PubMed2006

Adsorption of zinc on natural sediment of Tafna River (Algeria).

The environmental impact of metal additions to sediment depends on its sorption ability. The paper presents a study of zinc adsorption using the experiment data on natural sediment of Tafna River in northwest of Algeria. The effect of various operating variables, namely initial concentration, mass of sediment, and contact time, have been studied. The optimum contact time needed to reach equilibrium is of the order of 30 min and is independent of initial concentration and mass of zinc ions. The extent of adsorption increases with increase of concentration, and with decrease of adsorbent mass. The content of carbonate in sediment increases the adsorption indicating the active support material towards zinc ions. A batch sorption model, which assumes the pseudo-second-order mechanism, is developed to predict the rate constant of the sorption, the equilibrium sorption capacity and the initial sorption rate with the effect of initial zinc ion concentration and sediment dose. Various thermodynamic parameters, such as DeltaG degrees , DeltaH degrees and DeltaS degrees , have been calculated. The thermodynamics of zinc ion/sediment system indicates spontaneous, endothermic and randomness nature of the process.

Adsorption↗

PubMed2006

Reduction of clinkerization temperature by using phosphogypsum.

Valorization of phosphogypsum as mineralizer in the burning of Portland cement clinker was studied in our laboratory. X-ray fluorescence, optical microscope technique and powder X-ray diffraction were then used to characterize the synthesized clinker and its raw mixture in terms of chemical composition and clinker mineralogical composition. The effects of phosphogypsum on structural and morphological properties of clinker minerals and on the presence of alite were followed by scanning electron microscopy combined with microprobe analysis. The addition of phosphogypsum to the cement raw mixture shows that the burning temperature decreases and therefore improves the production process of clinker. The addition of 10% phosphogypsum permits a complete clinkerization at low burning temperature (1200 degrees C), instead of 1470 degrees C, which increases the cement factory efficiency by 25% and extends the service life of furnace fire brick. Structural and morphological analysis of clinker produced under the new conditions show that phosphogypsum preserve perfectly the crystalline structure of silicate phases, which leads to the improvement of physical and mechanical properties of cement.

Calcium Sulfate↗

PubMed2005

Removal of Supranol Yellow 4GL by adsorption onto Cr-intercalated montmorillonite.

Cr(III)-intercalated montmorillonite was utilized as an adsorbent for the removal of the organic pollutant, Supranol Yellow 4GL, a synthetic dye used for chemical fibres. The material was prepared by the reaction of Na montmorillonite with a base-hydrolyzed solution of Cr nitrate salt (OH(-)/Cr(3+) molar ratios of 2). XRD data showed that the interlayer spacing (d(001)) of montmorillonite was increased from 12.35 to 23.06 Angstroms. The kinetics and mechanism of the adsorption of the acid dye, Supranol Yellow 4GL, on Cr(III)-intercalated montmorillonite was investigated. The equilibrium time was reached within 30 min. The process follows pseudo-second-order rate kinetics. The Langmuir isotherm described the adsorption data over the concentration range (20-160 mg/l). The separator factor R(L) revealed the favourable nature of this adsorption process. Also, the thermodynamic parameters such as DeltaS degrees, DeltaH degrees, DeltaG degrees were determined.

Adsorption↗

PubMed2005

Sorption study of an acid dye from an aqueous solutions using modified clays.

The removal of the pollutant Supranol Yellow 4GL (S.Y.4GL) was studied by using different clays: clay exchanged with sodium (BNa+) and hydroxyaluminic polycation pillared clays in the presence or absence of non-ionic surfactant. While decomposing the surfactant at 500 degrees C, the surface of the clay changed significantly. The study of the behaviour of the three clays with respect to coloring solutions, allowed to determine the equilibrium time and the rate-determining step of the dye S.Y.4GL adsorption. Two simplified kinetic models, were tested to investigate the adsorption mechanisms in terms of pseudo-first order and pseudo-second order equations. Besides, the adsorption capacity data were fitted to Langmuir and Freundlich equations as well. A better fixation was obtained with an acidic pH. The effect of temperature on the adsorption of dye has been also studied and the thermodynamic parameters DeltaG degrees , DeltaH degrees and DeltaS degrees were determined.

Adsorption↗

PubMedDate not supplied

Equilibrium and kinetics of color removal from dye solutions with bentonite and polyaluminum hydroxide.

Wastewater from the textile industry contains soluble dyes that are toxic and particularly difficult to remove. A promising low-cost treatment, however, is use of polyaluminum hydroxide associated with bentonite. At suitable conditions, this process is able to efficiently remove color from solutions containing mixtures of soluble acid azo dyes and produce easily settleable sludge. The removal mechanism, which is believed to involve adsorption or precipitation and weak pH variations, is not well understood. With the overall reaction being second order, two elementary first-order reactions could be assumed. The equilibrium removal is a decreasing function of the temperature. However, this effect is weak and decreases when the dye concentration increases. At usual values of concentration in textile wastewater, this effect can be neglected. The resulting solid compound is particularly resistant to mechanical stress. Moreover, color was significantly released at pH greater than 8. Sodium ions have no influence on the compound stability, which reinforces the assumption of the involvement of an adsorption process.

Aluminum Hydroxide↗