Stress response of adherent cells on a polymer blend surface composed of a segmented polyurethane and MPC copolymers.

To better understand the effect of 2-methacryloyloxyethyl phosphorylcholine (MPC) copolymer in improving the biocompatibility of segmented polyurethane (SPU), the expression of heat shock protein (HSP) mRNA in HeLa S3 cells adhered on SPU blended with MPC copolymers was measured. Conventionally, MPC copolymers (PMEH) were synthesized by changing the feed ratios of MPC and 2-ethylhexyl methacrylate. X-ray photoelectron spectroscopic analysis of the SPU/PMEH film indicated that the surface concentration of MPC units on the SPU/PMEH film increased with an increase in PMEH composition. HeLa S3 cells were cultured on SPU/PMEH films. The number of adherent cells on the SPU/PMEH films decreased with an increase in the concentration of PMEH. When the PMEH composition was greater than 0.5 wt %, cell adhesion and proliferation decreased markedly. Expressions of HSP27 and HSP47 mRNA were detected using the reverse transcription-polymerase chain reaction (RT-PCR). After incubation for 24 h, both the HSP mRNA expressions in the HeLa S3 cells showed no significant differences among all samples. In HeLa S3 cells that adhered to the SPU film for 48 h, the expressions of HSP27 and HSP47 mRNA increased significantly when compared with those incubated for 24 h. In contrast, the two kinds of mRNA expressions decreased in the HeLa S3 cells that adhered to the SPU/PMEH films for 48 h. From these results, we concluded that PMEH was quite important in suppressing the stress response of adherent HeLa S3 cells. Therefore, SPU/PMEH blend polymers are useful as implantable biomedical materials.

Adsorption↗
PubMed2006

Enzyme-degradable phosphorylcholine porous hydrogels cross-linked with polyphosphoesters for cell matrices.

Biodegradable highly porous hydrogels composed of poly [2-methacryloyloxyethyl phosphorylcholine (MPC)] cross-linked with polyphosphoesters have been prepared as novel cellular matrices. Well-controlled porous hydrogels were fabricated by using potassium hydrogen carbonate as a porogen salt for forming gas. This process enabled the homogeneous expansion of pores within the polymer hydrogel matrices, leading to well-interconnected high porosity. The mechanical properties of the hydrogels were influenced by the cross-linking density and porous structure. Hydrolysis and enzymatic digestion of the hydrogels were determined under basic conditions. The cross-linking density and porosity influenced the rate of degradation of the hydrogels. Acceleration of the degradation with alkaline phosphatase was also observed. Cultivation of mouse osteoblastic cell (MC3T3-E1) was performed in the highly porous hydrogels and cell viability was well maintained. The rate of cell proliferation also was relatively increased with an increase in the amount of polyphosphoesters in the hydrogel. Basic fibroblast growth factor (bFGF) was physically absorbed by the hydrogels and effectively induced cell proliferation. In conclusion, the porous hydrogels prepared in this study contributed a suitable environment for three-dimensional cell cultivation and may be useful for cell and tissue matrices.

3T3 Cells↗
PubMed2006

A flexible and wearable glucose sensor based on functional polymers with soft-MEMS techniques.

A novel biosensor for glucose measurement using functional polymers was fabricated and tested. The biosensor utilizes the physical and chemical functions of hydrophobic polydimethyl siloxane (PDMS) and hydrophilic 2-methacryloyloxyethyl phosphorylcholine (MPC) copolymerized with dodecyl methacrylate (DMA). The glucose sensor was constructed by immobilizing glucose oxidase (GOD) onto a flexible hydrogen peroxide electrode (Pt working electrode and Ag/AgCl counter/reference electrode). The electrodes were fabricated using microelectromechanical systems (MEMS) techniques onto those functional polymers. The sensor showed novel functions of flexibility and it was stretchable so that the sensor could normally work when it was released after expanding to 120% longer than that of normal length. Also, basic characteristics of the sensor were evaluated. The output current of the hydrogen peroxide electrode was linearly related to the hydrogen peroxide concentration in a range of 0.20-2.50 mmol/l, with a correlation coefficient of 0.998. GOD was then immobilized onto the surface of the sensor using MPC polymer. In this case, the current output of the glucose sensor related to the glucose level over a range of 0.06-2.00 mmol/l, with a correlation coefficient of 0.997. The calibration range includes the reported concentration of tear glucose in normal human subject (0.14 mmol/l).

