles with different shapes and complicated structures. The increase in the amount and size of these heterogeneous particles, distributed in the medium of transparent polyurethane, is the main cause that brings on an opaque appearance of polyurethane.

English Abstract↗

PubMed2005

[The studies on YCl3/PEU system by rheology analysis and FTIR].

FTIR spectroscopy and rheology analysis were applied to study the YCl3/PEU system. It is apparent that modification with lanthanide complexes such as yttrium leads to a slight increase in viscosity of the polyether urethane solution. The authors conclude that this may be due to the interaction between the lanthanide ions and the polar group in urethane.A new band appears at 1650 cm(-1) in the infrared spectra of the YCl3/PEU system, which corresponds to the new carbonyl structure formed through the coordination with yttrium cations. The dynamic rheological behaviors of the solutions demonstrate the interaction furthermore. A higher molecular weight formed with the higher concentration of the lanthanide ions in this DMF solution. And this could be an effective method to characterize the structure of the polymer solutions.

English Abstract↗

PubMed2004

[The interaction between La and polyurethane system].

A series of polyether polyurethane (PU)-LaCl3 composites with different lanthanum contents were prepared. DSC results indicate that LaCl3 promotes phase transition behavior of the LaCl3/PU composites, which causes the endothermic peak at 11.58 degrees C to disappear. FTIR spectroscopy demonstrates that significant variation can be observed. The peak at 1633 cm(-1) attributed to carbonyl vibration and the peak at 3311 cm(-1) attributed to N-H stretching band moves to 1647 cm(-1) and 3355 cm(-1), respectively, when LaCl3 is introduced into the PU system. A new band (-200 cm(-1)) assigned to the La-O band was observed, and the far IR result provided a direct evidence of the coordination between La3+ ion and C=O group of PU system.

English Abstract↗