PubMed2006

[Structure and performance of calcium polyphosphate for bone tissue engineering].

Porous calcium polyphosphate (CPP) has shown promise of tissue engineered implant application because of the biocompatibility and biodegradation. CPP with different polymerization degree were prepared by controlling the calcining time, and its polymerization degree could be calculated by developed method in this paper. Different crystal types CPP were prepared by quenching from the melt and crystallization of amorphous CPP. From the in vitro degradation, carried out in Tris-HCl buffer, the degradation velocity of CPP was controllable. The weight loss of CPP with different polymerization degrees and crystal types were different. With the increasing of polymerization degree, the weight loss during the degradation was decreasing, contrarily the strength of CPP was increasing. The amorphous CPP could degrade completely in 17 days while gamma-CPP do completely in 25 days. The degradation velocity beta-CPP and alpha-CPP was slower than gamma-CPP and the weight loss was about 12% and 5% respectively. The results of this study indicate that CPP have potential applications for bone tissue engineering as inorganic polymeric biomaterials.

Absorbable Implants↗

PubMed2004

[Methods for the pre-treatment of biological tissues for vascular scaffold].

Today, the blood vessel substitutes are in large demand for coronary and peripheral bypass procedures, and the demand cannot be met by conventional sources. This problem will be solved by applying tissue-engineered blood vessel in clinics. The prefabrication of vascular scaffold will be involved in engineering a blood vessel substitute. Biological tissues are important biomaterials fabricating vascular scaffold which can offer better constructs for adhesion and growth of cells onto synthetic materials. Because of immediate degradation of biological tissues obtained from the abattoir, cadaver or patient and the presence of antigenicity in allogenic or xenogenic tissues, the fresh biological tissues can not directly be preserved and applied. The use and preservation of these natural biomaterials have typically required pre-treatment aimed at (1) reducing the antigenicity of the materials, (2) enhancing the resistance of the materials to enzymatic degradation, (3) stabilizing the structure of the tissues and maintaining their mechanical properties. Physical and chemical methods for the pre-treatment of biological tissues are available. The predominant chemical agents that have been investigated for the pre-treatment of biological tissues for vascular scaffold are glutaraldehyde, polyepoxy compound, carbodiimide, genipin and proanthocyanidin. Typical and particularly promising physical pre-treatment of biological tissues for vascular scaffold is dye-mediated photooxidation. The crosslinking mechanisms of all classes of pre-treatments and the effects of pre-treatments on antigenicity, biostability, mechanical properties, cytoxicity and calcification of treated tissues are described in this article. The advantages and disadvantages of all pre-treatments are also reviewed. The trend of pre-treatment of biological tissues is to investigate and exploit the naturally occurring crosslinking reagent with less cytoxicity. Meanwhile, dye-mediated photooxidation crosslink is also a promising pre-treatment which should be widely applied in vascular scaffold.

Biocompatible Materials↗

PubMed2004

[Synthesis and application of the polyacrylamide beads acting as LDL adsorbent's matrices].

This study in pursuit of the synthetic technologies and structure characterization of polyacrylamide-based matrices (PAM beads) for low density lipoprotein (LDL) adsorbent and their adsorbability for LDL was intended for an experimental evidence of developing advanced matrices for LDL adsorbent. PAM beads were synthesized by inverse suspension polymerization, and their structure characterization was characterized by SEM, image analyzer and small angle X-ray scattering. The tripeptide serine-aspartic-glutamic acid (SDE) was coupled on the PAM beads to prepare the LDL adsorbents whose adsorbability for LDL was determined in vitro. The results showed that the PAM beads with the average size diameter 142.1 microm and the average pore diameter 119.8 nm could act as the matrices in accordance with the requirement of adsorbent for LDL. When the amount of acrylamide and the crosslinking agent N,N'-methylene-bis(acrylamide) was fixed, the average pore diameter decreased with the increase of the crosslinking agent content. Although the nonspecific binding of PAM beads for LDL was low, they could selectively adsorb LDL after coupling the SDE on the PAM beads.

Acrylic Resins↗

PubMed2003

[Peptides used in lowering the level of LDL in plasma when treating familial hypercholesterolemia].

While introducing the indications of low-density lipoprotein (LDL) apheresis, LDL absorption systems were reviewed generally. As the key components for binding LDL, four kinds of ligands which are synthesized by different principles are: 1. Positively charged peptides designed according to state charge force between ligand and LDL; 2. Peptides designed according to structural characteristics of the binding site between LDL and its receptors; 3. Antibody of Lp (a) obtained by immunizing mammals with designed peptides with the characteristics of Lp (a); 4. Segments of LDL binding proteins (LBPs) synthesized with genetic engineering method based on the specific binding of LBPs to LDL. Requirements of matrices carrying these ligands are also considered. Finally, future developments in treatments of familial hypercholesterolemia by means of blood purification using synthesized peptides are overlooked.

Adsorption↗