Biomedical subjects

Young Ha Rhee

Publications and source records attributed to Young Ha Rhee.

11 recordsLinked to original sources

PubMed2006

Preparation of alginate-quaternary ammonium complex beads and evaluation of their antimicrobial activity.

Alginate-quaternary ammonium complex beads with antimicrobial activity were prepared by the reaction of sodium alginate (SA) with 3-(trimethoxysilyl)propyl-octadecyldimethylammonium chloride (TSA) in acid solution, followed by crosslinking with CaCl(2). FTIR spectroscopy analysis showed that the resulting complex was formed mainly through covalent bonds between the hydroxyl groups of SA and the methoxysilyl groups of TSA. The complex beads exhibited a maximum swelling of 20% in water at 37 degrees C and were not hydrolyzed in water during experiments lasting for 30 days. The in vitro antimicrobial activity of the complex beads was evaluated against four species of bacteria and fungi. The test microorganisms were completely eliminated within 20 min when treated with 5% (v/v) complex beads, which showed a wide spectrum of excellent antimicrobial activity. The antimicrobial activity of the complex beads was retained after 10 cycles of washing and drying. The present results indicate that these SA-TSA complex beads are a new type of insoluble cationic polymer that can kill or remove microorganisms in water by mere contact without releasing the reactive agent.

Alginates↗

PubMed2006

Preparation and hydrolytic degradation of semi-interpenetrating networks of poly(3-hydroxyundecenoate) and poly(lactide-co-glycolide).

Semi-interpenetrating networks (semi-IPNs), where poly(lactide-co-glycolide) (PLGA) molecules were entrapped in the crosslinked matrices of poly(3-hydroxyundecenoate) (PHU), were prepared by irradiating homogeneous solutions of PHU and PLGA in chloroform with UV light. Attenuated total reflectance infrared spectroscopy showed that the PLGA chains were entrapped in PHU networks. The semi-IPNs showed enhanced mechanical strength as the PLGA content increased. The semi-IPNs were incubated at 37 degrees C in a 0.01N NaOH solution, and the extent of hydrolytic degradation was investigated by monitoring changes in various parameters such as water uptake, pH, mass, and morphology. Hydrolysis of semi-IPNs were significantly affected by the presence of PLGA. A semi-IPN prepared from a 9:1 (by weight) mixture of PHU and PLGA lost 25% of its original weight in 12 weeks while a PHU sample containing no PLGA lost only 5% of its weight during the same period under identical conditions. The hydrolysis was most likely accelerated when the pH of the medium was lowered by the hydrolyzed products of PLGA, 2-hydroxyalkanoic acids. These results showed that hydrolysis of PHA could be enhanced by incorporating a second component that lowered the pH of the hydrolysis system.

Hydrogen-Ion Concentration↗

PubMed2005

Drug release from and hydrolytic degradation of a poly(ethylene glycol) grafted poly(3-hydroxyoctanoate).

Monoacrylate-poly(ethylene glycol)-grafted poly(3-hydroxyoctanoate) (PEGMA-g-PHO) copolymers were synthesized to develop a swelling-controlled release delivery system for ibuprofen as a model drug. The in vitro hydrolytic degradation of and the drug release from a film made of the PEGMA-g-PHO copolymer were carried out in a phosphate buffer saline (pH 7.4) medium. The hydrolytic degradation of the copolymer was strongly dependent on the degree of grafting (DG) of the PEGMA group. The degradation rate of the copolymer films in vitro increased with increasing DG of the PEGMA group on the PHO chain. The copolymer films showed a controlled delivery of ibuprofen to the medium in periods of time that depend on the composition, hydrophilic/hydrophobic characteristics, initial drug loading amount and film thickness of the graft copolymer support. The drug release rate from the grafted copolymer films was faster than the rate of weight loss of the films themselves. In particular, a combination of the low DG of the PEGMA group in the PHO chains with the low ibuprofen solubility in water led to long-term constant release from these matrices in vitro.

