PubMed · 10895724
The source did not provide an abstract. Follow the original record for more information.
Explore connections, maps & timelines
E R Fein. 1999. Fluoride supplements.. https://pubmed.ncbi.nlm.nih.gov/10895724/
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
A series of "profile" laboratory studies was conducted to confirm the anticaries potential and hard tissue safety of a novel sodium hexametaphosphate dentifrice technology which provides dual-action tooth whitening (i.e., stain prevention as well as stain removal), while simultaneously providing improved anticalculus action. Under remineralization pH cycling conditions, the dual-action whitening dentifrice produced lesion fluoridation comparable to a conventional NaF dentifrice. Under lesion progression pH cycling conditions, the dual-action whitening dentifrice produced enamel protection against caries initiation and progression comparable to a conventional NaF dentifrice, as well as comparable to a conventional tartar control dentifrice, also containing NaF. These results are consistent with clinical data supporting the anticaries effectiveness of NaF dentifrices combined with anionic tartar control inhibitors, such as pyrophosphate. Abrasion assessments were made using Radioactive Dentin and Enamel Abrasivity (RDA and REA) methods. These laboratory studies demonstrated that the new, dual-action whitening dentifrice produces dentin and enamel abrasivity similar to conventional silica-based dentifrice formulations. These in vitro studies verify the anticaries potential and demonstrate the hard tissue safety of the dual-action, sodium hexametaphosphate dentifrice.
The aim of this 2-year prospective randomized clinical study was to evaluate the efficacy of a prevention program for schoolchildren with high caries risk. A sample of 419 subjects was divided into a test (T, n = 259) and control group (C, n = 160). Four times a year, the test group received professional tooth-cleaning and application of a 0.1% fluoride varnish as well as motivation and instruction in oral hygiene. The control group received only oral hygiene instruction and took part in supervised toothbrushing once a year. At baseline and after 2 years, the D3,4MFS and the incipient lesions (D1,2) were recorded. After 2 years, 318 subjects (T = 187, C = 131) were included in the data analysis. The baseline D1,2 was 6.18 (T) and 5.50 (C), the D3,4MFS 2.13 (T) and 2.08 (C), respectively. No statistically significant difference was found for the baseline values. At the final examination, the D1,2 increment was 3.96 in the test and 6.53 in the control group, showing a statistically significant difference (P < 0.001). No such difference was found for the D3,4MFS increment (T: 2.22; C: 2.61). The results indicate that it might not be possible to prevent cavities in high caries risk children by means of the described program.
Considerable attention has been given to the release of the cariostatic fluoride ion from glass-based dental cements (dental silicate and glass ionomer). In these, the total available fluoride content is not precisely known since fluorine is distributed between the cross-linked aqueous salt matrix, partially dissolved glass, and undissolved glass. In analogous cements based on zinc oxide the fluoride is added as highly soluble SnF2. The object of this study is to compare the F- ion release profiles of commercial zinc polycarboxylate and zinc phosphate containing 4.4 and 3.6% SnF2, respectively. Mixed cements were clamped in split ring moulds to produce discs of 10 mm x 1 mm after storage at 37 degrees C for 1 h. Each was weighed and immersed in 10 ml of deionised water. When this changed, at 13 time intervals up to 98 days, the fluoride content was measured using an ion selective electrode. The mean (N = 3) values obtained were expressed cumulatively [F] in micromol F ion/g cement. The total [F] released was 111 for the zinc polycarboxylate and 286 for zinc phosphate compared with total F in the cements of 561 and 464, respectively. When the cumulative [F] was plotted versus t(1/2) close associations were found for both cements. For the polycarboxylate the regression line [F] = 10.6t(1/2) + 9.9 fitted well over the whole 98 days (R = 0.997). For the phosphate a better fit regression line was obtained using results up to 32 days only; [F] = 36.8t(1/2) - 8.4 (R = 0.999). For t > 32 days results increasingly deviated from this line. These results fitted a regression line of the form [F] = 81.7log(e) t - 87.3 (R = 0.9997). Comparisons are made with data from previous authors both for zinc phosphate cement and glass-based cements and with diffusion theory of F ion release. It is concluded that zinc-based cements provide some indications of how glass-based cements may behave over long periods of release and that zinc phosphate is the material of clinical choice for orthodontic cementation if maximal fluoride release is the prime criterion.