Facile synthesis of gold-silver nanocages with controllable pores on the surface.

Gold-silver alloy nanocages with controllable pores on the surface have been synthesized via galvanic replacement reaction between truncated Ag nanocubes and aqueous HAuCl4. Unlike in the previous studies, the initiation of replacement reaction started in a controllable way, simultaneously from eight corners of the truncated Ag nanocubes where {111} facets were exposed. The formation of cubic nanocages with pores at all the corners was determined by the capping agent, poly(vinyl pyrrolidone) (PVP), which preferentially covered the {100} facets of a truncated Ag nanocube.

Gold↗
PubMed2006

Optical properties of Au-Ag nanoboxes studied by single nanoparticle spectroscopy.

The optical properties of two Au-Ag nanobox samples with average edge lengths of 44 and 58 nm and wall thicknesses of 6 and 8 nm, respectively, have been studied by single particle spectroscopy. The measurements gave an average line width of Gamma = 306 +/- 7 meV with a standard deviation of sigma = 30 meV for the 44-nm boxes, and Gamma = 350 +/- 9 meV with sigma = 35 meV for the 58-nm boxes. These line widths are much broader than those of gold nanorods with comparable resonance energies. The increased broadening is attributed to a combination of surface scattering of electrons, as well as increased radiation damping for the nanoboxes. Discrete dipole approximation calculations have been performed with and without surface scattering of electrons to compare with the experimental spectra. The calculations confirm that both electron-surface scattering and radiation damping are important effects in this system.

Algorithms↗
PubMed2006

Poly(vinyl pyrrolidone): a dual functional reductant and stabilizer for the facile synthesis of noble metal nanoplates in aqueous solutions.

Poly(vinyl pyrrolidone) (PVP) has been extensively used in the solution-phase synthesis of many types of colloidal particles, where it is mainly considered as a steric stabilizer or capping agent with a major role to protect the product from agglomeration. In a recent study, we discovered that the hydroxyl end groups of PVP could also serve as a very mild reductant for kinetically controlled synthesis of Ag nanoplates with yields as high as 75%. Here we further demonstrate that hydroxyl-terminated PVP is also a well-suited reductant for the aqueous synthesis of circular, triangular, and hexagonal nanoplates made of other noble metals including Pd, Au, and Pt. The reduction kinetics of a metal salt by the hydroxyl end groups of PVP can be maneuvered in at least two different ways to facilitate the evolution of plate morphology: (i) by adjusting the molar ratio of PVP to the salt precursor and (ii) by altering the molecular weight of PVP. Unlike previously reported studies of Ag and Au thin plates, light was found to have a negligible role in the present synthesis.

Journal Article↗
PubMed2006

Gold nanostructures: engineering their plasmonic properties for biomedical applications.

The surface plasmon resonance peaks of gold nanostructures can be tuned from the visible to the near infrared region by controlling the shape and structure (solid vs. hollow). In this tutorial review we highlight this concept by comparing four typical examples: nanospheres, nanorods, nanoshells, and nanocages. A combination of this optical tunability with the inertness of gold makes gold nanostructures well suited for various biomedical applications.

Biomedical Engineering↗
PubMed2006

Maneuvering the surface plasmon resonance of silver nanostructures through shape-controlled synthesis.

Silver nanostructures are containers for surface plasmons - the collective oscillation of conduction electrons in phase with incident light. By controlling the shape of the container, one can control the ways in which electrons oscillate, and in turn how the nanostructure scatters light, absorbs light, and enhances local electric fields. With a series of discrete dipole approximation (DDA) calculations, each of a distinctive morphology, we illustrate how shape control can tune the optical properties of silver nanostructures. Calculated predictions are validated by experimental measurements performed on nanocubes with controllable corner truncation, right bipyramids, and pentagonal nanowires. Control of nanostructure shape allows optimization of plasmon resonance for molecular detection and spectroscopy.

Nanostructures↗
PubMed2006

Preparation and study of polyacryamide-stabilized silver nanoparticles through a one-pot process.

A one-pot route was illustrated to synthesize stable well-dispersed silver colloids stabilized by polyacrylamide on a large scale. Reduction of silver ions and polymerization of acrylamide occurred almost simultaneously in the absence of a commonly used reducing agent and initiator. A possible mechanism for the formation of silver nanoparticles with bimodal size distribution was proposed. The structure and composition of the obtained nanoparticles were characterized carefully. Furthermore, light scattering simulation and UV-vis absorption studies confirmed that the obtained colloids were the mixture of Ag and Ag2O nanoparticles. The presence of silver oxide layers on the nanoparticle surface should be responsible for the broadening of the surface plasmon band of silver nanoparticles. Ag2O layers could be added or removed from Ag nanoparticle surfaces by the addition of HNO3, HAc, or NaCl solution to the as-obtained silver colloids.

