Surface preparation for orthodontic bonding to porcelain.

This study evaluated the effect of various porcelain surface treatments on the tensile strength of orthodontic brackets bonded to a feldspathic metal ceramic porcelain. The porcelain was fused to flat gold alloy tabs and divided into six groups that were subjected to sandblasting, silane application, intermediate resin, or etchants (9.6% hydrofluoric acid or 4% APF gels). Two brackets were bonded onto each porcelain/metal tab (n=60) with Bis-GMA resin (Concise, 3M Corp., St. Paul, Minn.) or 4-META resin (MCP-bond, Sun Medical Co. Ltd., Tokyo, Japan). The samples were stored in 37 degrees C water, thermocycled 1000 times from 5 degrees C to 55 degrees C and tested in tension. Alignment and uniform loading during testing were secured by engaging a hook in a circular ring soldered onto the bracket slot before bonding. Similar control brackets (n=12) were bonded with Concise to extracted caries-free mandibular incisors. Bond failure sites were classified according to a modified Adhesive Remnant Index (ARI) system. Silane application to the sandblasted porcelain surface significantly increased the bond strengths according to analysis of variance and Duncan's multiple range test. The quality of the bonds was further enhanced by the addition of the intermediate resin. Etching the porcelain with 9.6% hydrofluoric acid provided similar bond strengths, but the 4% APF gel was less effective. The MCP-bond was not significantly better than Concise in bond strength to sandblasted porcelain. Several difficulties associated with the clinical interpretation of laboratory data on bonding to dental porcelains are discussed, and clinical trials are necessary for final evidence of efficacy.

Acid Etching, Dental↗

PubMed1995

Improving orthodontic bonding to gold alloy.

Flat tabs of cast gold alloy (n = 156) were subjected to either of three surface treatments: (1) roughening with diamond bur, (2) aluminum oxide sandblasting, and (3) sandblasting plus tin electroplating. Mandibular incisor edgewise brackets were bonded with Concise (BIS-GMA resin) (Unitek, Monrovia, Calif.) or Superbond C&B (4-META metal bonding resin) (Sun Medical Co. Ltd., Kyoto, Japan), or with Concise after application of an intermediate resin. All-Bond 2 Primers A and B (Bisco Dental Products, Itasca, Ill.), or B alone. All specimens were stored in water at 37 degrees C for 24 hours, and 60 were then thermocycled 1,000 times from 5 degrees C to 55 degrees C and back. The tensile bond strength testing was performed in a Lloyd 1,000R machine (Fareham, Hants, England). Alignment and uniform loading during testing were secured by engaging a hook in a circular ring soldered onto the bracket slot before bonding. Similar control brackets (n = 24) were bonded with Concise to extracted human premolars and lower incisors according to a routine procedure. Bond failure sites were classified by a modified ARI system. The results showed that sandblasting produced significantly stronger bonds to gold alloy than roughening with diamond bur. Superbond C&B provided significantly stronger bonds to gold alloy than Concise. There were generally insignificant differences in bond strengths between the water stored and the thermocycled specimens. Bond failures of Concise to sandblasted plus tin-plated gold alloy invariably occurred at the gold/adhesive interface, whereas those of Superbond C&B occurred within the adhesive or in the adhesive/bracket interface.(ABSTRACT TRUNCATED AT 250 WORDS)

Analysis of Variance↗

PubMed1995

Improving orthodontic bonding to silver amalgam.

Flat rectangular tabs (n = 84) prepared from lathe-cut amalgam (ANA 2000) were subjected to aluminum oxide sandblasting or roughening with a diamond bur. Mandibular incisor edgewise brackets were bonded to these tabs using: Concise (Bis-GMA resin); one of three metal-bonding adhesives, viz., Superbond C&B (4-META resin), Panavia Ex (10-MDP Bis-GMA resin) or Geristore (composite base); and Concise after application of the intermediate resins All-Bond 2 Primers A+B, or the Scotch-Bond Multi-Purpose (SBMP) system. All specimens were stored in water at 37 degrees C for 24 hours before tensile bond strength testing. Alignment and uniform loading during testing were secured by engaging a hook in a circular ring soldered onto the bracket slot before bonding. Similar control brackets (n = 12) were bonded with Concise to extracted caries-free mandibular incisors. Bond failure sites were classified by a modified ARI system. Mean tensile bond strengths in the experimental group ranged from 3.4 to 6.4 MPa--significantly weaker than the control sample (13.2 MPa). Bond failure generally occurred at the amalgam/adhesive interface. Superbond C&B created the strongest bonds to amalgam; according to ANOVA and Duncan's Multiple-Range test, they were significantly stronger than the bonds with Panavia Ex and Concise, with Geristore in between. However, the bond strength of Concise to sandblasted amalgam was comparable to the Superbond C&B bonds when coupled with an intermediate application of All-Bond 2 Primers A+B. The SBMP, on the other hand, was less effective.(ABSTRACT TRUNCATED AT 250 WORDS)

Aluminum Oxide↗

PubMed1988

Bacterial agglutinins in rat salivary glands: effect of glandular stimulation and calcium dependency.

The secretory pattern of salivary, bacterial agglutinins was studied in the rat. The three major salivary glands were cannulated bilaterally and their secretions collected separately after parasympathomimetic and sympathetic stimulation. The bacterial aggregating activity of the secretions was tested against four strains of bacteria indigenous to the rat. Agglutinin activity was demonstrated in both parasympathomimetic and sympathetic secretions. The parotid glands tended to show the highest total output of agglutinins, with the highest titers found in parotid saliva on sympathetic stimulation. In submandibular and, particularly, parotid saliva, titers tended to increase when stimulation with pilocarpine was followed by sympathetic stimulation. In contrast, titer in sublingual saliva tended to decrease on sympathetic stimulation. When expressed as titer output per minute, sympathetic parotid secretion showed the highest agglutinin activity. Agglutinin activity appeared unrelated to total protein or to duct-derived amidolytic activity. Titers of parotid or submandibular saliva were increased 5- to 10-fold by the presence of 3.3 mM CaCl2 in the reaction mixture. By contrast, the agglutinating activity of sublingual saliva on parasympathomimetic stimulation was unaffected by extraneous CaCl2. Measurements of Ca concentration in similarly obtained rat salivary secretions did not show patterns of Ca concentration that could be related to the varying sensitivity of the agglutinating activity to Ca.