PubMed2006

Oxidized, bioactive implants are rapidly and strongly integrated in bone. Part 1--experimental implants.

OBJECTIVES: The study presented was designed to investigate the speed and the strength of osseointegration of oxidized implants at early healing times in comparison which machined, turned implants. MATERIAL AND METHODS: Screw-shaped titanium implants were prepared and divided into two groups: magnesium ion incorporated, oxidized implants (Mg implants, n=10) and machined, turned implants (controls, n=10). Mg implants were prepared using micro-arc oxidation methods. Surface oxide properties of implants such as surface chemistry, oxide thickness, morphology/pore characteristics, crystal structures and roughness were characterized with various surface analytic techniques. Implants were inserted into the tibiae of ten New Zealand white rabbits. After a follow-up period of 3 and 6 weeks, removal torque (RTQ), osseointegration speed (DeltaRTQ/Deltahealing time) and integration strength of implants were measured. Bonding failure analysis of the bone-to-implant interface was performed. RESULTS: The speed the and strength of osseointegration of Mg implants were significantly more rapid and stronger than for turned implants at follow-up periods of 3 and 6 weeks. Bonding failure for Mg implants dominantly occurred within the bone tissue, whereas bonding failure for turned implants mainly occurred at the interface between implant and bone. CONCLUSIONS: Oxidized, bioactive implants are rapidly and strongly integrated in bone. The present results indicate that the rapid and strong integration of oxidized, bioactive Mg implants to bone may encompass immediate/early loading of clinical implants.

Animals↗

PubMed2006

Inflammatory response to a titanium surface with potential bioactive properties: an in vitro study.

BACKGROUND: The current hard tissue implants research aims to accelerate bone healing by designing surfaces that are bioactive. However, the role of the inflammatory response to these surfaces is so far incompletely described. PURPOSE: The aim of the study was to evaluate early inflammatory response in vitro to a potentially bioactive surface--an anodized surface with Mg ions incorporated (anodized/Mg)--and to compare it to a turned, a blasted, and an anodized surface. MATERIALS AND METHODS: An interferometer was used for topographical characterizations. The disks were incubated with human mononuclear cells. Adherent cells were investigated with respect to number of cells, viability, differentiation, and cytokine production with and without lipopolysaccharide stimulation after 24 and 72 hours. RESULTS: The number of adhered mononuclear cells differed significantly between the different modified surfaces, with the highest number on the anodized surface. However, there were no significant differences in cytokine production and differentiation between the different modified surfaces. The amount of anti-inflammatory mediator interleukin-10 remained over time, while the number of cells and pro-inflammatory cytokine tumor necrosis factor-alpha decreased. The cells were viable on all surfaces, respectively. CONCLUSION: The anodized surfaces with and without Mg ions showed an increased cell adherence, however, otherwise an inflammatory response similar to the turned and blasted surfaces. Furthermore, the potentially bioactive anodized/Mg surface showed a similar response to the TiUnite-like anodized surface despite the former having a surface roughness of a smoother character.

Cell Adhesion↗

PubMed2005

The bone response of oxidized bioactive and non-bioactive titanium implants.

A number of experimental and clinical data on so-called oxidized implants have reported promising outcomes. However, little is investigated on the role of the surface oxide properties and osseointegration mechanism of the oxidized implant. Sul [On the Bone Response to Oxidized Titanium Implants: The role of microporous structure and chemical composition of the surface oxide in enhanced osseointegration (thesis). Göteborg: Department of Biomaterials/Handicap Research, University of Göteborg, Sweden; 2002; Biomaterials 2003; 24: 3893-3907] recently proposed two action mechanisms of osseointegration of oxidized implants, i.e. mechanical interlocking through bone growth in pores/other surface irregularities (1) and biochemical bonding (2). The aim of the present study is two-fold: (i) investigating the role of the implant surface chemistry on bone responses; (ii) investigating the validity of the biochemical bonding theory of the oxidized, bioactive bone implants with specific implant surface chemistry. Two groups of oxidized implants were prepared using micro arc oxidation process and were then inserted in rabbit bone. One group consisted of magnesium ion incorporated implants (MgTiO implant), the other consisted of TiO2 stoichiometry implants (TiO implant). Surface oxide properties of the implants were characterized with various surface analytic techniques. After 6 weeks of follow up, the mean peak values of removal torque of Mg implants dominated significantly over TiO implants (p < or = 0.0001). Bonding failure generally occurred in the bone away from the bone to implant interface for the MgTiO implant and mainly occurred at the bone to implant interface for the TiO implant that consisted mainly of TiO2 chemistry and significantly rougher surface as compared to the MgTiO implant. Between bone and the Mg- incorporated implant surface, ionic movements and ion concentrations gradient were detected. The current in vivo experimental data may provide positive evidence for the surface chemistry-mediated biochemical bonding theory of oxidized bioactive implants. However, the present study does not rule out potential synergy effects of the oxide thickness, micro-porous structure, crystal structure and surface roughness on improvements of bone responses to oxidized bioactive implants.