Absorption↗

PubMed2005

Molecular characterization of extracellular medium-chain-length poly(3-hydroxyalkanoate) depolymerase genes from Pseudomonas alcaligenes strains.

A bacterial strain M4-7 capable of degrading various polyesters, such as poly(epsilon-caprolactone), poly(3-hydroxybutyrate-co-3-hydroxyvalerate), poly(3-hydroxyoctanoate), and poly(3-hydroxy-5-phenylvalerate), was isolated from a marine environment and identified as Pseudomonas alcaligenes. The relative molecular mass of a purified extracellular medium-chain-length poly(3-hydroxyalkanoate) (MCL-PHA) depolymerase (PhaZ(PalM4-7)) from P. alcaligenes M4-7 was 28.0 kDa, as determined by SDS-PAGE. The PhaZ(PalM4-7) was most active in 50 mM glycine-NaOH buffer (pH 9.0) at 35 degrees C. It was insensitive to dithiothreitol, sodium azide, and iodoacetamide, but susceptible to p-hydroxymercuribenzoic acid, N-bromosuccinimide, acetic anhydride, EDTA, diisopropyl fluorophosphate, phenylmethylsulfonyl fluoride, Tween 80, and Triton X-100. In this study, the genes encoding MCL-PHA depolymerase were cloned, sequenced, and characterized from a soil bacterium, P. alcaligenes LB19 (Kim et al., 2002, Biomacromolecules 3, 291-296) as well as P. alcaligenes M4-7. The structural gene (phaZ(PalLB19)) of MCL-PHA depolymerase of P. alcaligenes LB19 consisted of an 837 bp open reading frame (ORF) encoding a protein of 278 amino acids with a deduced M((r)) of 30,188 Da. However, the MCL-PHA depolymerase gene (phaZ(PalM4-7)) of P. alcaligenes M4-7 was composed of an 834 bp ORF encoding a protein of 277 amino acids with a deduced Mr of 30,323 Da. Amino acid sequence analyses showed that, in the two different polypeptides, a substrate-binding domain and a catalytic domain are located in the N-terminus and in the C-terminus, respectively. The PhaZ(PalLB19) and the PhaZ(PalM4-7) commonly share the lipase box, GISSG, in their catalytic domains, and utilize 111Asn and 110Ser residues, respectively, as oxyanions that play an important role in transition-state stabilization of hydrolytic reactions.

Amino Acid Sequence↗

PubMed2004

UV-induced graft copolymerization of monoacrylate-poly(ethylene glycol) onto poly(3-hydroxyoctanoate) to reduce protein adsorption and platelet adhesion.

Homogeneous solutions of poly(3-hydroxyoctanoate) (PHO) and the monoacrylate-poly(ethylene glycol) (PEGMA) monomer in chloroform were irradiated with UV light to obtain PEGMA-grafted PHO (PEGMA-g-PHO) copolymers. Variables affecting the degree of grafting (DG), such as the time of UV irradiation and the concentrations of the PEGMA monomer and initiator, were investigated. The PEGMA-g-PHO copolymers were characterized by measuring the water contact angle, molecular weight, thermal transition temperatures and mechanical properties, as well as by nuclear magnetic resonance spectroscopy. The results from all of these measurements indicate that PEGMA groups were present on the PHO polymer. The protein adsorption and platelet adhesion on the PEGMA-g-PHO surfaces were examined using poly(L-lactide) (PLLA) surfaces as the control. The proteins and platelets had a significantly lower tendency to adhere to the PEGMA-g-PHO copolymers than to PLLA. The graft copolymer with a high DG of PEGMA was very effective in reducing the protein adsorption and platelet adhesion and did not activate the platelets. The results obtained in this study suggest that PEGMA-g-PHO copolymers have the potential to be used as blood-contacting devices in a broad range of biomedical applications.