Blood Glucose Self-Monitoring↗
PubMed2006

Dual mode bioreactions on polymer nanoparticles covered with phosphorylcholine group.

We investigated the preparation of polymer nanoparticles covered with phosphorylcholine (PC) groups and the immobilization of proteins in order to observe dual mode bioreactions on the nanoparticles. For the surface modification on the nanoparticles, a water-soluble amphiphilic phospholipid polymer with PC groups as a hydrophilic moiety was synthesized. In this polymer, an active ester group, which can immobilize proteins, was introduced. Using the phospholipid polymer as a solubilizer, poly(L-lactic acid) nanoparticles were prepared from its methylene chloride solution in an aqueous medium by the solvent evaporation method. The diameter of the nanoparticles was ca. 200 nm and the surface was covered with the PC groups and active ester groups. Proteins could immobilize on the nanoparticles under mild conditions by the reaction between the active ester group and amino group in the proteins. Both an antibody and enzyme were immobilized on the nanoparticles and bioreactions such as the antigen/antibody reaction and enzymatic reaction were observed. When an antigen was added to the suspension of the nanoparticles, aggregation of the nanoparticles occurred and then they precipitated. Also, the enzymatic reaction proceeded well when the enzyme substrate was added to the suspension. Based on these results, we provided polymer nanoparticles functionalized with both the antibody and enzyme, and the dual mode bioreactions could occur. We concluded that the novel polymer nanoparticles could be used for nano-/micro-scaled diagnostic and medical treatment systems.

Antibodies, Monoclonal↗
PubMed2006

Synthesis and characterization of amphiphilic polyphosphates with hydrophilic graft chains and cholesteryl groups as nanocarriers.

Amphiphilic polyphosphate graft copolymers with varied densities of cholesteryl esters and hydrophilic graft chains were prepared, and the solution properties of the graft copolymers were evaluated. Polyphosphates were synthesized as backbones by ring-opening polymerization of 2-isopropyl-2-oxo-1,3,2-dioxaphospholane (IPP), 2-(2-oxo-1,3,2-dioxaphosphoroyloxyethyl-2-bromoisobutyrate) (OPBB), and 2-choresteryl-2-oxo-1,3,2-dioxaphospholane (ChOP) using triisobutylaluminum as an initiator. Three types of polyphosphates (PIBr(x)Ch(y), x = number of OPBB units in a polymer; y = number of ChOP units in a polymer) such as PIBr4, PIBr6Ch1, and PIBr3Ch2 were obtained. The molecular weights of these polymers were 2.4 x 10(4), 2.4 x 10(4), and 2.6 x 10(4) g/mol, respectively. 2-Methacryloyloxyethyl phosphorylcholine (MPC) was grafted from the OPBB sites in PIBr(x)Ch(y) via atom transfer radical polymerization (ATRP) in EtOH. In each polymer system, the molecular weight of the graft polymer was linear with conversion. Furthermore, the polymer radical concentration remained constant during polymerization; that is, the molecular weights of the graft chains were easily controllable with polymerization time. The solution properties of amphiphilic PIBr(x)Ch(y)-g-PMPCs were investigated by the methods of surface tension measurement, light scattering, and fluorescence probe. The transition point (cmc) of the surface tension of the PIBr(x)Ch(y)-g-PMPCs aqueous solution decreased with an increase in the number of ChOP units in a graft polymer. Particularly, PIBr3Ch2-g-PMPC14.9K formed nanosized associates (R(h) = 7.5 nm) with 2.2 molecules above 0.1 wt %. v79 cells were used to evaluate the cytotoxicity of the graft polymers, but no cytotoxicity was observed. The graft polymers containing cholesteryl groups effectively enhanced the solubility of paclitaxel in an aqueous solution.

Biopolymers↗
PubMed2006

Platelet separation from whole blood in an aqueous two-phase system with water-soluble polymers.