Absorbable Implants↗

PubMed2004

Biomechanical measurements of calcium-incorporated oxidized implants in rabbit bone: effect of calcium surface chemistry of a novel implant.

BACKGROUND: In oral implantology there has been a general trend away from machine-turned minimally rough and acid-etched and blasted implants toward intermediary roughened surfaces. Mechanical interlocking at micron resolution is claimed to be the dominant reason for the fixation of such implants in bone. However, clinical demands for stronger and faster bone bonding to the implant (eg, in immediately loaded and compromised bone cases) have motivated the development of novel surfaces capable of chemical bonding. PURPOSE: The purpose of the present study is to investigate bone tissue reactions to a newly developed calciumincorporated oxidized implant. The specific aim is to assess the effect of calcium surface chemistry on the bone response. MATERIALS AND METHODS: Calcium (Ca) ion-incorporated implants were prepared by micro arc oxidation methods. Surface oxide properties were characterized by using various surface analytic techniques involving scanning electron microscopy, x-ray diffractometry, x-ray photoelectron spectroscopy, and optical interferometry. Twenty screw-shaped commercially pure (CP) titanium implants (10 turned implants [controls] and 10 Ca-incorporated implants [tests]) were inserted in the femoral condyles of 10 New Zealand White rabbits. RESULTS: After a healing period of 6 weeks, resonance frequency analyses and removal torque measurements of the Ca-incorporated oxidized implants demonstrated statistically significant improvements of implant integration with bone in comparison to machine-turned control implants (p = 0.013 and p = 0.005, respectively). CONCLUSIONS: The Ca-reinforced surface chemistry of the oxidized implants significantly improved bone responses in a rabbit model. The present study suggests that biochemical bonding at the bone-implant interface, in combination with mechanical interlocking, may play a dominant role in the fixation of Ca-incorporated oxidized implants in bone. The observed rapid and strong integration of test Ca implants may have clinical implications for immediate or early loading and improved performance in compromised bone.

Animals↗

PubMed2003

The significance of the surface properties of oxidized titanium to the bone response: special emphasis on potential biochemical bonding of oxidized titanium implant.

The aim of the present study is to investigate bone tissue reactions to various surface oxide properties, in particular to different surface oxide chemistry of oxidized titanium implants (grade 1). One control and three test screw-shaped implant groups were prepared. Controls were turned implants. Test implants, i.e. S implants, P implants and Ca implants were by the micro-arc oxidation (MAO) method. The surface characterizations were performed with X-ray photoelectron spectroscopy, Auger electron spectroscopy, scanning electron microscopy, X-ray diffractometry and TopScan 3D. Eighty implants were inserted in the femora and tibiae of ten mature New Zealand white rabbits for 6 weeks. The removal torque values (RTQ) showed significant differences between S implants and controls (p=0.022), Ca implants and controls (p=0.0001), Ca implants and P implants (p=0.005) but did not show significant differences between the others (p>0.05). In addition, the bone to metal contact (BMC) around the entire implants demonstrated 186% increase in S implants, 232% increase in P implants and 272% increase in Ca implants when compared to the paired control groups. Based on the comparative analysis of the surface characteristics resulting different bone responses between all groups, it was concluded that surface chemistry and topography separately or together play important roles in the bone response to the oxidized implants.

Animals↗

PubMed2002

Characteristics of the surface oxides on turned and electrochemically oxidized pure titanium implants up to dielectric breakdown: the oxide thickness, micropore configurations, surface roughness, crystal structure and chemical composition.

