Formation of orientation-ordered superlattices of magnetite magnetic nanocrystals from shape-segregated self-assemblies.

Magnetic magnetite (Fe3O4) nanocrystals have been synthesized by combining nonhydrolytic reaction with seed-mediated growth. The shape of these magnetite nanocrystals can be controlled either as pure spheres or a mixture of mainly faceted nanocrystals. Faceted magnetite nanocrystals consist of truncated tetrahedral platelets (TTPs), truncated octahedrons (TOs), and octahedrons (OTs). Transmission electron microscopy analysis indicates that the faceted nanocrystal mixture tends to self-segregate based upon the shape in a self-assembly process, and each shape forms its own distinct crystallographic orientation-ordered superlattice assemblies. Self-assemblies of the Fe3O4 nanocrystals in the shapes of TTP, TO, and OT show hexagonal, primitive cubic, and distorted body-centered cubic (bcc) superlattice structures, respectively. The possible mechanism for the formation of different superstructures is attributed to van der Waals interactions. Nanocrystals with different shapes provide diverse building blocks for bottom-up approaches in building nano- and mesosystems. Furthermore, the self-segregation phenomenon of different shaped nanocrystals in self-assembly processes could be very important in envisioning efficient assembly strategies for nanoscience- and nanotechnology-based devices.

Crystallization↗
PubMed2006

Activation of RAGE induces elevated O2- generation by mononuclear phagocytes in diabetes.

Oxidative stress has been found to play a role in the pathogenesis of diabetic complications. The aim of this study was to define the oxidative burst of diabetic monocytes to characterize the phenotype associated with poor diabetic control. Superoxide (O(2)(-)) is the first molecule generated during the respiratory burst of phagocytes by NADPH oxidase, and its generation by monocytes from 26 controls and 34 diabetic subjects was evaluated in this study. Under resting states or stimulation by PMA or opsonized zymosan, diabetic monocytes produce significantly more O(2)(-) than nondiabetic cells. The increased O(2)(-) generation was found to be correlated with glycemic control (glycated hemoglobin) of patients. To clarify the effects of hyperglycemia on O(2)(-) generation, normal human monocytes were treated with receptor for advanced glycation endproducts (RAGE) ligands (AGE protein and S100B) or high glucose media before stimulation. RAGE ligands and high glucose concentration increased O(2)(-) generation from human mononuclear phagocytes. RAGE ligands, specifically and potently, increased O(2)(-) generation from mononuclear phagocytes, and high-glucose effects were associated with correspondingly increased osmotic pressure. Differentiated THP-1 cells, from a human monocytic cell line, were used as a model of human monocytes to study the effects of S100B, the RAGE ligand. It was confirmed that RAGE is involved in the priming of O(2)(-) generation by S100B. This study demonstrates that RAGE ligands can contribute significantly to the hyper-responsive phenotype of diabetic monocytes, which might be reversible by blocking the RAGE or controlling the presence of RAGE ligands by controlling hyperglycemia.

Adult↗
PubMed2006

PLD-assisted VLS growth of aligned ferrite nanorods, nanowires, and nanobelts-synthesis, and properties.

We report here a systematic synthesis and characterization of aligned alpha-Fe2O3 (hematite), epsilon-Fe2O3, and Fe3O4 (magnetite) nanorods, nanobelts, and nanowires on alumina substrates using a pulsed laser deposition (PLD) method. The presence of spherical gold catalyst particles at the tips of the nanostructures indicates selective growth via the vapor-liquid-solid (VLS) mechanism. Through a series of experiments, we have produced a primitive "phase diagram" for growing these structures based on several designed pressure and temperature parameters. Transmission electron microscopy (TEM) analysis has shown that the rods, wires, and belts are single-crystalline and grow along <111>m or <110>h directions. X-ray diffraction (XRD) measurements confirm phase and structural analysis. Superconducting quantum interference device (SQUID) measurements show that the iron oxide structures exhibit interesting magnetic behavior, particularly at room temperature. This work is the first known report of magnetite 1D nanostructure growth via the vapor-liquid-solid (VLS) mechanism without using a template, as well as the first known synthesis of long epsilon-Fe2O3 nanobelts and nanowires.

Journal Article↗
PubMed2006

Converting ceria polyhedral nanoparticles into single-crystal nanospheres.

Ceria nanoparticles are one of the key abrasive materials for chemical-mechanical planarization of advanced integrated circuits. However, ceria nanoparticles synthesized by existing techniques are irregularly faceted, and they scratch the silicon wafers and increase defect concentrations. We developed an approach for large-scale synthesis of single-crystal ceria nanospheres that can reduce the polishing defects by 80% and increase the silica removal rate by 50%, facilitating precise and reliable mass-manufacturing of chips for nanoelectronics. We doped the ceria system with titanium, using flame temperatures that facilitate crystallization of the ceria yet retain the titania in a molten state. In conjunction with molecular dynamics simulation, we show that under these conditions, the inner ceria core evolves in a single-crystal spherical shape without faceting, because throughout the crystallization it is completely encapsulated by a molten 1- to 2-nanometer shell of titania that, in liquid state, minimizes the surface energy. The principle demonstrated here could be applied to other oxide systems.

