PubMed2006

Size- and shape-dependent transformation of nanosized titanate into analogous anatase titania nanostructures.

A size- and shape-dependent morphological transformation was demonstrated during the hydrothermal soft chemical transformation, in neutral solution, of titanate nanostructures into their anatase titania counterparts. Specifically, lepidocrocite hydrogen titanate nanotubes with diameters of approximately 10 nm were transformed into anatase nanoparticles with an average size of 12 nm. Lepidocrocite hydrogen titanate nanowires with relatively small diameters (average diameter range of < or = 200 nm) were converted into single-crystalline anatase nanowires with relatively smooth surfaces. Larger diameter (>200 nm) titanate wires were transformed into analogous anatase submicron wire motifs, resembling clusters of adjoining anatase nanocrystals with perfectly parallel, oriented fringes. Our results indicate that as-synthesized TiO2 nanostructures possessed higher photocatalytic activity than the commercial titania precursors from whence they were derived.

Materials Testing↗
PubMed2006

Synthesis and growth mechanism of titanate and titania one-dimensional nanostructures self-assembled into hollow micrometer-scale spherical aggregates.

Three-dimensional, dendritic micrometer-scale spheres of alkali metal hydrogen titanate 1D nanostructures (i.e., nanowires and nanotubes) have been generated using a modified hydrothermal technique in the presence of hydrogen peroxide and an alkali metal hydroxide solution. Sea-urchin-like assemblies of these 1D nanostructures have been transformed into their hydrogen titanate analogues (lepidocrocite HxTi2-x/4squarex/4O4 (x approximately 0.7, square: vacancy)) by neutralization as well as into their corresponding anatase TiO2 nanostructured counterparts through a moderate high-temperature annealing dehydration process without destroying the 3D hierarchical structural motif. The as-prepared hollow spheres of titanate and titania 1D nanostructures have overall diameters, ranging from 0.8 to 1.2 microm, while the interior of these aggregates are vacuous with a diameter range of 100 to 200 nm. The constituent, component titanate and TiO2 1D nanostructures have a diameter range of 7+/-2 nm and lengths of up to several hundred nanometers. A proposed two-stage growth mechanism of these hollow micrometer-scale spheres was supported by time-dependent scanning electron microscopy, atomic force microscopy, and inductively coupled plasma atomic emission spectrometry data. We have also demonstrated that these assemblies are active photocatalysts for the degradation of synthetic Procion Red dye under UV light illumination.

Journal Article↗
PubMed2005

Synthesis of classes of ternary metal oxide nanostructures.

Nanoscale structures, such as nanoparticles, nanorods, nanowires, nanocubes, and nanotubes, have attracted extensive synthetic attention as a result of their novel size-dependent properties. Ideally, the net result of nanoscale synthesis is the production of structures that achieve monodispersity, stability, and crystallinity with a predictable morphology. Many of the synthetic methods used to attain these goals have been based on principles derived from semiconductor technology, solid state chemistry, and molecular inorganic cluster chemistry. We describe a number of advances that have been made in the reproducible synthesis of various ternary oxide nanomaterials, including alkaline earth metal titanates, alkali metal titanates, bismuth ferrites, ABO(4)-type oxides, as well as miscellaneous classes of ternary metal oxides.

Journal Article↗
PubMed2004

General, room-temperature method for the synthesis of isolated as well as arrays of single-crystalline ABO4-type nanorods.

Single-crystalline BaWO(4) and BaCrO(4) nanorods of reproducible shape and of varying sizes have been controllably prepared using a simple, room-temperature approach, based on the use of porous alumina template membranes. Aligned BaWO(4) and BaCrO(4) nanorod arrays can be obtained by dissolving the template. Our facile technique, which is analogous to biomineralization, offers a promising and generalized methodology to prepare other types of free-standing ABO(4) nanorods and their corresponding nanorod arrays. Extensive characterization of these samples has been performed using scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), energy-dispersive X-ray spectroscopy (EDS), selected area electron diffraction (SAED), Raman spectroscopy, FT-infrared spectroscopy (FT-IR), and X-ray diffraction (XRD).

Journal Article↗
PubMed2003

Large-scale synthesis of single-crystalline perovskite nanostructures.

Single-crystalline perovskite nanostructures with reproducible shape have been prepared using a simple, readily scaleable solid-state reaction in the presence of NaCl and a nonionic surfactant. Pristine BaTiO3 nanowires have diameters ranging from 50 to 80 nm with an aspect ratio larger than 25. Single-crystalline SrTiO3 nanocubes with a mean edge length of 80 nm have been produced using a similar procedure.

Journal Article↗
PubMed2003

Hydrothermal synthesis of perovskite nanotubes.

A low-temperature hydrothermal reaction has been utilized to generate crystalline barium titanate and strontium titanate nanotubes, which have been characterized by means of X-ray diffraction and transmission electron microscopy, coupled with energy dispersive X-ray analysis.

Journal Article↗