Titanium implants have been used widely and successfully for various types of bone-anchored reconstructions. It is believed that properties of oxide films covering titanium implant surfaces are of crucial importance for a successful osseointegration, in particular at compromized bone sites. The aim of the present study is to investigate the surface properties of anodic oxides formed on commercially pure (c.p.) titanium screw implants as well as to study 'native' oxides on turned c.p. titanium implants. Anodic oxides were prepared by galvanostatic mode in CH3COOH up to the high forming voltage of dielectric breakdown and spark formation. The oxide thicknesses, measured with Auger electron spectroscopy (AES), were in the range of about 200-1000 nm. Barrier and porous structures dominated the surface morphology of the anodic film. Quantitative morphometric analyses of the micropore structures were performed using an image analysis system on scanning electron microscopy (SEM) negatives. The pore sizes were < or = 8 microm in diameter and had 1.27-2.1 microm2 opening area. The porosity was in the range of 12.7-24.4%. The surface roughness was in the range of 0.96-1.03 microm (Sa), measured with TopScan 3D. The crystal structures of the titanium oxide were amorphous, anatase, and a mixtures of anatase and rutile type, as analyzed with thin-film X-ray diffractometry (TF-XRD) and Raman spectroscopy. The chemical compositions consisted mainly of TiO2, characterized with X-ray photoelectron spectroscopy (XPS). The native (thermal) oxide on turned implants was 17.4 nm (+/- 6.2) thick and amorphous. Its chemical composition was TiO2. The surface roughness had an average height deviation of 0.83 microm (Sa). The present results are needed to elucidate the influence of the oxide properties on the biological reaction. The results of animal studies using the presently characterized surface oxides on titanium implants will be published separately.

Crystallography, X-Ray↗

PubMed2002

Qualitative and quantitative observations of bone tissue reactions to anodised implants.

Research projects focusing on biomaterials related factors; the bulk implant material, the macro-design of the implant and the microsurface roughness are routinely being conducted at our laboratories. In this study, we have investigated the bone tissue reactions to turned commercially pure (c.p.) titanium implants with various thicknesses of the oxide films after 6 weeks of insertion in rabbit bone. The control c.p. titanium implants had an oxide thickness of 17-200 nm while the test implants revealed an oxide thickness between 600 and 1000 nm. Routine histological investigations of the tissue reactions around the implants and enzyme histochemical detections of alkaline and acid phosphatase activities demonstrated similar findings around both the control and test implants. In general, the histomorphometrical parameters (bone to implant contact and newly formed bone) revealed significant quantitative differences between the control and test implants. The test implants demonstrated a greater bone response histomorphometrically than control implants and the osteoconductivity was more pronounced around the test implant surfaces. The parameters that differed between the implant surfaces, i.e. the oxide thickness, the pore size distribution, the porosity and the crystallinity of the surface oxides may represent factors that have an influence on the histomorphometrical results indicated by a stronger bone tissue response to the test implant surfaces, with an oxide thickness of more than 600 nm.

Acid Phosphatase↗

PubMed2002

Resonance frequency and removal torque analysis of implants with turned and anodized surface oxides.

The present experimental study was designed to address two issues. The first was to investigate whether oxide properties of titanium implants influenced bone tissue responses after an in vivo implantation time of six weeks. If such a result was found, the second aim was to investigate which oxide properties are involved in such bone tissue responses. Screw-shaped implants with a wide range of oxide properties were prepared by electrochemical oxidation methods, where the oxide thickness varied in the range of 200 nm to 1000 nm. The surface morphology was prepared in two substantially different ways, i.e. barrier and porous oxide film structures. The micropore structure revealed pore sizes of 8 microm in diameter, with a range in opening area from 1.27 microm 2 to 2.1 microm 2. Porosity ranged from 12.7% to 24.4%. The crystal structures of the titanium oxide were amorphous, anatase and a mixture of anatase and rutile type. The chemical compositions consisted mainly of TiO2. Surface roughness ranged from 0.96 microm to 1.03 microm (Sa). Each group of test samples showed its own, defined status with respect to these various parameters. The oxide properties of turned commercially pure titanium implants were used in the control group, which was characterized by an oxide thickness of 17.4 +/- 6.2 nm, amorphous type in crystallinity, TiO2 in chemical composition, and a surface roughness of 0.83 microm (Sa). Bone tissue responses were evaluated by resonance frequency measurements and removal torque tests that were undertaken six weeks after implant insertion in rabbit tibia. Implants that had an oxide thickness of approximately 600, 800 and 1000 nm demonstrated significantly stronger bone responses in the evaluation of removal torque values than did implants that had an oxide thickness of approximately 17 and 200 nm (P < 0.05). However, there were no difference between implants with oxide thicknesses of 17 and 200 nm (P = 0.99). It was concluded that oxide properties of titanium implants, which include oxide thickness, micropore configurations and crystal structures, greatly influence the bone tissue response in the evaluation of removal torque values. However, it is not fully understood whether these oxide properties influence the bone tissue response separately or synergistically.