Journal Article↗
PubMed2006

Growth of large-area aligned molybdenum nanowires by high temperature chemical vapor deposition: synthesis, growth mechanism, and device application.

Large-area aligned Mo nanowires have been grown on stainless steel substrates by high-temperature chemical vapor deposition with the use of Mo metal. The detailed physical and chemical growth processes regarding the formation of the nanowires have been investigated using mass spectroscopy, thermogravimetry, and differential scanning calorimetry analysis, as well as structure analysis by electron microscopy. In reference to Gibbs energy calculation, our study reveals that the growth relies on the decomposition of MoO2 vapors through condensation of its vapor at high substrate temperatures. The aligned growth is a result of competing growth with the nanowires normal to the substrate surface reaching the final growth front. The field emission measurement and the vacuum luminescent tube study show that the Mo nanowires have potential application as electron emitters.

Journal Article↗
PubMed2006

A general approach to binary and ternary hybrid nanocrystals.

We describe and demonstrate a general strategy for engineering binary and ternary hybrid nanoparticles based on spontaneous epitaxial nucleation and growth of a second and third component onto seed nanoparticles in high-temperature organic solutions. Multifunctional hybrid nanoparticles that combine magnetic, plasmonic, and semiconducting properties and that are tunable in size and morphology can be realized, as demonstrated for combinations of Au, Fe3O4 and PbS or PbSe. The properties of each component within the hybrids can be modulated strongly by the conjugating component(s) aided by the coherent interfaces between them.

Crystallization↗
PubMed2006

[Preparation and biocompatibility of a novel cornea scaffold material].

A novel cornea tissue scaffold material was prepared with N-vinly pyrrolidome (NVP) and a biodegradable crosslinking agent by radical polymerization, using azoisobutyronitrile (AIBN) as initiator. Water absorption test and contact angle measure were conducted, and the degradation process of material was investigated. The biocompatibility evaluation was carried out by implantation of material in the rabbits, and by cell culture. The water absorption was over 104%, the contact angle was lower than 41degrees, and the degradation speed in vitro kept steady. The results of implantation in the rabbits showed that the material was almost degraded 3 months later and lots of collagen and cornea stroma cells appeared in it,but there was no inflammation around it. The result of epithelial cells culture showed that the cells conglutinated on the material, but no remarkable cytotoxicity was noted.

Animals↗
PubMed2006

[Ecological characteristics of Artemisia halodendron community and population on Horqin sandy land].

Based on the analysis of species important values and Shannon-Wiener index of Artemisia halodendron community on different type sandy lands in Horqin, A. halodendron community was classified into three types, i. e., A. halodendron - annual herbage, A. halodendron - perennial grass, and A. frigida - A. scoparia + perennial grass, which distributed on shifting sandy land, semi-fixed sandy land, and fixed sandy land, respectively. With the sand fixed, the community succession was ranked from A. halodendron - annual herbage (pioneer stage, coverage < 10%, Shannon-Wiener index 0. 33) to A. halodendron - perennial grass (coverage 30% to approximately 35%, Shannon-Wiener index 0. 56), and then to A. frigida - A. scoparia + perennial grass (steppe community, coverage 40% to approximately 45%, Shannon-Wiener index 0. 59). The A. halodendron population on shifting sandy land and that planted 5 years ago showed growing age distribution, that planted 18 years ago showed stable age distribution, and that on semi-fixed and fixed sandy lands showed declining age distribution. The results proved that A. halodendron populations had different ecological effects on A. halodendron community.

Artemisia↗
PubMed2005

Formation of PbSe nanocrystals: A growth toward nanocubes.

In this paper we report an electron microscopic observation of crystal shape development when PbSe nanocrystals were synthesized using a dynamic injection technique at different temperatures in the presence of oleic acid. A two-step evolution mechanism was proposed, indicating that the shape evolution of PbSe nanocrystals is dependent on the growth time, whereas the crystalline size can be tuned by varying the growth temperature under the studied conditions. It also implies that a higher growth rate in the 111 direction compared to that in the 100 direction results in the formation of nanocubes.

Journal Article↗
PubMed2005

Conversion of zinc oxide nanobelts into superlattice-structured nanohelices.