Acrylates↗

PubMed2004

Enzymatic and non-enzymatic degradation of poly (3-hydroxybutyrate-co-3-hydroxyvalerate) copolyesters produced by Alcaligenes sp. MT-16.

Poly(3-hydroxybutyrate-co-3-hydroxyvalerate), poly(3HB-co-3HV), copolyesters with a variety of 3HV contents (ranging from 17 to 60 mol%) were produced by Alcaligenes sp. MT-16 grown on a medium containing glucose and levulinic acid in various ratios, and the effects of hydrophilicity and crystallinity on the degradability of the copolyesters were evaluated. Measurements of thermo-mechanical properties and Fourier-transform infrared spectroscopy in the attenuated total reflectance revealed that the hydrophilicity and crystallinity of poly(3HB-co-3HV) copolyesters decreased as 3HV content in the copolyester increased. When the prepared copolyester film samples were non-enzymatically hydrolysed in 0.01 N NaOH solution, the weights of all samples were found to have undergone no changes over a period of 20 weeks. In contrast, the copolyester film samples were degraded by the action of extracellular polyhydroxybutyrate depolymerase from Emericellopsis minima W2. The overall rate of weight loss was higher in the films containing higher amounts of 3HV, suggesting that the enzymatic degradation of the copolyester is more dependent on the crystallinity of the copolyester than on its hydrophilicity. Our results suggest that the degradability characteristics of poly(3HB-co-3HV) copolyesters, as well as their thermo-mechanical properties, are greatly influenced by the 3HV content in the copolyesters.

Acyltransferases↗

PubMed2003

Poly(ethylene glycol)-grafted poly(3-hydroxyundecenoate) networks for enhanced blood compatibility.

Poly(ethylene glycol)-grafted poly(3-hydroxyundecenoate) (PEG-g-PHU) networks were prepared by irradiating homogeneous solutions of poly(3-hydroxyundecenoate) (PHU) and the monoacrylate of poly(ethylene glycol) (PEG) with UV light. The resulting polymer networks were characterized by measuring the water contact angle, water uptake, and mechanical properties and by performing attenuated total reflectance infrared spectroscopy and scanning electron microscopy. These measurements showed that the PEG chains were present in polymer networks. Adsorption of blood proteins and platelets on cross-linked PHU (CLPHU) and PEG-g-PHU were examined using poly(L-lactide) (PLLA) surfaces as control. Blood proteins and platelets had significantly lower tendency of adhesion to surfaces composed of CLPHU and PEG-g-PHU networks than to PLLA. Blood compatibility of polymer networks increased as the fraction of grafted PEG increased. The results of this study suggest that PEG-g-PHU networks might be useful for blood-compatible biomedical applications.

Adsorption↗

PubMed2003

Characterization of an extracellular medium-chain-length poly(3-hydroxyalkanoate) depolymerase from Streptomyces sp. KJ-72.

A bacterial strain capable of degrading medium-chain-length polyhydroxyalkanoates (MCL-PHAs) was isolated from a soil sample. This organism, which was identified as Streptomyces sp. KJ-72, secreted MCL-PHA depolymerase into the culture fluid only when it was cultivated on MCL-PHAs. The extracellular MCL-PHA depolymerase of the organism was purified to electrophoretic homogeneity by ion exchange column chromatography and gel filtration. The enzyme consisted of a monomeric subunit having a molecular mass of 27.1 kDa and isoelectric point of 4.7. The maximum activity was observed at pH 8.7 and 50 degrees C. The enzyme was sensitive to N-bromosuccinimide and acetic anhydride, indicating the presence of tryptophan and lysine residues in the catalytic domain. The enzyme was able to hydrolyze various chain-length p-nitrophenyl esters of fatty acids and polycaprolactone as well as various types of MCL-PHAs. However, lipase activity of the enzyme was not detected. The main hydrolysis product of poly(3-hydroxyheptanoate) was identified to be the dimer of 3-hydroxyheptanoate.