Acrylic Resins↗
PubMed2006

Right bipyramids of silver: a new shape derived from single twinned seeds.

Silver nanoparticles with a single (111) twin were selectively nucleated and grown for the first time to produce right bipyramids 75-150 nm in edge length. Key to the production of single twinned seeds was the addition of NaBr to a polyol synthesis in which AgNO3 is reduced by ethylene glycol in the presence of poly(vinyl pyrrolidone). Examination of nanoparticles at different stages of the reaction with electron microscopy revealed that the spherical, single twinned seeds grew to become right bipyramids through enlargement of their (100) facets. The UV-vis-NIR spectrum exhibited by right bipyramids is distinct from that of any other silver nanostructure, and their sharp corners make these new nanoparticles especially promising for enhancement of Raman scattering.

Crystallization↗
PubMed2005

Kinetically controlled synthesis of triangular and hexagonal nanoplates of palladium and their SPR/SERS properties.

The rapid reduction of Na(2)PdCl(4) by ethylene glycol in the presence of poly(vinyl pyrrolidone) (PVP) has recently been demonstrated as a convenient method of generating Pd cubooctahedra and twinned nanoparticles. Here we describe a new procedure where Pd triangular or hexagonal nanoplates could be selectively synthesized by manipulating the reduction kinetics of the polyol process. More specifically, the reduction rate was substantially reduced through the introduction of Fe(III) species and the O(2)/Cl(-) pair, two wet etchants for Pd(0). The etching power of the O(2)/Cl(-) pair could be further enhanced by adding an acid to lower the pH of the reaction solution. Unlike the previously reported synthesis of Ag and Au nanoplates, light was found to have no indispensable role in the formation of Pd nanoplates. Both triangular and hexagonal nanoplates of Pd exhibited surface plasmon resonance (SPR) peaks in the visible region, and their positions matched with the results of discrete dipole approximation (DDA) calculation. Thanks to their sharp corners and edges, these Pd nanoplates could serve as active substrates for surface-enhanced Raman scattering (SERS).

Journal Article↗
PubMed2005

Gold nanocages as contrast agents for spectroscopic optical coherence tomography.

We describe gold nanocages as a new class of potential contrast agent for spectroscopic optical coherence tomography (OCT). Monodispersed gold nanocages of an approximately 35 nm edge length exhibit strong optical resonance, with the peak wavelength tunable in the near-infrared range. We characterized the optical properties of the nanocage by using OCT experiments along with numerical calculations, revealing an absorption cross section approximately 5 orders of magnitude larger than conventional dyes. Experiments with tissue phantoms demonstrated that the nanocages provide enhanced contrast for spectroscopic as well as conventional intensity-based OCT imaging.

Contrast Media↗
PubMed2005

Gold nanocages: bioconjugation and their potential use as optical imaging contrast agents.

Gold nanocages of <40 nm in dimension have been synthesized using the galvanic replacement reaction between Ag nanocubes and HAuCl4 in an aqueous solution. By controlling the molar ratio between Ag and HAuCl4, the gold nanocages could be tuned to display surface plasmon resonance peaks around 800 nm, a wavelength commonly used in optical coherence tomography (OCT) imaging. OCT measurements on phantom samples indicate that these gold nanocages have a moderate scattering cross-section of approximately 8.10 x 10(-16) m2 but a very large absorption cross-section of approximately 7.26 x 10(-15) m2, suggesting their potential use as a new class of contrast agents for optical imaging. When bioconjugated with antibodies, the gold nanocages have also been demonstrated for specific targeting of breast cancer cells.

Cell Line, Tumor↗
PubMed2005

Monodispersed spherical colloids of Se@CdSe: synthesis and use as building blocks in fabricating photonic crystals.