A previously unknown rigid helical structure of zinc oxide consisting of a superlattice-structured nanobelt was formed spontaneously in a vapor-solid growth process. Starting from a single-crystal stiff nanoribbon dominated by the c-plane polar surfaces, an abrupt structural transformation into the superlattice-structured nanobelt led to the formation of a uniform nanohelix due to a rigid lattice rotation or twisting. The nanohelix was made of two types of alternating and periodically distributed long crystal stripes, which were oriented with their c axes perpendicular to each other. The nanohelix terminated by transforming into a single-crystal nanobelt dominated by nonpolar (0110) surfaces. The nanohelix could be manipulated, and its elastic properties were measured, which suggests possible uses in electromechanically coupled sensors, transducers, and resonators.

Journal Article↗
PubMed2005

Electron energy-loss spectroscopy study of ZnO nanobelts.

Nanobelts of ZnO have well-defined shapes that are enclosed by {0001}, {0110} and {2110} facets. The nanobelts grow along [0110] and [2110] with large flat surfaces of +/-(0001) and +/-(0110), respectively. Electron energy-loss spectroscopy has been applied to study the electronic structure of ZnO nanobelts of different growth orientations. A plasmon peak observed at 13 eV is suggested to be the result of polar surface excitation. The energy-loss near-edge structure of the oxygen K and zinc L3 edges acquired from the two types of nanobelts show clear orientation dependence, and they agree well to the calculated results.

Journal Article↗
PubMed2005

Bismuth telluride hexagonal nanoplatelets and their two-step epitaxial growth.

We report a synthesis of discrete, single-crystal, defect-free, and hexagonal Bi2Te3 nanoplatelets using a high-temperature organic solution approach, and we demonstrate a two-step epitaxial growth of the cylindrical strings of Bi2Te3 nanoplatelets on the surface of the Te rod by packing them along c-axis in a top-bottom-top-bottom sequence. This type of building-up provides additional opportunity for the exploration of novel thermoelectric properties from such quantum-confined materials, in which the boundary scattering of phonons is anticipated to enhance.

Journal Article↗
PubMed2005

Controlled growth of large-area, uniform, vertically aligned arrays of alpha-Fe2O3 nanobelts and nanowires.

Vertically aligned iron oxide nanobelt and nanowire arrays have been synthesized on a large-area surface by direct thermal oxidation of iron substrates under the flow of O(2). The effects of reactive gas pressure, composition, and temperature have been systematically studied. It was found that nanobelts (width, tens of nanometers; thickness, a few nanometers) are produced in the low-temperature region (approximately 700 degrees C) whereas cylindrical nanowires tens of nanometers thick are formed at relatively higher temperatures (approximately 800 degrees C). Both nanobelts and nanowires are mostly bicrystallites with a length of tens of micrometers which grow uniquely along the [110] direction. The growth habits of the nanobelts and nanowires in the two temperature regions indicate the role of growth rate anisotropy and surface energy in dictating the ultimate nanomorphologies.

Ferric Compounds↗
PubMed2005

Study on biocompatibility of complexes of collagen-chitosan-sodium hyaluronate and cornea.

In this study we investigated the biocompatibility of collagen-chitosan-sodium hyaluronate (Col-Chi-NaHA) complexes and cornea tissue, and the feasibility of Col-Chi-NaHA complexes as substrates for cultivating rabbit corneal cells. Different components of Col-Chi-NaHA complexes were prepared and tested. A circular complex film with a diameter of 6 mm was inserted into rabbit stomal pocket and traced for a period of 5 months. Clinical examination was made. Rabbit limbal corneal epithelial cells, corneal endothelial cells, and keratocytes were cultured primarily on complexes. Phase contrast microscope examination was made daily. Histological, immunohistochemical, and scanning electron microscopic examinations were carried out. The complexes of 20% collagen, 10% chitosan, and 0.5% sodium hyaluronate showed rather weak corneal edema and other responses. The degradation of materials was obvious after 5 months. Corneas were transparent and translucent. Cells seeded on Col-Chi-NaHA were allowed to proliferate and partly form confluent monolayer after 9 days in culture. Cultured cells were well attached to the complexes of 20% collagen, 10% chitosan, and 0.5% sodium hyaluronate, or 10% chitosan and 0.5% sodium hyaluronate. The results showed that Col-Chi-NaHA complexes had good biocompatibility with cornea. The complexes can degrade and be absorbed in cornea. Col-Chi-NaHA complex may be a suitable substrate for cultivating corneal cells and a feasible material as a scaffold of tissue-engineered cornea.

Animals↗
PubMed2004

Crystal orientation-ordered ZnS nanowire bundles.

We report a novel approach for growing aligned and orientation-ordered ZnS nanowires. Our method relies on a buffer layer of CdSe grown on a Si(111) substrate, on which ZnS nanowires are grown. The growth process of the nanowire bundles is presented. The technique demonstrated could be an effective pathway for growing patterned, aligned, size-controlled, and orientation-ordered ZnS nanowires.

Journal Article↗