A simple solution route to single-crystalline Sb2O3 nanowires with rectangular cross sections.

We report a simple solution route to large-scale synthesis of uniform, single-crystalline, and well-faceted orthorhombic antimony trioxide (Sb(2)O(3)) nanowires with rectangular cross sections by direct air oxidation of bulk metal antimony (Sb) in a mixed solution made of ethylenediamine (EDA) and deionized water (DIW). The as-synthesized products were analyzed by range of methods, such as XRD, SEM, EDX, TEM, SAED, HRTEM, FTIR, Raman, UV-vis absorption, and photoluminescence (PL) spectra. The as-synthesized Sb(2)O(3) nanowires with rectangular cross sections are usually hundreds of micrometers in length, typically 80-100 nm in width, and 60-80 nm in thickness. The novel room temperature photoluminescence properties of Sb(2)O(3) nanowires with rectangular cross sections displayed a significant UV luminescence with a strong emission band at 374 nm, which was reported for the first time, indicating the as-synthesized products with an optical band gap E(g) = 3.3 eV. It is expected that as-synthesized Sb(2)O(3) nanowires would be a new member of functional materials and used in the manufacture of advanced nanodevices.

Antimony↗

PubMed2005

A new route to zinc-blende CdSe nanocrystals: mechanism and synthesis.

We report the possible mechanism of forming of CdSe nanocrystals in the high boiling point solvents with long alkane chains and a novel Non-TOP-Based route to zinc-blende CdSe nanocrystals. A new mechanism shows that there exits a redox reaction in the long alkane chain solvents: Se is reduced to H2Se gas; at the same time, the long alkane chains are oxidated to alkene chains; then, the Cd complex reacts with H2Se to form CdSe nanocrystals. Possible chemical reaction equations involved in the process of forming the CdSe nanocrystals have been discussed. The alkene chain and H2Se were detected respectively by a series of experiments to support the new mechanism. Under the guidance of this mechanism, we have developed a much cheaper and greener Non-TOP-Based route for the synthesis of a size series of high-quality zinc-blende (cubic) CdSe nanocrystals. Low-cost, green, and environmentally friendlier reagents are used, without use of expensive solvents such as trioctylphosphine (TOP) or tributylphosphine (TBP). The new route enables us to achieve high-quality CdSe nanocrystals with sharp ultraviolet and visible (UV-vis) absorption peaks, controllable size (2.0-5.0 nm), bright photoluminescence (PL), narrow PL full width of half-maximum (fwhm) (29-48 nm), and high PL quantum yield (up to 60%) without any size sorting.

Cadmium↗