PubMed2006

MnS hierarchical hollow spheres with novel shell structure.

High yields of MnS microspheres with novel hierarchical structure were prepared through a simple solution method. Field emission scanning electron microscopy and transmission electron microscopy analyses reveal that the microsphere has a core-shell structure: the interior hollow sphere is covered by a shell consisting of nanorod arrays. Interestingly, the nanorod is a wurtzite (WZ)/zinc blende (ZB) phase admixture with a large amount of stacking faults/twins. The alternation of WZ and ZB along the growth direction of the nanorod enables it to exhibit the features of a quantum well. Furthermore, the WZ/ZB admixture structure could also be regarded as a type II homomaterial heterostructure. All these features imply that the novel core-shell structure has great potential for applications, among them the quantum well photoelectrical and heterostructure photoconduction fields.

Journal Article↗

PubMed2006

Tunable red-green upconversion luminescence in novel transparent glass ceramics containing Er: NaYF4 nanocrystals.

To develop NaYF(4) as bulk luminescence material, transparent glass ceramics containing Er(3+): NaYF(4) nanocrystals were fabricated for the first time, and the influences of heat-treatment temperature and Er(3+) doping level on their upconversion luminescence were investigated. With increasing heating temperature, the upconversion intensity enhanced accordingly, attributing to the incorporation of more Er(3+) into the grown NaYF(4). Notably, when the heating temperature reached 650 degrees C, the upconversion intensity augmented drastically due to the occurrence of phase transition from the cubic NaYF(4) to the hexagonal one. Interestingly, for the samples heat-treated at 620 degrees C, when the Er(3+) doping level was increased from 0.05 to 2.0 mol %, the upconversion emission was whole-range tunable from monochromatic green to approximately monochromatic red, which could be mainly attributed to the cross-relaxation between Er(3+) ions. The excellent optical properties and its convenient, low-cost synthesis of the present glass ceramic imply that it is an excellent substitution material for the unobtainable bulk NaYF(4) crystal, potentially applicable in many fields.

Journal Article↗

PubMed2006

Spectroscopic properties of Nd3+ doped transparent oxyfluoride glass ceramics.

In this paper, the spectroscopic properties of Nd(3+) doped transparent oxyfluoride glass ceramics containing LaF(3) nano-crystals were systematically studied. The formation and distribution of LaF(3) nano-crystals in the glass matrix were investigated by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Based on Judd-Ofelt theory, the intensity parameters Omega(t) (t=2, 4, 6), spontaneous emission probability, radiative lifetime, radiative quantum efficiency, width of the emission line and stimulated emission cross-section of Nd(3+) were evaluated. Particularly, the effect of Nd(3+) doping level on them was discussed. With the increase of Nd(3+) concentration in the glass ceramic, the experimental luminescence lifetime, radiative quantum efficiency and stimulated emission cross-section vary from 353.4 micros, 78.3% and 1.86 x 10(-20)cm(2) to 214.7 micros, 39.9% and 1.52 x 10(-20)cm(2), respectively. The comparative study of Nd(3+) spectroscopic parameters in different hosts suggests that the investigated glass ceramic system is potentially applicable as laser materials for 1.06 microm emission.

Ceramics↗

PubMed2006

Shape control of monodisperse CdS nanocrystals: hexagon and pyramid.

The wurtzite CdS nanocrystals with hexagonal or pyramidal geometries were selectively synthesized by tuning the molar ratio of Cd and S precursors in the solution system. For hexagonal nanocrystals, a 2-D or 3-D superlattice assembly could be obtained due to the narrow particle size distribution. The pyramidal CdS nanocrystals were divided into two geometries: the hexagon-based pyramid and the triangle-based pyramid. The realization of the pyramidal geometries further extends the shape multiformity of wurtzite CdS nanocrystals, which may bring new opportunities for the development of CdS semiconductors. The room-temperature absorption spectra of CdS nanoparticles with hexagonal and pyramidal morphologies exhibited a discrepancy in peak positions, revealing the existence of a profound shape-property relationship for the CdS nanophase.

Journal Article↗

PubMed2006

Metastable gamma-MnS hierarchical architectures: synthesis, characterization, and growth mechanism.

Preparation of shape-controlled metastable gamma-MnS semiconductor nanocrystals has been achieved on a large scale through a simple solvothermal method in the presence of PVP. The key strategy is the use of sulfur powder as sulfur source in ethylene glycol (EG) solvent that also acted as a weak reducing agent. Reaction parameters such as reaction time and temperature are found to be important in controlling various hierarchical architectures, such as homogeneous semi-hollow core-shell, hollow nanospheres, and nanowires. Transmission electron microscopy observations indicate that these hierarchical architectures are formed mainly via Ostwald ripening. The optical absorption measurements reveal that these novel architectures exhibit remarkable shift of absorption peak during the course of structural compaction and grain growth.

Journal Article↗

PubMed2006

Quasicubic alpha-Fe2O3 nanoparticles with excellent catalytic performance.

Uniform quasicubic alpha-Fe(2)O(3) nanoparticles enclosed by six identical {110} planes were synthesized by a simple solvothermal method. TEM investigations revealed that they were formed through oriented attachment of primary nanocrystals assisted by Ostwald ripening, and PVP surfactant played an important role in control over the final morphology of the products. These quasicubic nanoparticles could catalyze oxidation of almost 100% CO at a temperature of 230 degrees C, much lower than those of nanophases with flowerlike, hollow, or other forms of irregular external morphologies having various crystal planes exposed to the gas, indicating that the external morphology and especially the exposure crystal planes of alpha-Fe(2)O(3) nanocatalyst affect the catalytic activity more significantly than the traditionally accepted factors (such as high BET surface area, hollow structure, etc.) do for CO catalytic oxidation.

Journal Article↗

PubMed2005

Two-step self-assembly of nanodisks into plate-built cylinders through oriented aggregation.

Oriented aggregation-based self-assembly of hexagonal LaF3 nanodisks with cavities into plate-built cylinders proceeding in acidic solution in the absence of any organic additive was disclosed. The self-assembly consists of two steps. First, the nanodisks sequentially aggregated together by coalescence mainly through {100} planes to form larger monocrystalline plates, followed by Ostwald ripening to smooth their surfaces. The holes on the primary nanodisks should be responsible for this intriguing growth. Second, the surface-smoothed plates were stacked face-to-face with each other along the [001] direction to construct the cylinders. The acidic condition was found to be a prerequisite for the oriented aggregations in this system.

Journal Article↗

PubMed2005

Evolution of single crystalline dendrites from nanoparticles through oriented attachment.

Single crystalline PbMoO4 dendrites were prepared by a simple hydrothermal method in the presence of surfactants. The formation and evolution of these dendrites was investigated by transmission electron microscopy, and the results clearly showed that the dendritic structure was achieved through oriented attachment of nanoparticles along crystallographically specific direction while the traditional Ostwald ripening mechanism also acted to form the initial particles before attachment and smooth the morphology of the dendrites after attachment.

Journal Article↗