Animals↗

PubMed2002

Bone reactions to oxidized titanium implants with electrochemical anion sulphuric acid and phosphoric acid incorporation.

BACKGROUND: The importance of the surface properties of implants for a successful osseointegration has been emphasized. It is generally known that bone response to implant surfaces is considerably related to the various surface properties. PURPOSE: The purpose of this study was to investigate bone tissue reactions to multifactorial biocompatibility of the surface oxide of electrochemically oxidized titanium implants. The ultimate objective was to improve surface quality, resulting in enhancement of clinical outcomes of osseointegrated implants. MATERIALS AND METHODS: Three different surface types of commercially pure titanium (c.p. Ti) implants were prepared. Turned implants were used for controls and test implants were prepared by the micro arc oxidation (MAO) method, either in sulphuric acid (S implants) or in phosphoric acid (P implants). Implants were inserted in the femur and tibia of 10 mature New Zealand White rabbits. The bone response was evaluated by biomechanical tests, histology, and histomorphometry. The follow-up time was 6 weeks. RESULTS: The mean peak values of the removal torque showed significant differences between control and test S implants (p =.022) but showed no significant differences between control and test P implants (p =.195) or between test S and test P implants (p =.457). In addition, the histomorphometric comparisons of the bone-to-metal contact around entire implants demonstrated 186% increase in S implants (p =.028) and 232% increase in P implants (p =.028) compared with the paired control groups. Quantification of the bone area in the threads did not show any significant differences. CONCLUSIONS: The present results suggest that the primary mode of action in strong bone response to S implants is mechanical interlocking, and to P implants, it is biochemical interaction. It is possible that the phosphate groups in the titanium oxide of P implants provide potential chemical bonding sites for calcium ions and hydroxyapatite of the bone matrix during biologic mineralization. key words: bone responses, histomorphometry, oxidized implants, removal torque test, surface oxide properties

Animals↗

PubMedDate not supplied

Oxidized titanium screws coated with calcium ions and their performance in rabbit bone.

PURPOSE: The aim was to answer a fundamental question: Do the chemical properties of titanium implants influence osseointegration? MATERIALS AND METHODS: Screw-type implants produced of turned commercially pure (grade 1) titanium (controls) and electrochemically calcium-deposited titanium implants (Ca test implants) were placed in the tibiae and femora of a total of 10 mature New Zealand white rabbits. The macro arc oxidation method was applied for Ca implants. Surface oxides were characterized with different analytic techniques, including x-ray photoelectron spectroscopy, auger electron spectroscopy, scanning electron microscopy, thin-film x-ray diffractometry, and TopScan 3D. The bone response was evaluated by biomechanical tests, histology, and histomorphometry. RESULTS: After a follow-up period of 6 weeks, test Ca implants showed a significant increase in mean peak removal torque (P = .0001) and in the histomorphometric measurement of bone-to-metal contact around the implants (P = .028) in comparison to controls. In addition, more mature mineralized bone was observed adjacent to test Ca implants compared to controls, as evaluated on 10-microm undecalcified, toluidine blue-stained, cut, and ground sections. DISCUSSION: The potential role of surface Ca chemistry to a superior bone response is discussed with specific reference to interaction with Ca(+)-binding proteins and function as binding sites of calcium phosphate mineral. CONCLUSION: The present results suggest that the surface chemical composition of titanium implants is of great importance for the bone response. Ca ion-deposited titanium implants showed fast and strong osseointegration in the rabbit bone model.

Animals↗

PubMedDate not supplied

Optimum surface properties of oxidized implants for reinforcement of osseointegration: surface chemistry, oxide thickness, porosity, roughness, and crystal structure.