Monodispersed spherical core-shell colloids of Se@Ag(2)Se have been exploited as a chemical template to synthesize Se@CdSe core-shell particles using a cation-exchange reaction. A small amount of tributylphosphine could facilitate the replacement of Ag(+) by Cd(2+) in methanol at 50 degrees C to complete the conversion within 150 min. The orthorhombic structure of beta-Ag(2)Se changed to a well-defined wurtzite lattice for CdSe. The CdSe shells could be converted back to beta-Ag(2)Se by reacting with AgNO(3) in methanol at room temperature. Because of the uniformity in size and high refractive index associated with the Se@CdSe core-shell colloids, they could serve as a new class of building blocks to fabricate photonic crystals with wide and strong stop bands.

Cadmium Compounds↗
PubMed2005

Size-dependence of surface plasmon resonance and oxidation for Pd nanocubes synthesized via a seed etching process.

Pd nanocubes between 8 and 50 nm in size were synthesized at the same concentration of Na2PdCl4 precursor by controlling the number of seeds formed in the nucleation stage. Increasing the concentration of FeCl3, an oxidative etchant for Pd, reduced the number of seeds and led to formation of larger Pd nanocubes. The larger nanocubes exhibited surface plasmon resonance peaks in the visible region, the locations of which matched with the results of the discrete dipole approximation calculation. While the nanocubes of 25 and 50 nm in size oxidized in air to form Pd@PdO core-shell structures, the 8-nm nanocubes were stable in air for over 90 days.

Crystallization↗
PubMed2005

Optical properties of Pd-Ag and Pt-Ag nanoboxes synthesized via galvanic replacement reactions.

Silver nanocubes dispersed in water were transformed into Pd-Ag or Pt-Ag nanoboxes by adding either Na(2)PdCl(4) or Na(2)PtCl(4). By controlling the amount of noble metal salt added, and therefore the molar ratio of Na(2)PdCl(4) or Na(2)PtCl(4) to Ag, we could tune the surface plasmon resonance peak of the nanostructures across the entire visible spectrum, from 440 to 730 nm. Replacement of Ag with Pd resulted in the formation of a nanobox composed of a Pd-Ag alloy single crystal, but the nanobox formed after replacement of Ag with Pt was instead composed of distinct Pt nanoparticles. DDA calculations suggest that both nanoboxes absorb light strongly, with Q(abs)/Q(sca) approximately 5. After galvanic replacement, Pd-Ag and Pt-Ag nanostructures remain SERS active, suggesting their use as a SERS probe for studying the dependence of interfacial chemistry on composition.

Journal Article↗
PubMed2004

Engineering the structure-induced enhanced absorption in three-dimensional metallic photonic crystals.

Order-of-magnitude enhancement of light absorption can take place near the photonic band gaps in three-dimensional layer-by-layer metallic photonic crystals in the mid-infrared wavelength regime where a conventional bulk metallic material shows weak absorption. In this paper we investigate the dependence of this enhanced absorption on several structural parameters of the crystal by means of a plane-wave-based transfer-matrix method in combination with an analytic model expansion approach. We find that when the metallic layers are brought out of touch, the magnitude of the absorption peaks grows rather than decays, in contrast with the conventional wisdom that the connectivity of metallic structure can enhance the absorption. Besides, the increase in the metallic layer separation distance will result in redshifts of absorption peak. The position of the absorption peak can also be engineered conveniently by simply changing the refractive index of the dielectric material filling the open domain between metal walls. Due to the approximate scalability of Maxwell's equations, the absorption peak shows a nearly linear dependence in position on this refractive index.

Journal Article↗
PubMed2004

Synthesis and optical properties of nanorattles and multiple-walled nanoshells/nanotubes made of metal alloys.

The galvanic replacement reaction between silver and chloroauric acid has been exploited as a powerful means for preparing metal nanostructures with hollow interiors. Here, the utility of this approach is further extended to produce complex core/shell nanostructures made of metals by combining the replacement reaction with electroless deposition of silver. We have fabricated nanorattles consisting of Au/Ag alloy cores and Au/Ag alloy shells by starting with Au/Ag alloy colloids as the initial template. We have also prepared multiple-walled nanoshells/nanotubes (or nanoscale Matrioshka) with a variety of shapes, compositions, and structures by controlling the morphology of the template and the precursor salt used in each step of the replacement reaction. There are a number of interesting optical features associated with these new core/shell metal nanostructures. For example, nanorattles made of Au/Ag alloys displayed two well-separated extinction peaks, a feature similar to that of gold or silver nanorods. The peak at approximately 510 nm could be attributed to the Au/Ag alloy cores, while the other peak was associated with the Au/Ag alloy shells and could be continuously tuned in the spectral range from red to near-infrared.

Journal Article↗