Platelet-rich plasma (PRP) stimulates tissue healing and centrifugation is the only method for PRP preparation. The purpose of the present study was to develop a method to separate platelets without centrifugation. We used 16 polymers of different chemical characteristics and mixed each polymer with fresh whole blood containing anticoagulant citrate-dextrose. Then, we observed blood cell separation. Focusing on the effective polymers and comparing our method with the conventional centrifugation method, we examined platelet recovery rate and P-selectin expression, which represents platelet activation. Poly-L-glutamic acid (PGA) and poly-L-aspartic acid (PAA) separated platelets efficiently; however, these polymers activated platelets. On the contrary, poly (2-methacryloyloxyethyl phosphorylcholine-co-n-butyl methacrylate) (PMB), which has phosphorylcholine residues mimicking a cellular membrane molecule, separated platelets moderately and the PMB-separated platelets were nearly inactive compared to the separation with the ordinary centrifugation and PGA. Conclusively, the present experiments demonstrated that without centrifugation platelets can be separated from whole blood with some water-soluble polymers, such as PGA, PAA, and PMB, and that PMB has an advantage not to activate platelets.

Biopolymers↗
PubMed2005

High functional hollow fiber membrane modified with phospholipid polymers for a liver assist bioreactor.

For practical application of a liver assist system with a tissue-conjugated hollow fiber membrane (HFM) bioreactor used in an extracorporeal therapy, it would require a highly sophisticated HFM which has both hemocompatibility on one side and cytocompatibility on the other side. In this study, we present a cellulose acetate (CA) HFM modified with 2-methacryloyloxyethyl phosphorylcholine (MPC) copolymers (PMB30 (MPC-co-n-butyl methacrylate) and PMA30 (MPC-co-methacrylic acid) for preparing a novel liver assist HFM bioreactor. A CA/PMB-PMA30 HFM modified asymmetrically on the inner and outer surface with the PMB30 and PMA30 was prepared successfully. Analysis with an X-ray photoelectron spectroscope showed that the intensity of the phosphorus atom attributed to the MPC units on the outer surface of the modified HFM was stronger than that of the inner surface. The PMA30 was immobilized on the outer surface of the CA/PMB30 blend HFM by a chemical condensation reaction. The CA/PMB-PMA30 HFM showed good water and solute permeability in comparison with the CA HFM. The morphologies of the adherent hepatocytes were round in shape in comparison with the cells that adhered on CA HFM. Furthermore, hepatocytes cultured on the inner surface of the CA/PMB-PMA30 HFM showed higher functional expression in terms of urea synthesis and albumin synthesis than that of the CA HFM.

Animals↗
PubMed2005

Hybrid nanogels with physical and chemical cross-linking structures as nanocarriers.

Polymerizable nanogels were prepared by self-assembly of cholesteryl group-bearing pullulan (CHP) with methacryloyl groups (CHPMA). The CHPMA nanogel was polymerized with 2-methacryloyloxyethyl phosphorylcholine (MPC) by radical polymerization in dilute aqueous solution. The solution properties of the polymers in water were investigated by TEM, SEC-MALS, and fluorescence quenching technique. Monodispersed hybrid nanogels of CHPMA-MPC (CM nanogels) (25-30 nm in radius of gyration) were obtained by using CHPMA nanogel as a seed-nanogel. CM nanogels have a dual cross-linking structure that is physically cross-linked with the cholesteryl groups and chemically cross-linked with the MPC polymer chains. CM nanogels trap heat-denatured carbonic anhydrase B (CAB) and prevent their aggregations. The nanogels maintained the ability of trapping and releasing enzymes by host-guest interaction of cholesteryl group and cyclodextrin.

Cholesterol↗
PubMed2005

Phospholipid polymer surfaces reduce bacteria and leukocyte adhesion under dynamic flow conditions.

Persistence of infection can occur when the host immune response is compromised because of the presence of a foreign implant. Surface modification of biomaterials with phospholipid polymers may enhance biocompatibility and reduce incidence of infection by impeding bacterial and leukocyte adhesion. A rotating disk model, which generates shear stress from 0 to 18 dynes/cm(2), was used to characterize adhesion of neutrophils, monocytes, and bacteria in phosphate-buffered saline (PBS) or 25% human serum on polyethylene terephthalate surfaces coated with a phospholipid polymer, poly[omega-methacryloyloxyalkyl phosphorylcholine (MAPC)-co-n-butyl methacrylate (BMA)]. The material designated PMB30 contains a methylene chain length, (CH(2))(n), of n = 2, whereas PMHB30 contains a chain length of n = 6. In PBS, bacterial adhesion was shear stress dependent with the lowest bacterial density observed on PMB30. However, the presence of serum proteins eliminated shear stress and surface chemistry effects in addition to bacterial adhesion reduced to <10% of adhesion in PBS. Trends for leukocyte adhesion in serum demonstrated shear dependence with PMB30 exhibiting the lowest cell density throughout the range of shear stresses. In conclusion, modification of the polyethylene terephthalate surfaces with phospholipid polymers resulted in reduced bacterial and leukocyte adhesion. Furthermore, shortening the methylene chain length of the MAPC copolymer most effectively reduced adhesion.