PURPOSE: To investigate detailed surface characterization of oxidized implants in a newly invented electrolyte system and to determine optimal surface oxide properties to enhance the bone response in rabbits. MATERIALS AND METHODS: A total of 100 screw-type titanium implants were prepared and divided into 1 control group (machine-turned implants) and 4 test groups (magnesium ion-incorporated oxidized implants). Forty implants were used for surface analyses. A total of 60 implants, 12 implants from each group, were placed in the tibiae of 10 New Zealand white rabbits and measured with a removal torque test after a healing period of 6 weeks. RESULTS: For the test groups, the oxide thicknesses ranged from about 1,000 to 5,800 nm; for the control group, mean oxide thickness was about 17 nm. The surface morphology showed porous structures for test groups and nonporous barrier film for the control group. Pore diameter ranged from < or = 0.5 microm to < or = 3.0 microm. In regard to surface roughness, arithmetic average height deviation (Sa) values varied from 0.68 to 0.98 microm for test implants and 0.55 microm for control implants; developed surface ratio (Sdr) values ranged from 10.6% to 46% for the test groups and were about 10.6% for the control group. A mixture of anatase and rutile-type crystals were observed in the test groups; amorphous-type crystals were observed in the control group. After a healing period of 6 weeks, removal torque measurements in all 4 test groups demonstrated significantly greater implant integration as compared to machine-turned control implants (P < or = .033). DISCUSSION: Determinant oxide properties of oxidized implants are discussed in association with bone responses. Of all surface properties, RTVs were linearly increased as relative atomic concentrations of magnesium ion increase. CONCLUSIONS: Surface properties of the oxidized implants in the present study, especially surface chemistry, influenced bone responses. The surface chemistry of the optimal oxidized implant should be composed of approximately 9% magnesium at relative atomic concentration in titanium oxide matrix and have an oxide thickness of approximately 1,000 to 5,000 nm, a porosity of about 24%, and a surface roughness of about 0.8 microm in Sa and 27% to 46% in Sdr; its oxide crystal structure should be a mixture of anatase- and rutile-phase crystals.

Animals↗

PubMedDate not supplied

Which surface properties enhance bone response to implants? Comparison of oxidized magnesium, TiUnite, and Osseotite implant surfaces.

PURPOSE: This study compared the speed and strength of osseointegration and osteoconductivity between an oxidized experimental magnesium (Mg) implant, an oxidized commercially available TiUnite implant, and a dual acid-etched surface Osseotite implant. The aim was to investigate which surface properties enhance bone response to implants, and thereby to test a biochemical bonding theory. MATERIALS AND METHODS: A total of 60 screw implants (20 of each design) were inserted through 1 cortex into the tibiae of 10 rabbits. Surface chemistry, oxide thickness, morphology, crystal structure, and surface roughness were evaluated. After healing times of 3 and 6 weeks, all bone implants were unscrewed with removal torque (RTQ) devices, and the bone specimens were subjected to histomorphometry. RESULTS: RTQ values for Mg, TiUnite, and Osseotite implants were 27.1, 21.3, and 15.4 Ncm, with new bone formation values of 29%, 18%, and 15%, respectively, at 3 weeks. At 6 weeks the RTQ values were 37.5, 36.4, and 21.5 Ncm, with new bone formation values of 39%, 31%, and 26%, respectively. DISCUSSION: Mg implants demonstrated significantly greater RTQ values (P = .008 and P = .0001) and more new bone formation (P = .031 and P = .030) than Osseotite at 3 and 6 weeks, respectively. Mg implants also showed higher RTQ values at 3 weeks and new bone formation at 6 weeks than TiUnite, but neither were significant (P > .05). TiUnite showed significantly higher RTQ values than Osseotite at 6 weeks (P = .001), but was not significant at 3 weeks (P > .05). Osseointegration rate (deltaRTQ/deltaweeks) was significantly faster for Mg (P = .011) and TiUnite (P = .001) implants between 3 and 6 weeks of healing time, but was not significant for Osseotite. CONCLUSIONS: The results indicate that surface chemistry facilitated more rapid and stronger osseointegration of the Mg implants despite their minimal roughness compared to the moderately roughened TiUnite. This suggests potential advantages of Mg implants for reducing high implant failure rates in the early postimplantation stage and in compromised bone, making it possible to shorten bone healing time from surgery to functional loading, and enhancing the possibility of immediate/early loading.

Animals↗