High magnetization helical carbon nanofibers produced by nanoparticle catalysis.

Helical carbon nanofibers were synthesized by means of acetylene pyrolysis at 450 degrees C using Fe nanoparticles as catalyst. There is no need to modify the Fe nanoparticles by a chiral reagent. The carbon nanofibers generated are crystalline and symmetric, with the (110) plane of Fe particle being the mirror plane. There would be a change in the shape of the nanofibers if the temperature at the beginning or during the synthesis were altered. Compared to the helical carbon nanofibers reported elsewhere in the literature, our samples show higher magnetization.

Journal Article↗
PubMed2005

NixPb1-x nanowire arrays: effects of annealing.

Ni(x)Pb(1-x) nanowire arrays were successfully fabricated by AC electrodeposition within the nanopores of ordered porous alumina films prepared by a two-step anodization. Transmission electron microscopy analyses showed that the Ni-Pb nanoarrays are polycrystalline with dimension uniformity around 20 nm in diameter and lengths up to several micrometers. X-ray diffraction results revealed that the face-centered-cubic (fcc) Ni and fcc Pb peaks are detected when the Ni component (x) is below 0.71, indicating that the Ni(x)Pb(1-x) nanoarrays do not form metastable phase alloy. Hysteresis loops determined by vibrating sample magnetometer indicated that the Ni(x)Pb(1-x) nanoarrays obtained possess obvious magnetic anisotropy, and the perpendicular coercivity was lower than that of pure Ni nanowries before and after annealing. Annealing under magnetic field was carried out to examine the effect of a magnetic field on magnetic properties using an electromagnet field up to 0.3 T.

Journal Article↗
PubMed2005

Single crystal SnO2 zigzag nanobelts.

Zigzag SnO2 nanobelts have been synthesized by evaporating tin grain in air. XRD, SEM, and TEM were employed to characterize the prepared samples. SEM images showed large amounts of zigzag nanobelts with periodic morphology. XRD result showed a pure tetragonal SnO2 phase. HRTEM and SAED revealed a single crystal structure with [010] zone axis on the whole zigzag zone. The zigzag structure is deduced to be formed by shifting the growth direction from [101] to [10] or vice versa. Growing nanobelts along different equivalent directions opens a new avenue for the preparation of novel nanostructured materials.

Journal Article↗