Bacterial Adhesion↗
PubMed2005

Cell separation in microcanal coated with electrically charged phospholipid polymers.

To separate the cell population in whole blood using microcanal, the surface was covered with a polyion complex (PIC) composed of electrically charged phospholipid polymers. The phospholipids polymers were prepared by the polymerization of 2-methacryloyloxyethyl phosphorylcholine (MPC) and n-butyl methacrylate with 3-(methacryloyloxypropyl)-trimethyl ammonium iodide as the cationic unit or potassium 3-methacryloyloxypropyl sulfonate as the anionic unit. The PIC was formed at the solid-liquid interface, that is, first, the cationic polymer was coated on the substrate and an aqueous solution containing the anionic polymer with different concentrations was applied to the polymer-coated substrate. The formation of the PIC was followed using a quartz crystal microbalance (QCM), and the PIC surfaces were analyzed by both zeta-potential measurement and X-ray photoelectron spectroscopic measurement. The surface electrical potential on the PIC was controllable from +40 to -40 mV by increasing the amount of the adsorbed anionic polymer. The PIC surface was prepared in microcanal. The surface electrical potential was sequentially changed. When the whole blood was introduced into the microcanal, the cells adhered on the positively charged surface, but could not adhere to the negatively charged surface. Even when the cells adhere to the surface, the morphology of cells was maintained. This is due to MPC units at the surface, which show a good biocompatibility. These results indicated that the change in the surface electrical potential will be a useful method to separate the cells from whole blood.

Blood↗
PubMed2005

Segmented polyurethane modified by photopolymerization and cross-linking with 2-methacryloyloxyethyl phosphorylcholine polymer for blood-contacting surfaces of ventricular assist devices.

To improve the biocompatibility of pulsatile ventricular assist devices (VADs), the blood-contacting surface of the segmented polyurethane (SPU) diaphragm employed in an electromechanical VAD was modified by introducing 2-methacryloyloxyethyl phosphorylcholine (MPC) units into its surface and forming an interpenetrating polymer network (IPN) structure, which contained independently cross-linked MPC polymer and SPU. The SPU diaphragm modified with an IPN structure was then assembled into a target test pump and underwent continuous pump operation at 37 degrees C for 2 weeks in a simulated systemic circulation using a mock circulatory loop. The surface characteristics of the pump diaphragm after 2 weeks of pump operation were then analyzed with an X-ray photoelectron spectroscope (XPS) and gold-colloid-labeled immunoassay. The XPS surface analysis of the IPN-modified SPU indicated the firm anchoring of MPC units even after 2 weeks of pump operation (the phosphor : carbon ratio was reduced by only 0.09%). The IPN-modified diaphragm prevented protein adsorption as well as cell adhesion in comparison to the unmodified SPU surface. This result thus validated that (1) the IPN structure could firmly secure MPC units to the SPU surface even in a high-mechanical-stress and high-shear environment, (2) the antithrombogenic power of MPC units remained unchanged after 2 weeks of continuous exposure to a high-shear environment, and (3) the IPN modified SPU cross-linked with MPC could be a powerful antithrombogenic surface for blood pumps used for chronic circulatory support of cardiac patients.

Biocompatible Materials↗
PubMed2005

Design of functional hollow fiber membranes modified with phospholipid polymers for application in total hemopurification system.

In this study, we prepared cellulose acetate (CA) hollow fiber membranes (HFMs) modified with poly (2-methacryloyloxyethyl phosphorylcholine (MPC)-co-n-butyl methacrylate)(PMB30 and PMB80) by the dry-jet wet spinning process. The physical and chemical structures of the HFMs were controlled in order to design highly functional HFMs that had suitable performance to each targeting HFM device used in a total hemopurification system. The CA HFMs modified with the MPC polymer, such as CA/PMB30, CA/PMB80, and CA/PMB30-80 HFMs, were successfully prepared by controlling the spinning conditions. The modified HFMs showed an improved performance in solute and water permeability, due to the modification by the hydrophilic MPC polymers. The CA/PMB30 and CA/PMB80 showed a high potential in an application for a high performance hemocompatible plasmapheresis and hemofilter device. Furthermore, CA/PMB30-80 HFM, modified asymmetrically with PMB30 and PMB80, showed a potential for application in an advanced total hemopurification system as a highly functional scaffold for a biohybrid renal tubule, or a liver assist bioreactor device, because of their enhanced permeability, hemocompatibility, and cytocompatibility.