Carboxylic Ester Hydrolases↗

PubMed2003

Production of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with high molar fractions of 3-hydroxyvalerate by a threonine-overproducing mutant of Alcaligenes sp. SH-69.

A threonine overproducing mutant of Alcaligenes sp. SH-69 was isolated and its ability to produce poly(3-hydroxybutyrate-co-3-hydroxyvalerate), poly(3HB-co-3HV), was investigated. The 3HV fraction in poly(3HB-co-3HV) produced from glucose as the sole carbon source exceeded 22 mol%, which is approximately six times higher than that achieved by the wild type under the same culture conditions. Furthermore, the addition of a relatively low concentration (10 mM) of propionic acid, valeric acid or levulinic acid to the glucose medium greatly increased the molar fraction of 3HV in the copolyester, to 38-77 mol%. The results suggest that metabolic engineering of the biosynthetic pathways supplying polyhydroxyalkanoate monomers, such as the threonine biosynthetic pathway, can lead to new poly(3HB-co-3HV)-producing strains.

Alcaligenes↗

PubMed2002

Preparation and cell compatibility of acrylamide-grafted poly(3-hydroxyoctanoate).

Poly(3-hydroxyoctanoate) (PHO) films were treated with plasma of different discharge powers (10-50 W) and then treated with acryl amide solutions in order to prepare films with surfaces that contained different amounts of amide groups. The surfaces were characterized by contact angle measurement, attenuated total reflectance infrared spectroscopy, electron spectroscopy for chemical analysis, and scanning electron microscopy. Results from all these measurements indicated that amide groups were present on the surfaces. The amount of amide groups increased in proportion to the discharge power of the plasma. The interaction of Chinese hamster ovary cells with these grafted surfaces was investigated. The number of cells that adhered to and grew on the surfaces was highest for films grafted at 30 W of plasma discharge power, indicating that the moderate hydrophilicity was optimal for cells to adhere and grow. The present results support the suggestion that acryl amide-grafted PHO could be used as cell-compatible biomedical applications.

Acrylamides↗

PubMedDate not supplied

Characterization of an extracellular medium-chain-length poly(3-hydroxyalkanoate) depolymerase from Pseudomonas alcaligenes LB19.

An extracellular medium-chain-length poly(3-hydroxyalkanoate) (MCL-PHA) depolymerase from an isolate, Pseudomonas alcaligenes LB19, was purified to electrophoretic homogeneity by hydrophobic interaction chromatography using Octyl-Sepharose CL-4B and gel permeation chromatography using Sephadex G-150. The molecular mass of the enzyme, which consisted of a single polypeptide chain, was approximately 27.6 kDa. The pI value of the enzyme was estimated to be 5.7, and its maximum activity was observed at pH 9.0 and 45 degreesC. The enzyme was significantly inactivated by EDTA and phenylmethylsulfonyl fluoride (PMSF) but insensitive to dithiothreitol. It was also markedly inhibited by 0.1% Tween 80 and 0.05% Triton X-100. The purified enzyme could hydrolyze various types of bacterial aliphatic and aromatic MCL-PHAs but not poly(3-hydroxybutyrate), polycaprolactone, and poly(L-lactide). Biodegradation rates of the aromatic MCL-PHAs were significantly lower than those of the aliphatic MCL-PHAs, regardless of the compositions and types of aromatic substituents. It was able to hydrolyze medium-chain-length p-nitrophenylalkanoates more efficiently than the shorter-chain forms. The main hydrolysis products of poly(3-hydroxynonanoate) were identified as monomer units. The results demonstrated in this study suggest that the MCL-PHA depolymerase from P. alcaligenes LB19 is a distinct enzyme, which are different from those of other MCL-PHA degrading bacteria in its quaternary structure, pI value, sensitivity to EDTA and PMSF, and hydrolysis products of MCL-PHA.

Carboxylic Ester Hydrolases↗