Animals↗
PubMed2005

Evaluation of 2-methacryloyloxyethyl phosphorylcholine (MPC) polymer-coated dressing on surgical wounds.

The ideal dressing material is bio-inert and keeps the wound site moist. It is equally important that no regenerative tissue is peeled off on the removal of the dressing. 2-Methacryloyloxyethyl phosphorylcholine (MPC) has a phospholipid polar group that mimics a biomembrane. We prepared poly [MPC-co-n-dodecyl methacrylate (DMA)] (PMD), using conventional radical polymerization with 2,2'-azobisisobutyronitrile as an initiator, and coated it on polyurethane (PU; Tecoflex 60 Thermedics Inc.) membrane. Full-thickness surgical wounds were made on the dorsal skin of rats and wound healing was compared under the following three conditions: air-exposed control (no dressing), PU dressing, and PMD dressing. At 3, 4 and 7 days after the operation, the wound sizes of the PMD dressings were smaller than the non-dressed wound, and at 6 and 7 days after the operation, the wound sizes of PU dressing were smaller than that of the air-exposed group. But there were no significant difference between the PMD dressing group and PU dressing group. Histologically, scab formation was not observed on the PU or PMD-dressed wounds. However, in the air-exposed control, a scab was formed and re-epithelialization of the wound site was prevented. Additionally, no damage was observed in the histological section of PMD dressed wound after the wound was cured. These results indicate that PMD dressing (PMD-coated PU membrane) has the potential to provide an inert environment for wound healing as well as PU.

Animals↗
PubMed2004

Improved wet bonding of methyl methacrylate-tri-n-butylborane resin to dentin etched with ten percent phosphoric acid in the presence of ferric ions.

The objective of this study was to determine the influence of dissolved dentinal substances in demineralized dentin on the hybridization of resin for bonding to dentin. It was hypothesized that these substances, including polyelectrolytes, significantly change the substrates, which could then be assessed by the addition of Na(+), Ca(2+), or Fe(3+) in 10% phosphoric acid. Bovine dentin specimens were etched for 10 s with a solution of 10% phosphoric acid (control) or of 22.0 mM dissolved sodium chloride (10P-Na), calcium chloride (10P-Ca), or ferric chloride (10P-Fe). The specimens were then rinsed, blot-dried, and primed three times with 5% 4-methacryloyloxyethyl trimellitate anhydride in acetone for 60 s. Methyl methacrylate-tri-n-butylborane resin was then applied. The tensile bond strength of each of the dumbbell-shaped specimens was then measured. The fractured surfaces and modified cross-sections were examined by scanning electron microscopy. The cross-sections were soaked in 6N HCl for 10 s and then in 1% sodium hypochlorite for 30 min to determine the resin content in the hybridized specimens. Shrinkage of the demineralized dentins upon drying was assessed by atomic force microscopy. The tensile bond strengths were 10.8 +/- 4.5 (control), 15.0 +/- 7.0 (10P-Na), 19.3 +/- 5.5 (10P-Ca), and 27.8 +/- 8.1 (10P-Fe) MPa. The atomic force microscopy studies showed that Fe(3+) minimized the shrinkage by drying for 10 s but Ca(2+) and Na(+) did not decrease the shrinkage the same as the control. The results support the hypothesis that the monomer permeability of wet demineralized dentin is effectively improved by dissolving ferric ions in the phosphoric acid, resulting in a greater bond strength and higher resin content in the hybridized dentin. The dissolved dentinal substances, including the polyelectrolytes, had a significant influence on the characteristics of the demineralized dentin, changing the degree of hybridization and bonding.

Animals↗
PubMed2004

Nano-scale surface modification of a segmented polyurethane with a phospholipid polymer.

Nano-scale modification of a segmented polyurethane (SPU) with cross-linked 2-methacryloyloxyethyl phosphorylcholine (MPC) polymer was performed to obtain a biocompatible elastomer. To control the domain size and the depth of the modified layer, various compositions of monomers, including MPC, 2-ethylhexyl methacrylate (EHMA), and glycerol 1,3-diglycerolate diacrylate, were examined. SPU film was immersed in the monomer solution and visible light irradiation was applied to initiate polymerization to the SPU film that was held by mica to condense MPC units at the surface. The surfaces of the obtained film were analyzed by X-ray photoelectron spectroscopy and water contact angle measurement. The surface density of MPC units changed with the monomer concentration, and the density was the highest when the ratio between MPC and EHMA was 7:3. In modified SPU films, 6- to 25-nm MPC unit-enriched domains were observed and the density of these domains gradually decreased with depth. The sizes of the domains depended on the MPC composition in the monomer solution. The mechanical properties of the modified films as evaluated by tensile strength measurement under wet conditions were not significantly different from those of SPU. With increase in the existence of MPC unit-enriched domains on the MEG film surface, platelet adhesion and activation were remarkably reduced compared to the SPU film. This nano-scale surface modification may be a useful technique for applying elastic polymer biomaterials.

Biocompatible Materials↗
PubMed2004

Effect of remaining demineralised dentine on dental microleakage accessed by a dye penetration: how to inhibit microleakage?

OBJECTIVES: To demonstrate that microleakage has taken place at the defect, which was analysed previously by a tensile test using dumbbell shaped specimens trimmed from bonded resin/dentine restorations, and to suggest how microleakage can be inhibited reliably in dental treatment. METHODS: A total of 60 Class V box cavities were prepared at the cemento-enamel junction on fresh bovine incisors and randomly divided into four groups of 15 specimens each. Exposure times of etching for 10:3 conditioner were set at 10, 30 or 60 s, and for 10% phosphoric acid (positive control) at 10 s. The cavity walls were rinsed with water for 10 s, air-dried for 10 s and hybridised with 4-META/MMA-TBB resin. All the cavities were filled with a light cured resin composite and stored in 37 degrees C water for 24 h and then immersed in 15% methylene blue for 2 h. The length of dye penetration along the interface was graded by defined criteria and analysed using Kruskal-Wallis and Mann-Whitney tests. The dye penetration patterns were examined by light microscopy and the remaining demineralised dentine was analysed by Transmission Electron Microscopy (TEM). RESULTS: The least leakage score was obtained in 10s-10:3 etched group with 12 out of 15 specimens demonstrating no leakage. Leakage was significantly lower at the cementum margin than for the other three groups. No significant difference in the extent of greatest dye penetration was found between the 60s-10:3 and 10s-phosphoric etched groups. Dye penetration along the cementum margins was significantly higher than that of the enamel margins in all groups, except the 10s-10:3 etched group. TEM examination confirmed that there were exposed collagen fibrils in the remaining demineralised dentine, where microleakage had taken place. SIGNIFICANCE: It could be concluded from this study that microleakage has taken place at the defect in the bonded specimens which has correlations with zones of incompletely infiltrated demineralised dentine that was observed using TEM. A reliable method of inhibiting microleakage is the presence of well prepared hybridised dentine.

Acid Etching, Dental↗
PubMed2004

Polyethylene/phospholipid polymer alloy as an alternative to poly(vinylchloride)-based materials.

To develop new biomaterials for making medical devices, polymer alloys composed of a phospholipid polymer, poly(2-methacryloyloxyethyl phosphorylcholine) (PMPC), and polyethylene (PE) were prepared. The PE/PMPC alloy membrane could be obtained by a combination of solution mixing and solvent evaporation methods using xylene and n-butanol mixture as a solvent. Moreover, thermal treatment was applied to improve the mechanical properties of the PE/PMPC alloy membrane. In the PE/PMPC alloy membrane, the PMPC domains were located not only inside the membrane but also at the surface. Surface analysis of the PE/PMPC alloy membrane with X-ray photoelectron spectroscopy, wettability evaluation, and dynamic contact angle measurements revealed that the phospholipid polar groups in the PMPC covered the surface even after thermal treatment. Blood compatibility tests with attention to platelet adhesion and change in morphology of adhered platelets showed that the PE/PMPC alloy membrane had excellent platelet adhesion resistance. We finally concluded that the PE/PMPC alloy could be used as biomaterials instead of poly(vinyl chloride)-based materials.

Alloys↗